AKROMID®
B3 GK 15 natural (1824)
PA6 GB15
AKROMID® B3 GK 15 natural (1824) - PA 6, 15% glass beads reinforced, good surface, low warpage
4.000MPa
85MPa
30kJ/m²
AKROMID® B3 GK 15 natural (1824) - PA 6, 15% glass beads reinforced, good surface, low warpage
AKROMID®
B3 GM 10/20 1 black (1829)
PA6 (GF10+GB20)
AKROMID® B3 GM 10/20 1 black 950058 (1829) is a 10% glass fibre reinforced, 20% glass bead filled, heat stabilised polyamide 6 with good surface and low warpage
6.200MPa
115MPa
45kJ/m²
AKROMID® B3 GM 10/20 1 black 950058 (1829) is a 10% glass fibre reinforced, 20% glass bead filled, heat stabilised polyamide 6 with good surface and low warpage
AKROMID®
A3 1 black (2417)
PA66
AKROMID® A3 1 black (2417) is a heat stabilised, unreinforced polyamide 6.6
3.200MPa
85MPa
180kJ/m²
AKROMID® A3 1 black (2417) is a heat stabilised, unreinforced polyamide 6.6
AKROMID®
A3 1 natural (2416)
PA66
AKROMID® A3 1 natural (2416) - heat stabilised, unreinforced polyamide 6.6
3.200MPa
85MPa
180kJ/m²
AKROMID® A3 1 natural (2416) - heat stabilised, unreinforced polyamide 6.6
AKROMID®
A3 GK 30 black (2306)
PA66 GB30
AKROMID® A3 GK 30 black (2306) - PA 6.6, 30% glass beads reinforced, good surface, low warpage
5.000MPa
90MPa
28kJ/m²
AKROMID® A3 GK 30 black (2306) - PA 6.6, 30% glass beads reinforced, good surface, low warpage
AKROMID®
B3 GF 40 1 natural (2466)
PA6 GF40
AKROMID® B3 GF 40 1 natural (2466) is a 40% glass fibre reinforced, heat stabilised polyamide 6 with high rigidity and strength and light inherent color
12.800MPa
205MPa
100kJ/m²
AKROMID® B3 GF 40 1 natural (2466) is a 40% glass fibre reinforced, heat stabilised polyamide 6 with high rigidity and strength and light inherent color
AKROMID®
B3 GF 60 natural (2476)
PA6 GF60
AKROMID® B3 GF 60 natural (2476) is a 60% glass fibre reinforced polyamide 6 with very high rigidity and strength and light inherent color
21.000MPa
240MPa
90kJ/m²
AKROMID® B3 GF 60 natural (2476) is a 60% glass fibre reinforced polyamide 6 with very high rigidity and strength and light inherent color
AKROMID®
NEXT S3 GF 50 1 HU black (8827)PA6.10 GF50
AKROMID® NEXT S3 GF 50 1 black (8827) is a partially biobased and heat-stabilised PA6.10. With 50% glass fibre reinforcement, the material is suitable for household and industrial applications with high demands on strength and stiffness. This sustainable and UL listed grade is characterised by its low moisture absorption and high chemical resistance compared to classic PA6 and PA 6.6.
Features
Regulatory
Properties
14.500MPa
200MPa
100kJ/m²
Sustainability
Biobased carbon content
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Flexural modulus
ISO 178
Flexural strength
ISO 178
Flexural strain at break
ISO 178
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Ball indentation hardness
ISO 2039-1
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Temperature of deflection under load HDT/C
ISO 75
Melting temperature
ISO 11357-3
Flammability
Burning rate
UL 94
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Molding shrinkage
ISO 294-4
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.