AKROMID®

B3 GF 30 S1 white (3767)

PA6-I GF30

AKROMID® B3 GF 30 S1 white (3767) - PA 6, 30% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive

Modulus

9.000MPa

Strength

160MPa

Impact

105kJ/m²

AKROMID® B3 GF 30 S1 white (3767) - PA 6, 30% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive

AKROMID®

A3 GF 13 S3 black (3768)

PA66-I GF13

AKROMID® A3 GF 13 S3 black (3768) - PA 6.6, glass fiber reinforced, dry impact modified, for mechanical engineering and automotive industry

Modulus

5.200MPa

Strength

125MPa

Impact

75kJ/m²

AKROMID® A3 GF 13 S3 black (3768) - PA 6.6, glass fiber reinforced, dry impact modified, for mechanical engineering and automotive industry

AKROLOY®

PA GF 50 grey (3807)

PA66 + PA6I/6T GF50

AKROLOY® PA GF 50 grey (3807) is a 50% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength.

Modulus

17.200MPa

Strength

250MPa

Impact

105kJ/m²

AKROLOY® PA GF 50 grey (3807) is a 50% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength.

AKROMID®

A28 GF 40 1 natural (4919)

PA66 GF40

AKROMID® A28 GF 40 1 natural (4919) - 40% glass fiber reinforced, easy flowing PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

13.000MPa

Strength

245MPa

Impact

95kJ/m²

AKROMID® A28 GF 40 1 natural (4919) - 40% glass fiber reinforced, easy flowing PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMID®

B3 ICF 20 black (5103)

PA6 CF20

AKROMID® B3 ICF 20 black (5103) is a 20% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties

Modulus

13.500MPa

Strength

150MPa

Impact

55kJ/m²

AKROMID® B3 ICF 20 black (5103) is a 20% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties

AKROMID®

B3 GF 10 natural (2829)

PA6 GF10

AKROMID® B3 GF 10 natural (2829) is a 10% glass fibre reinforced polyamide 6 with medium stiffness and strength and light inherent color.

Modulus

4.800MPa

Strength

105MPa

Impact

47kJ/m²

AKROMID® B3 GF 10 natural (2829) is a 10% glass fibre reinforced polyamide 6 with medium stiffness and strength and light inherent color.

AKROMID®

B3 LA black (4056)

PA6

AKROMID® B3 LA black (4056) - PA6, unreinforced, laser markable, E&E, automotive, industry

Modulus

3.400MPa

Strength

85MPa

Impact

180kJ/m²

AKROMID® B3 LA black (4056) - PA6, unreinforced, laser markable, E&E, automotive, industry

157585980

AKROMID®

Preliminary
Internal

B3 S1 natural (8084)PA6-I

AKROMID® B3 S1 natural (8084) is an unreinforced, impact modified Polyamide 6. The material is characterised by a very high impact strength even at low temperatures and is therefore perfectly suitable for mountings and dowels in the furniture and construction industry as well as parts for sport and leisure. The material has a light inherent color.

Features

impact modified

Properties

Modulus

1.700MPa

Strength

45MPa

Impact

180kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
1700 MPa
540 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
45 MPa
30 MPa

Tensile strain at yield

ISO 527-2

50 mm/min | d.a.m.
4,5 %

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
> 100 %
> 200 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
1400 MPa
530 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
55 MPa
25 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
no break
no break
no break
no break

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
75 kJ/m²
> 100 kJ/m²
40 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
52 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,07 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2 %

Molding shrinkage

ISO 294-4

flow
transverse
1,0 - 1,2 %
1,1 - 1,3 %

Electrical Properties

Surface resistivity

DIN EN 62631-3-2

d.a.m.
1012 Ω

Comparative tracking index

IEC 60112

Test liquid A
600 V

Dielectric strength

IEC 60243

3 mm
20 kV/mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.