AKROMID®

B3 GK 15 natural (1824)

PA6 GB15

AKROMID® B3 GK 15 natural (1824) - PA 6, 15% glass beads reinforced, good surface, low warpage

Modulus

4.000MPa

Strength

85MPa

Impact

30kJ/m²

AKROMID® B3 GK 15 natural (1824) - PA 6, 15% glass beads reinforced, good surface, low warpage

AKROMID®

B3 GM 10/20 1 black (1829)

PA6 (GF10+GB20)

AKROMID® B3 GM 10/20 1 black 950058 (1829) is a 10% glass fibre reinforced, 20% glass bead filled, heat stabilised polyamide 6 with good surface and low warpage

Modulus

6.200MPa

Strength

115MPa

Impact

45kJ/m²

AKROMID® B3 GM 10/20 1 black 950058 (1829) is a 10% glass fibre reinforced, 20% glass bead filled, heat stabilised polyamide 6 with good surface and low warpage

AKROMID®

A3 1 natural (2416)

PA66

AKROMID® A3 1 natural (2416) - heat stabilised, unreinforced polyamide 6.6

Modulus

3.200MPa

Strength

85MPa

Impact

180kJ/m²

AKROMID® A3 1 natural (2416) - heat stabilised, unreinforced polyamide 6.6

AKROMID®

A3 1 black (2417)

PA66

AKROMID® A3 1 black (2417) is a heat stabilised, unreinforced polyamide 6.6

Modulus

3.200MPa

Strength

85MPa

Impact

180kJ/m²

AKROMID® A3 1 black (2417) is a heat stabilised, unreinforced polyamide 6.6

AKROMID®

A3 GK 30 black (2306)

PA66 GB30

AKROMID® A3 GK 30 black (2306) - PA 6.6, 30% glass beads reinforced, good surface, low warpage

Modulus

5.000MPa

Strength

90MPa

Impact

28kJ/m²

AKROMID® A3 GK 30 black (2306) - PA 6.6, 30% glass beads reinforced, good surface, low warpage

AKROMID®

B3 GF 60 natural (2476)

PA6 GF60

AKROMID® B3 GF 60 natural (2476) is a 60% glass fibre reinforced polyamide 6 with very high rigidity and strength and light inherent color

Modulus

21.000MPa

Strength

240MPa

Impact

90kJ/m²

AKROMID® B3 GF 60 natural (2476) is a 60% glass fibre reinforced polyamide 6 with very high rigidity and strength and light inherent color

AKROMID®

A3 GF 40 1 L black (4671)

PA66+PP GF40

AKROMID® A3 GF 40 1 L black (4671) - PA6.6/PP-Blend, 40% glass fibre reinforced, lower density, cost reduced, zinc chloride

Modulus

11.800MPa

Strength

170MPa

Impact

80kJ/m²

AKROMID® A3 GF 40 1 L black (4671) - PA6.6/PP-Blend, 40% glass fibre reinforced, lower density, cost reduced, zinc chloride

163646580

AKROMID®

UL
Preliminary

A3 GF 60 HU natural (6452)PA66 GF60

AKROMID® A3 GF 60 HU natural (6452) is a 60% glass fibre reinforced and heat stabilised polyamide 6.6 with very high rigidity and strength and light inherent color

Features

heat stabilised 130

Regulatory

ul

Properties

Modulus

20.500MPa

Strength

270MPa

Impact

105kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
20500 MPa
15800 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
270 MPa
190 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,4 %
2,5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
105 kJ/m²
107 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
20 kJ/m²
22 kJ/m²

UV Exposure and Water Immersion

UL 746C

UL
f2

Thermal Properties

RTI electrical

UL 746B

UL
0,4mm Wall thickness
UL
0,8mm Wall thickness
UL
1,6mm Wall thickness
UL
3,2mm Wall thickness
130 °C
130 °C
130 °C
130 °C

RTI impact

UL 746B

UL
0,8mm Wall thickness
UL
1,6mm Wall thickness
UL
3,2mm Wall thickness
120 °C
120 °C
120 °C

RTI strength

UL 746B

UL
0,8mm Wall thickness
UL
1,6mm Wall thickness
UL
3,2mm Wall thickness
130 °C
130 °C
130 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 °C

Flammability

Burning rate

UL 94

UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
HB Class
HB Class
HB Class

HWI

UL 746A

UL
0,4 mm Wall thickness
UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
4 PLC
4 PLC
4 PLC
4 PLC

HAI

UL 746A

UL
0,4 mm Wall thickness
UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
0 PLC
0 PLC
0 PLC
0 PLC

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,71 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,2 %
0,4 - 0,6 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

UL
d.a.m.
1011 Ω x cm

Comparative tracking index

IEC 60112

Test liquid A
600 V

Comparative tracking index

ASTM D3638

UL
0 PLC

Dielectric strength

IEC 60243

UL
3 mm
12 kV/mm

High voltage arc tracking rate (HVTR)

UL 746A

UL
1 PLC

High Volt, Low Current Arc Resistance

ASTM D495

UL
5 PLC

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.