Select your fitting and find the right compound for your intend
AKROMID®
B3 3 S3 10 natural (1808)
PA6-I
AKROMID® B3 3 S3 10 natural (1808) - PA 6 unreinforced and cold impact modified, e.g. for the furniture industry
2.700MPa
70MPa
180kJ/m²
AKROMID® B3 3 S3 10 natural (1808) - PA 6 unreinforced and cold impact modified, e.g. for the furniture industry
AKROMID®
B3 GM 10/20 1 black (1829)
PA6 (GF10+GB20)
AKROMID® B3 GM 10/20 1 black 950058 (1829) is a 10% glass fibre reinforced, 20% glass bead filled, heat stabilised polyamide 6 with good surface and low warpage
6.200MPa
115MPa
45kJ/m²
AKROMID® B3 GM 10/20 1 black 950058 (1829) is a 10% glass fibre reinforced, 20% glass bead filled, heat stabilised polyamide 6 with good surface and low warpage
AKROMID®
A3 GK 30 black (2306)
PA66 GB30
AKROMID® A3 GK 30 black (2306) - PA 6.6, 30% glass beads reinforced, good surface, low warpage
5.000MPa
90MPa
28kJ/m²
AKROMID® A3 GK 30 black (2306) - PA 6.6, 30% glass beads reinforced, good surface, low warpage
AKROMID®
A3 1 black (2417)
PA66
AKROMID® A3 1 black (2417) is a heat stabilised, unreinforced polyamide 6.6
3.200MPa
85MPa
180kJ/m²
AKROMID® A3 1 black (2417) is a heat stabilised, unreinforced polyamide 6.6
AKROMID®
A3 1 natural (2416)
PA66
AKROMID® A3 1 natural (2416) - heat stabilised, unreinforced polyamide 6.6
3.200MPa
85MPa
180kJ/m²
AKROMID® A3 1 natural (2416) - heat stabilised, unreinforced polyamide 6.6
AKROMID®
B3 black (2502)
PA6
AKROMID® B3 black (2502) is an unreinforced polyamide 6.
3.600MPa
85MPa
180kJ/m²
AKROMID® B3 black (2502) is an unreinforced polyamide 6.
AKROMID®
B3 GF 60 1 natural (2468)
PA6 GF60
AKROMID® B3 GF 60 1 natural (2468) is a 60% glass fibre reinforced heat stabilised polyamide 6 with very high rigidity and strength and light inherent color.
21.000MPa
240MPa
90kJ/m²
AKROMID® B3 GF 60 1 natural (2468) is a 60% glass fibre reinforced heat stabilised polyamide 6 with very high rigidity and strength and light inherent color.
AKROLOY®
AKROLOY® PA FGF 50 black (6546) is a 50% flat glass fiber reinforced, semi-aromatic polyamide blend. Due to the flat glass fiber, it is characterised by significantly improved properties 90° to the flow direction as well as low warpage. Even in conditioned state, the material impresses with very high stiffness and strength owing to its lower moisture uptake. The material is perfectly suitable for parts where dimensional stabilitiy is required. Furthermore, it can be used as an alternative for aluminium and zinc diecast alloys.
Features
Properties
17.000MPa
265MPa
100kJ/m²
ISO 527-2
ISO 527-2
ISO 527-2
ISO 178
ISO 178
ISO 178
ISO 179-1/1eU
ISO 179-1/1eA
ISO 75
ISO 11357-3
IEC 60216
UL 94
FMVSS 302
ISO 1183
ISO 1110
ISO 294-4
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
Contact
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.