HEADER Granulat 1920x700

Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/m²
558 Compounds found
Recommended  
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

AKROMID®

Preliminary

B3 GKM 40 black (8632)

PA6 M40

AKROMID® B3 GKM 40 black (8632) - PA 6, mineral and glass beads, excellent surface properties, low warpage, sanitary industry, automotive, chrome plating, adhesion to TPV, low odor.

Modulus

4.700MPa

Strength

70MPa

Impact

150kJ/m²

AKROMID® B3 GKM 40 black (8632) - PA 6, mineral and glass beads, excellent surface properties, low warpage, sanitary industry, automotive, chrome plating, adhesion to TPV, low odor.

AKROMID®

Preliminary

T91 GF 30 FR black (8184)

PPA GF30 FR(40)

AKROMID® T91 GF 30 FR black (8184) - PA9T, flame retardant, 30% glass fiber, high stiffness, high strength, free of halogenes, good flowability, low water uptake, reflow soldering, SMT devices, E&E, automotive.

Modulus

11.000MPa

Strength

140MPa

Impact

40kJ/m²

AKROMID® T91 GF 30 FR black (8184) - PA9T, flame retardant, 30% glass fiber, high stiffness, high strength, free of halogenes, good flowability, low water uptake, reflow soldering, SMT devices, E&E, automotive.

AKROMID®

Preliminary

B3 GKM 40 7 natural (8678)

PA6 M40

AKROMID® B3 GKM 40 7 natural (8678) - PA 6, mineral and glass beads, excellent surface properties, low warpage, chrome plating, adhesion to TPV, low odor, sanitary industry, automotive.

Modulus

5.100MPa

Strength

80MPa

Impact

70kJ/m²

AKROMID® B3 GKM 40 7 natural (8678) - PA 6, mineral and glass beads, excellent surface properties, low warpage, chrome plating, adhesion to TPV, low odor, sanitary industry, automotive.

AKROMID®

Preliminary

B3 GKM 40 natural (8630)

PA6 M40

AKROMID® B3 GKM 40 natur (8630) - PA 6, mineral and glass beads, excellent surface properties, low warpage, chrome plating, adhesion to TPV, low odor, sanitary industry, automotive.

Modulus

4.900MPa

Strength

70MPa

Impact

150kJ/m²

AKROMID® B3 GKM 40 natur (8630) - PA 6, mineral and glass beads, excellent surface properties, low warpage, chrome plating, adhesion to TPV, low odor, sanitary industry, automotive.

AKROMID®

A3 1 S3 black (1139)

PA66-I

AKROMID® A3 1 S3 black (1139) - PA 6.6 unreinforced, impact modified whilst maintaining good flowability, for connecting and fixing systems

Modulus

2.700MPa

Strength

63MPa

Impact

180kJ/m²

AKROMID® A3 1 S3 black (1139) - PA 6.6 unreinforced, impact modified whilst maintaining good flowability, for connecting and fixing systems

AKROMID®

B3 natural (1024)

PA6

AKROMID® B3 natural (1024) is an unreinforced polyamide 6 with light inherent color

Modulus

3.200MPa

Strength

83MPa

Impact

180kJ/m²

AKROMID® B3 natural (1024) is an unreinforced polyamide 6 with light inherent color

AKROMID®

B3 3 S3 10 natural (1808)

PA6-I

AKROMID® B3 3 S3 10 natural (1808) - PA 6 unreinforced and cold impact modified, e.g. for the furniture industry

Modulus

2.700MPa

Strength

70MPa

Impact

180kJ/m²

AKROMID® B3 3 S3 10 natural (1808) - PA 6 unreinforced and cold impact modified, e.g. for the furniture industry

162636480

AKROLOY®

PA GF 60 black (6418)PA66+PA6I/6T GF60

AKROLOY® PA GF 60 black (6418) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

Properties

Modulus

21.000MPa

Strength

275MPa

Impact

100kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
21000 MPa
20000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
275 MPa
225 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,4 %
2,4 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
21000 MPa
21000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
410 MPa
360 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
2,5 %
2,6 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
100 kJ/m²
100 kJ/m²
95 kJ/m²
95 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
19 kJ/m²
19 kJ/m²
18 kJ/m²
18 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
245 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
193 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
255 °C

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
20.000 h
150 °C
115 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,69 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,1 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,2 - 0,4 %

Rheological Properties

Flowability

AKRO

1 mm Thickness
2 mm Thickness
60 mm
200 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.