AKROMID®
B3 GF 20 1 black (2483)
PA6 GF20
AKROMID® B3 GF 20 1 black (2483) is a 20% glass fibre reinforced, heat stabilised polyamide 6 with medium stiffness and strength
6.800MPa
150MPa
73kJ/m²
AKROMID® B3 GF 20 1 black (2483) is a 20% glass fibre reinforced, heat stabilised polyamide 6 with medium stiffness and strength
AKROLOY®
PA GF 50 grey (3807)
PA66 + PA6I/6T GF50
AKROLOY® PA GF 50 grey (3807) is a 50% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength.
17.200MPa
250MPa
105kJ/m²
AKROLOY® PA GF 50 grey (3807) is a 50% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength.
AKROMID®
B3 LA black (4056)
PA6
AKROMID® B3 LA black (4056) - PA6, unreinforced, laser markable, E&E, automotive, industry
3.400MPa
85MPa
180kJ/m²
AKROMID® B3 LA black (4056) - PA6, unreinforced, laser markable, E&E, automotive, industry
AKROMID®
A3 1 S3 grey (2955)
PA66+PA6-I
AKROMID® A3 1 S3 grey (2955) - PA 6.6, unreinforced, impact modified, for connecting and fixing systems, automotive, E&E
2.500MPa
68MPa
180kJ/m²
AKROMID® A3 1 S3 grey (2955) - PA 6.6, unreinforced, impact modified, for connecting and fixing systems, automotive, E&E
AKROMID®
B3 GF 15 1 L natural (4690)
PA6+PP GF15
AKROMID® B3 GF 15 1 L natural (4690) - PA6/PP-Blend 15% glass fibre reinforced, lower density, cost reduced, calcium chloride
5.200MPa
110MPa
60kJ/m²
AKROMID® B3 GF 15 1 L natural (4690) - PA6/PP-Blend 15% glass fibre reinforced, lower density, cost reduced, calcium chloride
AKROMID®
T9 GF 35 4 black (7858)
PPA GF35
AKROMID® T9 GF 35 4 schwarz (7858) is a 35% glass fibre reinforced polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
11.000MPa
200MPa
75kJ/m²
AKROMID® T9 GF 35 4 schwarz (7858) is a 35% glass fibre reinforced polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
AKROMID®
A28 GF 40 1 natural (4919)
PA66 GF40
AKROMID® A28 GF 40 1 natural (4919) - 40% glass fiber reinforced, easy flowing PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry
13.000MPa
245MPa
95kJ/m²
AKROMID® A28 GF 40 1 natural (4919) - 40% glass fiber reinforced, easy flowing PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry
AKROMID®
B3 GF 40 1 HU black (8415)PA6 GF40
AKROMID® B3 GF 40 1 HU black (8415) is a 40% glass fibre reinforced, UV stabilised polyamide 6 with high rigidity and strength. This UL94 HB listed grade is suitable for technical components in mechanical engineering and the automotive industry.
Features
Regulatory
Properties
12.800MPa
205MPa
100kJ/m²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Flexural modulus
ISO 178
Flexural strength
ISO 178
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Temperature of deflection under load HDT/B
ISO 75
Temperature of deflection under load HDT/C
ISO 75
Melting temperature
ISO 11357-3
Temperature index for 50% loss of tensile strength
IEC 60216
Flammability
Burning rate
UL 94
GWFI
IEC 60695-2-12
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Water absorption
ISO 62
Molding shrinkage
ISO 294-4
Electrical Properties
Volume resistivity IEC
DIN EN IEC 62631-3-2
Surface resistivity
DIN EN 62631-3-2
Comparative tracking index
IEC 60112
Comparative tracking index
ASTM D3638
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.