AKROMID®

B3 GK 15 natural (1824)

PA6 GB15

AKROMID® B3 GK 15 natural (1824) - PA 6, 15% glass beads reinforced, good surface, low warpage

Modulus

4.000MPa

Strength

85MPa

Impact

30kJ/m²

AKROMID® B3 GK 15 natural (1824) - PA 6, 15% glass beads reinforced, good surface, low warpage

AKROMID®

B3 GM 10/20 1 black (1829)

PA6 (GF10+GB20)

AKROMID® B3 GM 10/20 1 black 950058 (1829) is a 10% glass fibre reinforced, 20% glass bead filled, heat stabilised polyamide 6 with good surface and low warpage

Modulus

6.200MPa

Strength

115MPa

Impact

45kJ/m²

AKROMID® B3 GM 10/20 1 black 950058 (1829) is a 10% glass fibre reinforced, 20% glass bead filled, heat stabilised polyamide 6 with good surface and low warpage

AKROMID®

A3 1 black (2417)

PA66

AKROMID® A3 1 black (2417) is a heat stabilised, unreinforced polyamide 6.6

Modulus

3.200MPa

Strength

85MPa

Impact

180kJ/m²

AKROMID® A3 1 black (2417) is a heat stabilised, unreinforced polyamide 6.6

AKROMID®

A3 1 natural (2416)

PA66

AKROMID® A3 1 natural (2416) - heat stabilised, unreinforced polyamide 6.6

Modulus

3.200MPa

Strength

85MPa

Impact

180kJ/m²

AKROMID® A3 1 natural (2416) - heat stabilised, unreinforced polyamide 6.6

AKROMID®

A3 GK 30 black (2306)

PA66 GB30

AKROMID® A3 GK 30 black (2306) - PA 6.6, 30% glass beads reinforced, good surface, low warpage

Modulus

5.000MPa

Strength

90MPa

Impact

28kJ/m²

AKROMID® A3 GK 30 black (2306) - PA 6.6, 30% glass beads reinforced, good surface, low warpage

AKROMID®

B3 GF 40 1 natural (2466)

PA6 GF40

AKROMID® B3 GF 40 1 natural (2466) is a 40% glass fibre reinforced, heat stabilised polyamide 6 with high rigidity and strength and light inherent color

Modulus

12.800MPa

Strength

205MPa

Impact

100kJ/m²

AKROMID® B3 GF 40 1 natural (2466) is a 40% glass fibre reinforced, heat stabilised polyamide 6 with high rigidity and strength and light inherent color

AKROMID®

B3 GF 60 natural (2476)

PA6 GF60

AKROMID® B3 GF 60 natural (2476) is a 60% glass fibre reinforced polyamide 6 with very high rigidity and strength and light inherent color

Modulus

21.000MPa

Strength

240MPa

Impact

90kJ/m²

AKROMID® B3 GF 60 natural (2476) is a 60% glass fibre reinforced polyamide 6 with very high rigidity and strength and light inherent color

163646580

AKROMID®

Preliminary

A3 1 S3 black (11392)PA66-I

AKROMID® A3 1 S3 black (11392) is an unreinforced, impact modified Polyamide 66. It is characterised by a medium dry impact strength whilst maintaining good flowability and low emission. Furthermore, the material is heat stabilised and therefore perfectly suitable for connecting and fixing systems which are used at elevated temperatures in the automotive and electronic industry. Its good flowability qualifies the material for processing in multi-cavity moulds. It was developed as successor of AKROMID® A3 1 S3 black (1139) to meet the stringent demand concerning emission values of automotive interior applications.

Features

heat stabilised 130
impact modified

Properties

Modulus

2.300MPa

Strength

60MPa

Impact

180kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
2300 MPa
1000 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
60 MPa
42 MPa

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
> 25 %
> 100 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2300 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
86 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
no break
no break

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
15 kJ/m²
95 kJ/m²
8 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
65 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 °C

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
20.000 h
129 °C
110 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,1 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,1 %

Molding shrinkage

ISO 294-4

flow
transverse
1,3 - 1,5 %
1,5 - 1,7 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
1015 Ω x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
1014 Ω

Rheological Properties

Flowability

AKRO

1 mm Thickness
2 mm Thickness
190 mm
620 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more