Find the right compound
Select your fitting and find the right compound for your intend
AKROMID®
B3 3 S3 10 natural (1808)
PA6-I
AKROMID® B3 3 S3 10 natural (1808) - PA 6 unreinforced and cold impact modified, e.g. for the furniture industry
2.700MPa
70MPa
180kJ/m²
AKROMID® B3 3 S3 10 natural (1808) - PA 6 unreinforced and cold impact modified, e.g. for the furniture industry
AKROMID®
B3 GM 10/20 1 black (1829)
PA6 (GF10+GB20)
AKROMID® B3 GM 10/20 1 black 950058 (1829) is a 10% glass fibre reinforced, 20% glass bead filled, heat stabilised polyamide 6 with good surface and low warpage
6.200MPa
115MPa
45kJ/m²
AKROMID® B3 GM 10/20 1 black 950058 (1829) is a 10% glass fibre reinforced, 20% glass bead filled, heat stabilised polyamide 6 with good surface and low warpage
AKROMID®
A3 1 natural (2416)
PA66
AKROMID® A3 1 natural (2416) - heat stabilised, unreinforced polyamide 6.6
3.200MPa
85MPa
180kJ/m²
AKROMID® A3 1 natural (2416) - heat stabilised, unreinforced polyamide 6.6
AKROMID®
A3 1 black (2417)
PA66
AKROMID® A3 1 black (2417) is a heat stabilised, unreinforced polyamide 6.6
3.200MPa
85MPa
180kJ/m²
AKROMID® A3 1 black (2417) is a heat stabilised, unreinforced polyamide 6.6
AKROMID®
A3 GK 30 black (2306)
PA66 GB30
AKROMID® A3 GK 30 black (2306) - PA 6.6, 30% glass beads reinforced, good surface, low warpage
5.000MPa
90MPa
28kJ/m²
AKROMID® A3 GK 30 black (2306) - PA 6.6, 30% glass beads reinforced, good surface, low warpage
AKROMID®
B3 GF 60 1 natural (2468)
PA6 GF60
AKROMID® B3 GF 60 1 natural (2468) is a 60% glass fibre reinforced heat stabilised polyamide 6 with very high rigidity and strength and light inherent color.
21.000MPa
240MPa
90kJ/m²
AKROMID® B3 GF 60 1 natural (2468) is a 60% glass fibre reinforced heat stabilised polyamide 6 with very high rigidity and strength and light inherent color.
AKROMID®
B3 GF 40 1 black (2487)
PA6 GF40
AKROMID® B3 GF 40 1 black (2487) is a 40% glass fibre reinforced, heat stabilised polyamide 6 with high rigidity and strength.
12.800MPa
205MPa
100kJ/m²
AKROMID® B3 GF 40 1 black (2487) is a 40% glass fibre reinforced, heat stabilised polyamide 6 with high rigidity and strength.
AKROMID®
B3 GF 15 S1 black (3228)PA6-I GF15
AKROMID® B3 GF 15 S1 black (3228) is a 15% glass fiber reinforced, impact modified Polyamide 6. It is characterised by medium stiffness and strength as well as a higher impact strength compared to a standard PA 6 GF 15. It also has good surface properties. The material is therefore perfectly suitable for toughness demanding but high integrated parts with a good surface appearance in the automotive, electro, and furniture industry.
Features
Properties
5.500MPa
110MPa
70kJ/m²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Flexural modulus
ISO 178
Flexural strength
ISO 178
Flexural strain at break
ISO 178
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Melting temperature
ISO 11357-3
Coefficient of linear thermal expansion
ISO 11359-1/2
Flammability
Burning rate
UL 94
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Molding shrinkage
ISO 294-4
Rheological Properties
MVR
ISO 1133
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.