HEADER Granulat 1920x700

Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/m²
558 Compounds found
Recommended  
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

AKROMID®

Preliminary

B3 GKM 40 natural (8630)

PA6 M40

AKROMID® B3 GKM 40 natur (8630) - PA 6, mineral and glass beads, excellent surface properties, low warpage, chrome plating, adhesion to TPV, low odor, sanitary industry, automotive.

Modulus

4.900MPa

Strength

70MPa

Impact

150kJ/m²

AKROMID® B3 GKM 40 natur (8630) - PA 6, mineral and glass beads, excellent surface properties, low warpage, chrome plating, adhesion to TPV, low odor, sanitary industry, automotive.

AKROMID®

UL

B3 GF 35 1 HU black (8413)

PA6 GF35

AKROMID® B3 GF 35 1 HU black (8413) - PA 6, 35% glass fibre, heat ageing resistant, high rigidity and strength, UL listed HB.

Modulus

11.500MPa

Strength

195MPa

Impact

100kJ/m²

AKROMID® B3 GF 35 1 HU black (8413) - PA 6, 35% glass fibre, heat ageing resistant, high rigidity and strength, UL listed HB.

AKROMID®

Preliminary

B3 GKM 40 7 natural (8678)

PA6 M40

AKROMID® B3 GKM 40 7 natural (8678) - PA 6, mineral and glass beads, excellent surface properties, low warpage, chrome plating, adhesion to TPV, low odor, sanitary industry, automotive.

Modulus

5.100MPa

Strength

80MPa

Impact

70kJ/m²

AKROMID® B3 GKM 40 7 natural (8678) - PA 6, mineral and glass beads, excellent surface properties, low warpage, chrome plating, adhesion to TPV, low odor, sanitary industry, automotive.

AKROMID®

Preliminary

B3 GKM 40 black (8632)

PA6 M40

AKROMID® B3 GKM 40 black (8632) - PA 6, mineral and glass beads, excellent surface properties, low warpage, sanitary industry, automotive, chrome plating, adhesion to TPV, low odor.

Modulus

4.700MPa

Strength

70MPa

Impact

150kJ/m²

AKROMID® B3 GKM 40 black (8632) - PA 6, mineral and glass beads, excellent surface properties, low warpage, sanitary industry, automotive, chrome plating, adhesion to TPV, low odor.

AKROMID®

B3 3 S3 10 natural (1808)

PA6-I

AKROMID® B3 3 S3 10 natural (1808) - PA 6 unreinforced and cold impact modified, e.g. for the furniture industry

Modulus

2.700MPa

Strength

70MPa

Impact

180kJ/m²

AKROMID® B3 3 S3 10 natural (1808) - PA 6 unreinforced and cold impact modified, e.g. for the furniture industry

AKROMID®

A3 1 S3 black (1139)

PA66-I

AKROMID® A3 1 S3 black (1139) - PA 6.6 unreinforced, impact modified whilst maintaining good flowability, for connecting and fixing systems

Modulus

2.700MPa

Strength

63MPa

Impact

180kJ/m²

AKROMID® A3 1 S3 black (1139) - PA 6.6 unreinforced, impact modified whilst maintaining good flowability, for connecting and fixing systems

AKROMID®

B3 natural (1024)

PA6

AKROMID® B3 natural (1024) is an unreinforced polyamide 6 with light inherent color

Modulus

3.200MPa

Strength

83MPa

Impact

180kJ/m²

AKROMID® B3 natural (1024) is an unreinforced polyamide 6 with light inherent color

162636480

AKROLOY®

Preliminary

PARA GF 35 FR orange (8039)PARA GF35 FR(40)

AKROLOY® PARA GF 35 FR orange (8039) is a flame retardant, 35% glass-fiber reinforced Polyarylamide with highest modulus and strength. The material is based on a flame retardant system that is free of red phosphorus and halogens and is colored in orange similar to RAL 2003. Due to its very good flowability, an improved surface quality is achieved. This grade is also suitable for applications in electrical industries, which need low creep even in conditioned state.

Features

electrically neutral
flame retardant
surface modified
reduced moisture
easy flow
E&E

Properties

Modulus

14.500MPa

Strength

190MPa

Impact

50kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
14500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
190 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
2,0 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
50 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
13 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
230 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
235 °C

Flammability

Burning rate

UL 94

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
V-0 Class
V-0 Class
V-0 Class
V-0 Class

GWFI

IEC 60695-2-12

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
960 °C
960 °C
960 °C
960 °C

GWIT

IEC 60695-2-13

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
825 °C
800 °C
800 °C
825 °C

General properties

Density

ISO 1183

23°C
1,48 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,2 - 0,4 %
0,4 - 0,6 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
1015 Ω x cm

Comparative tracking index

IEC 60112

Test liquid A
> 600 V

Dielectric strength

IEC 60243

1 mm
36 kV/mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more