AKROMID®

B3 1 L natural (4685)

PA6 + PP

AKROMID® B3 1 L natural (4685)- unreinforced PA6/PP-Blend lightweight, cost reduced

Modulus

2.400MPa

Strength

55MPa

Impact

180kJ/m²

AKROMID® B3 1 L natural (4685)- unreinforced PA6/PP-Blend lightweight, cost reduced

AKROMID®

B3 GF 15 1 L natural (4690)

PA6+PP GF15

AKROMID® B3 GF 15 1 L natural (4690) - PA6/PP-Blend 15% glass fibre reinforced, lower density, cost reduced, calcium chloride

Modulus

5.200MPa

Strength

110MPa

Impact

60kJ/m²

AKROMID® B3 GF 15 1 L natural (4690) - PA6/PP-Blend 15% glass fibre reinforced, lower density, cost reduced, calcium chloride

AKROMID®

B3 GF 10 natural (2829)

PA6 GF10

AKROMID® B3 GF 10 natural (2829) is a 10% glass fibre reinforced polyamide 6 with medium stiffness and strength and light inherent color.

Modulus

4.800MPa

Strength

105MPa

Impact

47kJ/m²

AKROMID® B3 GF 10 natural (2829) is a 10% glass fibre reinforced polyamide 6 with medium stiffness and strength and light inherent color.

AKROMID®

B3 1 L black (4525)

PA6+PP

AKROMID® B3 1 L schwarz (4525) - PA/PP-Blend lightweight, cost reduced

Modulus

2.300MPa

Strength

55MPa

Impact

180kJ/m²

AKROMID® B3 1 L schwarz (4525) - PA/PP-Blend lightweight, cost reduced

AKROMID®

B3 3 natural (5772)

PA6

AKROMID® B3 3 natural (5772) - PA6, unreinforced, nucleated, lubricated, Dryblend, furniture industry, automotive, cable gland

Modulus

3.200MPa

Strength

80MPa

Impact

NA

AKROMID® B3 3 natural (5772) - PA6, unreinforced, nucleated, lubricated, Dryblend, furniture industry, automotive, cable gland

AKROMID®

A3 GF 13 S3 natural (2788)

PA66-I GF13

AKROMID® A3 GF 13 S3 natural (2788) - PA 6.6, glass fiber reinforced, dry impact modified, for mechanical engineering and automotive industry

Modulus

5.200MPa

Strength

125MPa

Impact

75kJ/m²

AKROMID® A3 GF 13 S3 natural (2788) - PA 6.6, glass fiber reinforced, dry impact modified, for mechanical engineering and automotive industry

AKROMID®

A28 GF 40 1 natural (4919)

PA66 GF40

AKROMID® A28 GF 40 1 natural (4919) - 40% glass fiber reinforced, easy flowing PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

13.000MPa

Strength

245MPa

Impact

95kJ/m²

AKROMID® A28 GF 40 1 natural (4919) - 40% glass fiber reinforced, easy flowing PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

160616280

AKROMID®

A3 1 S3 15 natural (2892)PA66-I

AKROMID® A3 1 S3 15 natural (2892) is an unreinforced, impact modified Polyamide 66. It is characterised by a medium dry impact strength whilst maintaining good flowability. Furthermore, the material is heat stabilised and therefore perfectly suitable for connecting and fixing systems which are used at elevated temperatures in the automotive and electro industry. Its good flowability qualifies the material for processing in multi-cavity moulds. The material has a light inherent color.

Features

heat stabilised 130
impact modified

Properties

Modulus

2.700MPa

Strength

63MPa

Impact

180kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
2700 MPa
1300 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
63 MPa
45 MPa

Tensile strain at yield

ISO 527-2

50 mm/min | d.a.m.
7 %

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
> 35 %
> 100 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
no break
no break

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
15 kJ/m²
95 kJ/m²
10 kJ/m²

Izod notched impact strength

ISO 180/1A

23°C | d.a.m.
20°C | d.a.m.
-
40°C | d.a.m.
-
15 kJ/m²
12 kJ/m²
12 kJ/m²

Ball indentation hardness

ISO 2039-1

358N/30s | d.a.m.
93 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
70 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
213 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,1 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,1 %

Molding shrinkage

ISO 294-4

flow
transverse
1,3 - 1,5 %
1,5 - 1,7 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
1015 Ω x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
1014 Ω

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more