AKROMID®

B3 GF 50 S1 black (2000)

PA6-I GF50

AKROMID® B3 GF 50 S1 black 950089 (2000) - PA 6, 50% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive

Modulus

15.000MPa

Strength

190MPa

Impact

100kJ/m²

AKROMID® B3 GF 50 S1 black 950089 (2000) - PA 6, 50% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive

AKROMID®

A3 GF 25 1 black (2384)

PA66 GF25

AKROMID® A3 GF 25 1 black (2384) is a 25% glass fibre reinforced, heat stabilised polyamide 6.6 with high stiffness and strength.

Modulus

8.500MPa

Strength

175MPa

Impact

70kJ/m²

AKROMID® A3 GF 25 1 black (2384) is a 25% glass fibre reinforced, heat stabilised polyamide 6.6 with high stiffness and strength.

AKROMID®

A3 S1 natural (2310)

PA66-I

AKROMID® A3 S1 natural (2310) - PA 6.6, unreinforced, cold impact modified, for connecting and fixing systems, automotive, E&E

Modulus

2.000MPa

Strength

50MPa

Impact

180kJ/m²

AKROMID® A3 S1 natural (2310) - PA 6.6, unreinforced, cold impact modified, for connecting and fixing systems, automotive, E&E

AKROMID®

B3 GF 15 S3 black (2345)

PA6-I GF15

AKROMID® B3 GF 15 S3 black (2345) - PA 6 with 15% glass fiber reinforcement and impact modified, good surface appearance

Modulus

5.500MPa

Strength

110MPa

Impact

75kJ/m²

AKROMID® B3 GF 15 S3 black (2345) - PA 6 with 15% glass fiber reinforcement and impact modified, good surface appearance

AKROMID®

A3 GF 40 1 natural (2381)

PA66 GF40

AKROMID® A3 GF 40 1 natural (2381) is a 40% glass fibre reinforced, heat stabilised polyamide 6.6 with high rigidity and strength and light inherent color.

Modulus

13.100MPa

Strength

225MPa

Impact

100kJ/m²

AKROMID® A3 GF 40 1 natural (2381) is a 40% glass fibre reinforced, heat stabilised polyamide 6.6 with high rigidity and strength and light inherent color.

AKROMID®

A3 GF 15 1 black (2382)

PA66 GF15

AKROMID® A3 GF 15 1 black (2382) is a 15% glass fibre reinforced, heat stabilised polyamide 6.6 with medium stiffness and strength.

Modulus

6.400MPa

Strength

140MPa

Impact

35kJ/m²

AKROMID® A3 GF 15 1 black (2382) is a 15% glass fibre reinforced, heat stabilised polyamide 6.6 with medium stiffness and strength.

AKROMID®

A3 GF 15 1 natural (2308)

PA66 GF15

AKROMID® A3 GF 15 1 natural (2308) - 15% glass fibre, heat stabilised, polyamide 6.6, medium stiffness and strength

Modulus

6.400MPa

Strength

140MPa

Impact

45kJ/m²

AKROMID® A3 GF 15 1 natural (2308) - 15% glass fibre, heat stabilised, polyamide 6.6, medium stiffness and strength

156575880

PRECITE®

Preliminary

P3 GF 30 9 FR natural (8053)PBT GF30 FR(40)

PRECITE® P3 GF 30 9 FR natural (8053) is a 30% glass fibre reinforced, flame retardant polybutylene terephthalate (PBT) with high stiffness and strength. The material offers outstanding long-term heat-aging stability as well as mechanical advantages to conventional products. It achieves V0 classification at thicknesses of 1.6 mm and above by using a flame retardant system which is free of red phosphorous and halogens. Due to its low moisture absorption, this material has very good dimensional stability and it is particularly suitable for precision parts in E-Mobility or E&E industry.

Features

heat stabilised 130
flame retardant
low warpage
E&E
E-Mobility

Properties

Modulus

10.500MPa

Strength

122MPa

Impact

50kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
10500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
122 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
2,4 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
10500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
197 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2,6 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
30°C | d.a.m.
-
50 kJ/m²
59 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
30°C | d.a.m.
-
9 kJ/m²
9 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
205 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
222 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
224 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
V-0 Class

GWFI

IEC 60695-2-12

0,8 mm Wall thickness
1,6 mm Wall thickness
960 °C
960 °C

GWIT

IEC 60695-2-13

0,8 mm Wall thickness
1,6 mm Wall thickness
750 °C
750 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

Oxygen index

ISO 4589-2

> 30 %

General properties

Density

ISO 1183

23°C
1,53 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,1 - 0,3 %

Electrical Properties

Comparative tracking index

IEC 60112

Test liquid A
350 V

Rheological Properties

MVR

ISO 1133

275°C/2,16kg
25,5 cm³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more