AKROMIDĀ®

B3 GM 15/15 black (1830)

PA6 (GF15+GB15)

AKROMIDĀ® B3 GM 15/15 black (1830) is a 15% glass fibre and 15% glass bead reinforced polyamide 6 with good surface and low warpage

Modulus

7.200MPa

Strength

130MPa

Impact

64kJ/mĀ²

AKROMIDĀ® B3 GM 15/15 black (1830) is a 15% glass fibre and 15% glass bead reinforced polyamide 6 with good surface and low warpage

AKROMIDĀ®

A3 GF 15 1 black (2382)

PA66 GF15

AKROMIDĀ® A3 GF 15 1 black (2382) is a 15% glass fibre reinforced, heat stabilised polyamide 6.6 with medium stiffness and strength.

Modulus

6.400MPa

Strength

140MPa

Impact

35kJ/mĀ²

AKROMIDĀ® A3 GF 15 1 black (2382) is a 15% glass fibre reinforced, heat stabilised polyamide 6.6 with medium stiffness and strength.

AKROMIDĀ®

B3 GF 15 S3 black (2345)

PA6-I GF15

AKROMIDĀ® B3 GF 15 S3 black (2345) - PA 6 with 15% glass fiber reinforcement and impact modified, good surface appearance

Modulus

5.500MPa

Strength

110MPa

Impact

75kJ/mĀ²

AKROMIDĀ® B3 GF 15 S3 black (2345) - PA 6 with 15% glass fiber reinforcement and impact modified, good surface appearance

AKROMIDĀ®

A3 GF 40 1 natural (2381)

PA66 GF40

AKROMIDĀ® A3 GF 40 1 natural (2381) is a 40% glass fibre reinforced, heat stabilised polyamide 6.6 with high rigidity and strength and light inherent color.

Modulus

13.100MPa

Strength

225MPa

Impact

100kJ/mĀ²

AKROMIDĀ® A3 GF 40 1 natural (2381) is a 40% glass fibre reinforced, heat stabilised polyamide 6.6 with high rigidity and strength and light inherent color.

AKROMIDĀ®

A3 GF 15 1 natural (2308)

PA66 GF15

AKROMIDĀ® A3 GF 15 1 natural (2308) - 15% glass fibre, heat stabilised, polyamide 6.6, medium stiffness and strength

Modulus

6.400MPa

Strength

140MPa

Impact

45kJ/mĀ²

AKROMIDĀ® A3 GF 15 1 natural (2308) - 15% glass fibre, heat stabilised, polyamide 6.6, medium stiffness and strength

AKROMIDĀ®

A3 GF 25 1 natural (2390)

PA66 GF25

AKROMIDĀ® A3 GF 25 1 natural (2390) is a 25% glass fibre reinforced, heat stabilised polyamide 6.6 with high stiffness and strength and light inherent color.

Modulus

8.500MPa

Strength

185MPa

Impact

70kJ/mĀ²

AKROMIDĀ® A3 GF 25 1 natural (2390) is a 25% glass fibre reinforced, heat stabilised polyamide 6.6 with high stiffness and strength and light inherent color.

AKROMIDĀ®

A3 S1 natural (2310)

PA66-I

AKROMIDĀ® A3 S1 natural (2310) - PA 6.6, unreinforced, cold impact modified, for connecting and fixing systems, automotive, E&E

Modulus

2.000MPa

Strength

50MPa

Impact

180kJ/mĀ²

AKROMIDĀ® A3 S1 natural (2310) - PA 6.6, unreinforced, cold impact modified, for connecting and fixing systems, automotive, E&E

156575880

AKROMIDĀ®

T5 GF 40 8 black (6458)PPA GF40

AKROMIDĀ® T5 GF 40 8 black (6458) is a 40% glass fibre reinforced polyphthalamide with very high rigidity and strength, as well as high temperature and chemical resistance. This aromatic PPA keeps mechanical performance even at elevated temperatures as well as moisture pic-up. The material fulfills the requirements according to ACS, WRAS and NSF 61. It is suitable for applications that are in contact with cold and hot drinking water. This material corresponds to the European food guideline EU 10/2011 and to the American FDA 21 CFR and is suitable for parts of kitchen and household appliances.

Regulatory

acseu102011fdansf-coldnsf-hotwras

Properties

Modulus

15.000MPa

Strength

245MPa

Impact

80kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
15000 MPa
15000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
245 MPa
230 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,4 %
2,4 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
15600 MPa
15000 MPa

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
80 kJ/mĀ²
80 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
11 kJ/mĀ²
11 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
280 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
325 Ā°C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,5 g/cmĀ³

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Rheological Properties

Flowability

AKRO

1 mm Thickness
2 mm Thickness
120 mm
300 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more