AKROMIDĀ®

A3 GF 25 FR natural (7649)

PA66 GF25 FR(40)

AKROMIDĀ® A3 GF 25 FR natural (7649) is a 25% glass fibre reinforced, halogen and red phosphourus free flame retardant polyamide 6.6 with high stiffness and strength and light inherent color

Modulus

9.200MPa

Strength

135MPa

Impact

63kJ/mĀ²

AKROMIDĀ® A3 GF 25 FR natural (7649) is a 25% glass fibre reinforced, halogen and red phosphourus free flame retardant polyamide 6.6 with high stiffness and strength and light inherent color

AKROMIDĀ®

Preliminary

T9 GF 15 S1 black (7820)

PPA-I GF15

AKROMIDĀ® T9 GF 15 S1 black (7820) is a 15% glass fibre reinforced, cold impact strength polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.

Modulus

5.000MPa

Strength

120MPa

Impact

73kJ/mĀ²

AKROMIDĀ® T9 GF 15 S1 black (7820) is a 15% glass fibre reinforced, cold impact strength polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.

AKROMIDĀ®

Preliminary

T91 GF 30 FR black (8184)

PPA GF30 FR(40)

AKROMIDĀ® T91 GF 30 FR black (8184) - PA9T, flame retardant, 30% glass fiber, high stiffness, high strength, free of halogenes, good flowability, low water uptake, reflow soldering, SMT devices, E&E, automotive.

Modulus

11.000MPa

Strength

140MPa

Impact

40kJ/mĀ²

AKROMIDĀ® T91 GF 30 FR black (8184) - PA9T, flame retardant, 30% glass fiber, high stiffness, high strength, free of halogenes, good flowability, low water uptake, reflow soldering, SMT devices, E&E, automotive.

AKROMIDĀ®

UL

A3 1 FR black (3051)

PA66 FR(30)

AKROMIDĀ® A3 1 FR black (3051) - PA6.6, unreinforced, flame retardant, UL-listed, E&E market.

Modulus

3.500MPa

Strength

83MPa

Impact

70kJ/mĀ²

AKROMIDĀ® A3 1 FR black (3051) - PA6.6, unreinforced, flame retardant, UL-listed, E&E market.

AKROMIDĀ®

A3 GF 13 S3 black (3768)

PA66-I GF13

AKROMIDĀ® A3 GF 13 S3 black (3768) - PA 6.6, glass fiber reinforced, dry impact modified, for mechanical engineering and automotive industry

Modulus

5.200MPa

Strength

125MPa

Impact

75kJ/mĀ²

AKROMIDĀ® A3 GF 13 S3 black (3768) - PA 6.6, glass fiber reinforced, dry impact modified, for mechanical engineering and automotive industry

AKROMIDĀ®

A28 GF 40 1 natural (4919)

PA66 GF40

AKROMIDĀ® A28 GF 40 1 natural (4919) - 40% glass fiber reinforced, easy flowing PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

13.000MPa

Strength

245MPa

Impact

95kJ/mĀ²

AKROMIDĀ® A28 GF 40 1 natural (4919) - 40% glass fiber reinforced, easy flowing PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMIDĀ®

B3 ICF 20 black (5103)

PA6 CF20

AKROMIDĀ® B3 ICF 20 black (5103) is a 20% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties

Modulus

13.500MPa

Strength

150MPa

Impact

55kJ/mĀ²

AKROMIDĀ® B3 ICF 20 black (5103) is a 20% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties

158596080

AKROMIDĀ®

A3 GF 25 3 black (3094)PA66 GF25

AKROMIDĀ® A3 GF 25 3 black (3094) is a 25% glass fibre reinforced, nucleated polyamide 6.6 with high stiffness and strength

Features

nucleated

Properties

Modulus

8.500MPa

Strength

160MPa

Impact

50kJ/mĀ²

Sustainability

Recycled content

30 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
8500 MPa
6000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
160 MPa
110 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3 %
6 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
6600 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
230 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
3,6 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
50 kJ/mĀ²
70 kJ/mĀ²
45 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
6 kJ/mĀ²
10 kJ/mĀ²

Izod notched impact strength

ISO 180/1A

23Ā°C | d.a.m.
6 kJ/mĀ²

Thermal Properties

Melting temperature

ISO 11357-3

DSC, 10K/min
262 Ā°C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,32 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
2 - 2,2 %

Molding shrinkage

ISO 294-4

flow
transverse
0,15 - 0,35 %
0,75 - 0,95 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.