AKROMID®
B3 3 S3 10 natural (1808)
PA6-I
AKROMID® B3 3 S3 10 natural (1808) - PA 6 unreinforced and cold impact modified, e.g. for the furniture industry
2.700MPa
70MPa
180kJ/m²
AKROMID® B3 3 S3 10 natural (1808) - PA 6 unreinforced and cold impact modified, e.g. for the furniture industry
AKROMID®
B3 GM 10/20 1 black (1829)
PA6 (GF10+GB20)
AKROMID® B3 GM 10/20 1 black 950058 (1829) is a 10% glass fibre reinforced, 20% glass bead filled, heat stabilised polyamide 6 with good surface and low warpage
6.200MPa
115MPa
45kJ/m²
AKROMID® B3 GM 10/20 1 black 950058 (1829) is a 10% glass fibre reinforced, 20% glass bead filled, heat stabilised polyamide 6 with good surface and low warpage
AKROMID®
A3 1 natural (2416)
PA66
AKROMID® A3 1 natural (2416) - heat stabilised, unreinforced polyamide 6.6
3.200MPa
85MPa
180kJ/m²
AKROMID® A3 1 natural (2416) - heat stabilised, unreinforced polyamide 6.6
AKROMID®
A3 1 black (2417)
PA66
AKROMID® A3 1 black (2417) is a heat stabilised, unreinforced polyamide 6.6
3.200MPa
85MPa
180kJ/m²
AKROMID® A3 1 black (2417) is a heat stabilised, unreinforced polyamide 6.6
AKROMID®
A3 GK 30 black (2306)
PA66 GB30
AKROMID® A3 GK 30 black (2306) - PA 6.6, 30% glass beads reinforced, good surface, low warpage
5.000MPa
90MPa
28kJ/m²
AKROMID® A3 GK 30 black (2306) - PA 6.6, 30% glass beads reinforced, good surface, low warpage
AKROMID®
A3 GF 40 1 L black (4671)
PA66+PP GF40
AKROMID® A3 GF 40 1 L black (4671) - PA6.6/PP-Blend, 40% glass fibre reinforced, lower density, cost reduced, zinc chloride
11.800MPa
170MPa
80kJ/m²
AKROMID® A3 GF 40 1 L black (4671) - PA6.6/PP-Blend, 40% glass fibre reinforced, lower density, cost reduced, zinc chloride
AKROLOY®
PA GF 40 natural (6413)
PA66+PA6I/6T GF40
AKROLOY® PA GF 40 natural (6413) is a 40% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.
13.000MPa
235MPa
95kJ/m²
AKROLOY® PA GF 40 natural (6413) is a 40% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.
AKROMID®
NEXT G3 GF 30 1 L CR black (8314)PA6.9 + PP GF30
AKROMID® NEXT G3 GF 30 1 L CR black (8314) is a 30% glass fiber reinforced PA 6.9/PP blend with high strength and stiffness. The partially bio-based grade is characterised by particularly low moisture absorption and high chemical resistance compared to classic PA 6 and PA 6.6. It is suitable for applications where weight reduction and sustainability are required. The material is certified according to REDcert². 33% of the fossil raw materials required for manufacturing this product were replaced by sustainable biomass-balanced PP (≙ allocation factor).
Features
Regulatory
Properties
8.000MPa
125MPa
65kJ/m²
Sustainability
Biobased carbon content
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Melting temperature
ISO 11357-3
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Water absorption
ISO 62
Molding shrinkage
ISO 294-4
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.