Find the right compound
Select your fitting and find the right compound for your intend
AKROMID®
T9 GF 15 S1 black (7820)
PPA-I GF15
AKROMID® T9 GF 15 S1 black (7820) is a 15% glass fibre reinforced, cold impact strength polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
5.000MPa
120MPa
73kJ/m²
AKROMID® T9 GF 15 S1 black (7820) is a 15% glass fibre reinforced, cold impact strength polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
AKROMID®
B3 GF 25 1 black (2484)
PA6 GF25
AKROMID® B3 GF 25 1 black (2484) is a 25% glass fibre reinforced, heat stabilised polyamide 6 with high stiffness and strength and light inherent color.
8.500MPa
160MPa
85kJ/m²
AKROMID® B3 GF 25 1 black (2484) is a 25% glass fibre reinforced, heat stabilised polyamide 6 with high stiffness and strength and light inherent color.
AKROMID®
A3 1 FR black (3051)
PA66 FR(30)
AKROMID® A3 1 FR black (3051) - PA6.6, unreinforced, flame retardant, UL-listed, E&E market.
3.500MPa
83MPa
70kJ/m²
AKROMID® A3 1 FR black (3051) - PA6.6, unreinforced, flame retardant, UL-listed, E&E market.
AKROMID®
NEXT B3 GF 30 1 L CI black (8375)
PA6 + PP GF30
AKROMID® NEXT B3 GF 30 1 L CI schwarz (8375) - PA6/PP-Blend, biomass-balanced, 30% glass fibre, lower density, good chemical resistance.
8.800MPa
140MPa
70kJ/m²
AKROMID® NEXT B3 GF 30 1 L CI schwarz (8375) - PA6/PP-Blend, biomass-balanced, 30% glass fibre, lower density, good chemical resistance.
AKROMID®
A3 GF 35 1 EN black (5300)
PA66 GF35
AKROMID® A3 GF 35 1 EN black (5300) is a 35% glass fibre reinforced, heat stabilised, electrical neutral polyamide 6.6 with high rigidity and strength
11.600MPa
215MPa
92kJ/m²
AKROMID® A3 GF 35 1 EN black (5300) is a 35% glass fibre reinforced, heat stabilised, electrical neutral polyamide 6.6 with high rigidity and strength
AKROMID®
B3 GF 50 black (2939)
PA6 GF50
AKROMID® B3 GF 50 black (2939) - 50% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry
17.000MPa
240MPa
100kJ/m²
AKROMID® B3 GF 50 black (2939) - 50% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry
AKROLOY®
PA GF 50 grey (3807)
PA66 + PA6I/6T GF50
AKROLOY® PA GF 50 grey (3807) is a 50% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength.
17.200MPa
250MPa
105kJ/m²
AKROLOY® PA GF 50 grey (3807) is a 50% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength.
AKROMID®
B3 GF 40 5 black (7286)PA6 GF40
AKROMID® B3 GF 40 5 black (7286) is a 40% glass fiber reinforced polyamide 6. It is characterised by a very high stiffness and strength. Furthermore, the material is high heat stabilised and therefore perfectly suitable for technical parts which are used at elevated temperatures in industrial engineering and in the automotive industry. As successor AKROMID® B3 GF 40 5 black (8636) was delevoped, to meet the stringent UV stability requirements for outdoor applications.
Features
Properties
12.500MPa
200MPa
95kJ/m²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Flexural modulus
ISO 178
Flexural strength
ISO 178
Flexural strain at break
ISO 178
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Temperature of deflection under load HDT/B
ISO 75
Melting temperature
ISO 11357-3
Flammability
Burning rate
UL 94
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Molding shrinkage
ISO 294-4
Rheological Properties
Flowability
AKRO
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.