HEADER Granulat 1920x700

Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/mĀ²
558 Compounds found
Recommended Ā 
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

AKROMIDĀ®

UL

B3 GF 35 1 HU black (8413)

PA6 GF35

AKROMIDĀ® B3 GF 35 1 HU black (8413) - PA 6, 35% glass fibre, heat ageing resistant, high rigidity and strength, UL listed HB.

Modulus

11.500MPa

Strength

195MPa

Impact

100kJ/mĀ²

AKROMIDĀ® B3 GF 35 1 HU black (8413) - PA 6, 35% glass fibre, heat ageing resistant, high rigidity and strength, UL listed HB.

AKROMIDĀ®

Preliminary

T91 GF 30 FR black (8184)

PPA GF30 FR(40)

AKROMIDĀ® T91 GF 30 FR black (8184) - PA9T, flame retardant, 30% glass fiber, high stiffness, high strength, free of halogenes, good flowability, low water uptake, reflow soldering, SMT devices, E&E, automotive.

Modulus

11.000MPa

Strength

140MPa

Impact

40kJ/mĀ²

AKROMIDĀ® T91 GF 30 FR black (8184) - PA9T, flame retardant, 30% glass fiber, high stiffness, high strength, free of halogenes, good flowability, low water uptake, reflow soldering, SMT devices, E&E, automotive.

AKROMIDĀ®

Preliminary

B3 GKM 40 black (8632)

PA6 M40

AKROMIDĀ® B3 GKM 40 black (8632) - PA 6, mineral and glass beads, excellent surface properties, low warpage, sanitary industry, automotive, chrome plating, adhesion to TPV, low odor.

Modulus

4.700MPa

Strength

70MPa

Impact

150kJ/mĀ²

AKROMIDĀ® B3 GKM 40 black (8632) - PA 6, mineral and glass beads, excellent surface properties, low warpage, sanitary industry, automotive, chrome plating, adhesion to TPV, low odor.

AKROMIDĀ®

Preliminary

B3 GKM 40 7 natural (8678)

PA6 M40

AKROMIDĀ® B3 GKM 40 7 natural (8678) - PA 6, mineral and glass beads, excellent surface properties, low warpage, chrome plating, adhesion to TPV, low odor, sanitary industry, automotive.

Modulus

5.100MPa

Strength

80MPa

Impact

70kJ/mĀ²

AKROMIDĀ® B3 GKM 40 7 natural (8678) - PA 6, mineral and glass beads, excellent surface properties, low warpage, chrome plating, adhesion to TPV, low odor, sanitary industry, automotive.

AKROMIDĀ®

B3 natural (1024)

PA6

AKROMIDĀ® B3 natural (1024) is an unreinforced polyamide 6 with light inherent color

Modulus

3.200MPa

Strength

83MPa

Impact

180kJ/mĀ²

AKROMIDĀ® B3 natural (1024) is an unreinforced polyamide 6 with light inherent color

AKROMIDĀ®

B3 GK 15 natural (1824)

PA6 GB15

AKROMIDĀ® B3 GK 15 natural (1824) - PA 6, 15% glass beads reinforced, good surface, low warpage

Modulus

4.000MPa

Strength

85MPa

Impact

30kJ/mĀ²

AKROMIDĀ® B3 GK 15 natural (1824) - PA 6, 15% glass beads reinforced, good surface, low warpage

AKROMIDĀ®

B3 3 S3 10 natural (1808)

PA6-I

AKROMIDĀ® B3 3 S3 10 natural (1808) - PA 6 unreinforced and cold impact modified, e.g. for the furniture industry

Modulus

2.700MPa

Strength

70MPa

Impact

180kJ/mĀ²

AKROMIDĀ® B3 3 S3 10 natural (1808) - PA 6 unreinforced and cold impact modified, e.g. for the furniture industry

162636480

AKROMIDĀ®

B28 GF 30 6 LT black (6931)PA6 GF30

AKROMIDĀ® B28 GF 30 6 LT black (6931) is a 30% glass fibre reinforced, easy flowing Polyamide 6. The material is characterised by high stiffness and strength. Furthermore, it is high heat stabilised and therefore perfectly suitable for automotive and industrial applications. The compound can be welded via laser welding.

Features

heat stabilised 160
laser transparent

Properties

Modulus

9.800MPa

Strength

185MPa

Impact

90kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
9800 MPa
6400 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
185 MPa
100 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3 %
5,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
8000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
250 MPa

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
90 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
12 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
210 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 Ā°C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,35 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
2,1 - 2,3 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.