HEADER Granulat 1920x700

Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/m²
558 Compounds found
Recommended  
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

AKROMID®

B3 GK 15 natural (1824)

PA6 GB15

AKROMID® B3 GK 15 natural (1824) - PA 6, 15% glass beads reinforced, good surface, low warpage

Modulus

4.000MPa

Strength

85MPa

Impact

30kJ/m²

AKROMID® B3 GK 15 natural (1824) - PA 6, 15% glass beads reinforced, good surface, low warpage

AKROMID®

B3 GM 10/20 1 black (1829)

PA6 (GF10+GB20)

AKROMID® B3 GM 10/20 1 black 950058 (1829) is a 10% glass fibre reinforced, 20% glass bead filled, heat stabilised polyamide 6 with good surface and low warpage

Modulus

6.200MPa

Strength

115MPa

Impact

45kJ/m²

AKROMID® B3 GM 10/20 1 black 950058 (1829) is a 10% glass fibre reinforced, 20% glass bead filled, heat stabilised polyamide 6 with good surface and low warpage

AKROMID®

A3 1 black (2417)

PA66

AKROMID® A3 1 black (2417) is a heat stabilised, unreinforced polyamide 6.6

Modulus

3.200MPa

Strength

85MPa

Impact

180kJ/m²

AKROMID® A3 1 black (2417) is a heat stabilised, unreinforced polyamide 6.6

AKROMID®

A3 GK 30 black (2306)

PA66 GB30

AKROMID® A3 GK 30 black (2306) - PA 6.6, 30% glass beads reinforced, good surface, low warpage

Modulus

5.000MPa

Strength

90MPa

Impact

28kJ/m²

AKROMID® A3 GK 30 black (2306) - PA 6.6, 30% glass beads reinforced, good surface, low warpage

AKROMID®

A3 1 natural (2416)

PA66

AKROMID® A3 1 natural (2416) - heat stabilised, unreinforced polyamide 6.6

Modulus

3.200MPa

Strength

85MPa

Impact

180kJ/m²

AKROMID® A3 1 natural (2416) - heat stabilised, unreinforced polyamide 6.6

AKROMID®

B3 GF 40 1 black (2487)

PA6 GF40

AKROMID® B3 GF 40 1 black (2487) is a 40% glass fibre reinforced, heat stabilised polyamide 6 with high rigidity and strength.

Modulus

12.800MPa

Strength

205MPa

Impact

100kJ/m²

AKROMID® B3 GF 40 1 black (2487) is a 40% glass fibre reinforced, heat stabilised polyamide 6 with high rigidity and strength.

AKROMID®

B3 black (2502)

PA6

AKROMID® B3 black (2502) is an unreinforced polyamide 6.

Modulus

3.600MPa

Strength

85MPa

Impact

180kJ/m²

AKROMID® B3 black (2502) is an unreinforced polyamide 6.

163646580

AKROMID®

A3 GF 25 FR natural (7649)PA66 GF25 FR(40)

AKROMID® A3 GF 25 FR natural (7649) is a 25% glass fibre reinforced, halogen and red phosphourus free flame retardant polyamide 6.6 with high stiffness and strength and light inherent color

Properties

Modulus

9.200MPa

Strength

135MPa

Impact

63kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
9200 MPa
5800 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
135 MPa
90 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3 %
4,5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
63 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
10 kJ/m²

Thermal Properties

Melting temperature

ISO 11357-3

DSC, 10K/min
260 °C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
V-0 Class
V-0 Class
V-0 Class

GWFI

IEC 60695-2-12

0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
960 °C
960 °C
960 °C

GWIT

IEC 60695-2-13

0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
750 °C
725 °C
750 °C

General properties

Density

ISO 1183

23°C
1,37 g/cm³

Electrical Properties

Comparative tracking index

IEC 60112

Test liquid A
> 600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more