Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/m²
558 Compounds found
Recommended  
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

AKROMID®

B3 3 S3 10 natural (1808)

PA6-I

AKROMID® B3 3 S3 10 natural (1808) - PA 6 unreinforced and cold impact modified, e.g. for the furniture industry

Modulus

2.700MPa

Strength

70MPa

Impact

180kJ/m²

AKROMID® B3 3 S3 10 natural (1808) - PA 6 unreinforced and cold impact modified, e.g. for the furniture industry

AKROMID®

B3 GM 10/20 1 black (1829)

PA6 (GF10+GB20)

AKROMID® B3 GM 10/20 1 black 950058 (1829) is a 10% glass fibre reinforced, 20% glass bead filled, heat stabilised polyamide 6 with good surface and low warpage

Modulus

6.200MPa

Strength

115MPa

Impact

45kJ/m²

AKROMID® B3 GM 10/20 1 black 950058 (1829) is a 10% glass fibre reinforced, 20% glass bead filled, heat stabilised polyamide 6 with good surface and low warpage

AKROMID®

A3 1 natural (2416)

PA66

AKROMID® A3 1 natural (2416) - heat stabilised, unreinforced polyamide 6.6

Modulus

3.200MPa

Strength

85MPa

Impact

180kJ/m²

AKROMID® A3 1 natural (2416) - heat stabilised, unreinforced polyamide 6.6

AKROMID®

A3 1 black (2417)

PA66

AKROMID® A3 1 black (2417) is a heat stabilised, unreinforced polyamide 6.6

Modulus

3.200MPa

Strength

85MPa

Impact

180kJ/m²

AKROMID® A3 1 black (2417) is a heat stabilised, unreinforced polyamide 6.6

AKROMID®

A3 GK 30 black (2306)

PA66 GB30

AKROMID® A3 GK 30 black (2306) - PA 6.6, 30% glass beads reinforced, good surface, low warpage

Modulus

5.000MPa

Strength

90MPa

Impact

28kJ/m²

AKROMID® A3 GK 30 black (2306) - PA 6.6, 30% glass beads reinforced, good surface, low warpage

AKROMID®

A3 GF 40 1 L black (4671)

PA66+PP GF40

AKROMID® A3 GF 40 1 L black (4671) - PA6.6/PP-Blend, 40% glass fibre reinforced, lower density, cost reduced, zinc chloride

Modulus

11.800MPa

Strength

170MPa

Impact

80kJ/m²

AKROMID® A3 GF 40 1 L black (4671) - PA6.6/PP-Blend, 40% glass fibre reinforced, lower density, cost reduced, zinc chloride

AKROLOY®

Preliminary

PA GF 40 natural (6413)

PA66+PA6I/6T GF40

AKROLOY® PA GF 40 natural (6413) is a 40% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.

Modulus

13.000MPa

Strength

235MPa

Impact

95kJ/m²

AKROLOY® PA GF 40 natural (6413) is a 40% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.

163646580

AKROTEK®

UL
Preliminary

PK-VM GF 30 FR orange (8537)PK GF30 FR(40)

AKROTEK® PK-VM GF 30 FR orange (8537) is a 30% glass fibre reinforced, flame retardant and process improved Polyketone compound, colored in orange similar to RAL 2003. The flame retardant system is free of red phosphorous and halogens. Due to its good chemical resistance, good dimensional stability and high elongation at break it is suitable for high voltage components in e-mobility.

Features

hydrolysis / chemically stabilised
flame retardant
process improved
E&E
E-Mobility

Regulatory

ul

Properties

Modulus

8.600MPa

Strength

125MPa

Impact

70kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
8600 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
125 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
3,5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
70 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
13 kJ/m²

Thermal Properties

RTI electrical

UL 746B

UL
0,8mm Wall thickness
UL
1,6mm Wall thickness
UL
3,2mm Wall thickness
105 °C
105 °C
105 °C

RTI impact

UL 746B

UL
0,8mm Wall thickness
UL
1,6mm Wall thickness
UL
3,2mm Wall thickness
70 °C
70 °C
80 °C

RTI strength

UL 746B

UL
0,8mm Wall thickness
UL
1,6mm Wall thickness
UL
3,2mm Wall thickness
115 °C
115 °C
125 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Burning rate

UL 94

UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
V-0 Class
V-0 Class
V-0 Class

GWFI

IEC 60695-2-12

UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
960 °C
960 °C
960 °C

GWIT

IEC 60695-2-13

UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
825 °C
825 °C
850 °C

HWI

UL 746A

UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
0 PLC
0 PLC
0 PLC

HAI

UL 746A

UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
0 PLC
0 PLC
0 PLC

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,48 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,3 - 0,5 %
0,8 - 1,0 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

UL
d.a.m.
1010 Ω x cm

Surface resistivity

DIN EN 62631-3-2

UL
d.a.m.
1013 Ω

Comparative tracking index

IEC 60112

UL
Test liquid A
600 V

Comparative tracking index

ASTM D3638

UL
0 PLC

Dielectric strength

IEC 60243

1 mm
29 kV/mm

Inclined-Plane Tracking, IPT

ASTM D2303-13

UL
1 kV

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.