AKROMID®

Preliminary

B3 GKM 40 7 natural (8678)

PA6 M40

AKROMID® B3 GKM 40 7 natural (8678) - PA 6, mineral and glass beads, excellent surface properties, low warpage, chrome plating, adhesion to TPV, low odor, sanitary industry, automotive.

Modulus

5.100MPa

Strength

80MPa

Impact

70kJ/m²

AKROMID® B3 GKM 40 7 natural (8678) - PA 6, mineral and glass beads, excellent surface properties, low warpage, chrome plating, adhesion to TPV, low odor, sanitary industry, automotive.

AKROMID®

UL

B3 GF 35 1 HU black (8413)

PA6 GF35

AKROMID® B3 GF 35 1 HU black (8413) - PA 6, 35% glass fibre, heat ageing resistant, high rigidity and strength, UL listed HB.

Modulus

11.500MPa

Strength

195MPa

Impact

100kJ/m²

AKROMID® B3 GF 35 1 HU black (8413) - PA 6, 35% glass fibre, heat ageing resistant, high rigidity and strength, UL listed HB.

AKROMID®

Preliminary

B3 GKM 40 black (8632)

PA6 M40

AKROMID® B3 GKM 40 black (8632) - PA 6, mineral and glass beads, excellent surface properties, low warpage, sanitary industry, automotive, chrome plating, adhesion to TPV, low odor.

Modulus

4.700MPa

Strength

70MPa

Impact

150kJ/m²

AKROMID® B3 GKM 40 black (8632) - PA 6, mineral and glass beads, excellent surface properties, low warpage, sanitary industry, automotive, chrome plating, adhesion to TPV, low odor.

AKROMID®

Preliminary

B3 GKM 40 natural (8630)

PA6 M40

AKROMID® B3 GKM 40 natur (8630) - PA 6, mineral and glass beads, excellent surface properties, low warpage, chrome plating, adhesion to TPV, low odor, sanitary industry, automotive.

Modulus

4.900MPa

Strength

70MPa

Impact

150kJ/m²

AKROMID® B3 GKM 40 natur (8630) - PA 6, mineral and glass beads, excellent surface properties, low warpage, chrome plating, adhesion to TPV, low odor, sanitary industry, automotive.

AKROMID®

A3 1 S3 black (1139)

PA66-I

AKROMID® A3 1 S3 black (1139) - PA 6.6 unreinforced, impact modified whilst maintaining good flowability, for connecting and fixing systems

Modulus

2.700MPa

Strength

63MPa

Impact

180kJ/m²

AKROMID® A3 1 S3 black (1139) - PA 6.6 unreinforced, impact modified whilst maintaining good flowability, for connecting and fixing systems

AKROMID®

B3 natural (1024)

PA6

AKROMID® B3 natural (1024) is an unreinforced polyamide 6 with light inherent color

Modulus

3.200MPa

Strength

83MPa

Impact

180kJ/m²

AKROMID® B3 natural (1024) is an unreinforced polyamide 6 with light inherent color

AKROMID®

B3 3 S3 10 natural (1808)

PA6-I

AKROMID® B3 3 S3 10 natural (1808) - PA 6 unreinforced and cold impact modified, e.g. for the furniture industry

Modulus

2.700MPa

Strength

70MPa

Impact

180kJ/m²

AKROMID® B3 3 S3 10 natural (1808) - PA 6 unreinforced and cold impact modified, e.g. for the furniture industry

162636480

AKROMID®

UL

B28 GM 15/15 1 FR black (8750)PA6 (GF15+GB15) FR(40)

AKROMID® B28 GM 15/15 1 FR black (8750) is a flame retardant PA6 reinforced with 15% glass fibres and 15% glass beads. The flame retardant system is free of halogens and red phosphorus. Due to its good flowability, it is characterised by easy processability as well as good surface properties. The product is suitable for enclosure applications in the E&E industry due to its low warpage, high stiffness and strength. This grade is excellent for laser marking.

Features

flame retardant
laser markable
surface modified
low warpage
easy flow
E&E

Regulatory

ul

Properties

Modulus

8.400MPa

Strength

105MPa

Impact

45kJ/m²

Sustainability

Recycled content

15 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
8400 MPa
5200 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
105 MPa
65 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,7 %
4,5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
45 kJ/m²
40 kJ/m²
40 kJ/m²
35 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
7 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
200 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
217 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
102 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Burning rate

UL 94

UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
V-0 Class
V-0 Class
V-0 Class

GWFI

IEC 60695-2-12

0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
960 °C
960 °C
960 °C

GWIT

IEC 60695-2-13

1,6 mm Wall thickness
775 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,44 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,65 - 0,85 %
0,75 - 0,95 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more