AKROMIDĀ®
A3 GF 30 4 natural (3752)
PA66 GF30
AKROMIDĀ® A3 GF 30 4 natural (3752) is a 30% glass fibre reinforced, hydrolysis-/ chemical stabilised polyamide 6.6 with high stiffness and strength and light inherent color
11.500MPa
210MPa
100kJ/mĀ²
AKROMIDĀ® A3 GF 30 4 natural (3752) is a 30% glass fibre reinforced, hydrolysis-/ chemical stabilised polyamide 6.6 with high stiffness and strength and light inherent color
AKROMIDĀ®
B3 GF 30 S1 white (3767)
PA6-I GF30
AKROMIDĀ® B3 GF 30 S1 white (3767) - PA 6, 30% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive
9.000MPa
160MPa
105kJ/mĀ²
AKROMIDĀ® B3 GF 30 S1 white (3767) - PA 6, 30% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive
AKROMIDĀ®
B3 GF 50 S1 natural (3694)
PA6-I GF50
AKROMIDĀ® B3 GF 50 S1 natural (3694) - PA 6, 50% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive
14.500MPa
190MPa
110kJ/mĀ²
AKROMIDĀ® B3 GF 50 S1 natural (3694) - PA 6, 50% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive
AKROMIDĀ®
B3 1 L black (4525)
PA6+PP
AKROMIDĀ® B3 1 L schwarz (4525) - PA/PP-Blend lightweight, cost reduced
2.300MPa
55MPa
180kJ/mĀ²
AKROMIDĀ® B3 1 L schwarz (4525) - PA/PP-Blend lightweight, cost reduced
AKROMIDĀ®
B3 GF 15 1 L natural (4690)
PA6+PP GF15
AKROMIDĀ® B3 GF 15 1 L natural (4690) - PA6/PP-Blend 15% glass fibre reinforced, lower density, cost reduced, calcium chloride
5.200MPa
110MPa
60kJ/mĀ²
AKROMIDĀ® B3 GF 15 1 L natural (4690) - PA6/PP-Blend 15% glass fibre reinforced, lower density, cost reduced, calcium chloride
AKROMIDĀ®
T9 GF 15 S1 black (7820)
PPA-I GF15
AKROMIDĀ® T9 GF 15 S1 black (7820) is a 15% glass fibre reinforced, cold impact strength polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
5.000MPa
120MPa
73kJ/mĀ²
AKROMIDĀ® T9 GF 15 S1 black (7820) is a 15% glass fibre reinforced, cold impact strength polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
AKROMIDĀ®
T9 GF 35 4 black (7858)
PPA GF35
AKROMIDĀ® T9 GF 35 4 schwarz (7858) is a 35% glass fibre reinforced polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
11.000MPa
200MPa
75kJ/mĀ²
AKROMIDĀ® T9 GF 35 4 schwarz (7858) is a 35% glass fibre reinforced polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
AKROMIDĀ®
A28 GF 40 1 natural (4919)PA66 GF40
AKROMIDĀ® A3 GF 40 1 natural (2393) is a 40% glass fiber reinforced, easy flowing polyamide 6.6. It is characterised by a very high stiffness and strength. Furthermore, the material is heat stabilised and therefore perfectly suitable for technical parts and housings in industrial engineering and in the automotive industry. The material has a light inherent color.
Features
Properties
13.000MPa
245MPa
95kJ/mĀ²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Temperature of deflection under load HDT/B
ISO 75
Temperature of deflection under load HDT/C
ISO 75
Melting temperature
ISO 11357-3
Flammability
Burning rate
UL 94
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Molding shrinkage
ISO 294-4
Electrical Properties
Volume resistivity IEC
DIN EN IEC 62631-3-2
Surface resistivity
DIN EN 62631-3-2
Comparative tracking index
IEC 60112
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.