AKROMID®

A3 5 S3 15 black (1434)

PA66-I

AKROMID® A3 5 S3 15 black 950058 (1434) - unreinforced PA 6.6, impact modified, for connecting and fixing systems used at elevated temperatures

Modulus

2.500MPa

Strength

65MPa

Impact

180kJ/m²

AKROMID® A3 5 S3 15 black 950058 (1434) - unreinforced PA 6.6, impact modified, for connecting and fixing systems used at elevated temperatures

AKROMID®

B3 GM 15/15 black (1830)

PA6 (GF15+GB15)

AKROMID® B3 GM 15/15 black (1830) is a 15% glass fibre and 15% glass bead reinforced polyamide 6 with good surface and low warpage

Modulus

7.200MPa

Strength

130MPa

Impact

64kJ/m²

AKROMID® B3 GM 15/15 black (1830) is a 15% glass fibre and 15% glass bead reinforced polyamide 6 with good surface and low warpage

AKROMID®

A3 GF 40 1 natural (2381)

PA66 GF40

AKROMID® A3 GF 40 1 natural (2381) is a 40% glass fibre reinforced, heat stabilised polyamide 6.6 with high rigidity and strength and light inherent color.

Modulus

13.100MPa

Strength

225MPa

Impact

100kJ/m²

AKROMID® A3 GF 40 1 natural (2381) is a 40% glass fibre reinforced, heat stabilised polyamide 6.6 with high rigidity and strength and light inherent color.

AKROMID®

A3 GF 15 1 black (2382)

PA66 GF15

AKROMID® A3 GF 15 1 black (2382) is a 15% glass fibre reinforced, heat stabilised polyamide 6.6 with medium stiffness and strength.

Modulus

6.400MPa

Strength

140MPa

Impact

35kJ/m²

AKROMID® A3 GF 15 1 black (2382) is a 15% glass fibre reinforced, heat stabilised polyamide 6.6 with medium stiffness and strength.

AKROMID®

A3 S1 natural (2310)

PA66-I

AKROMID® A3 S1 natural (2310) - PA 6.6, unreinforced, cold impact modified, for connecting and fixing systems, automotive, E&E

Modulus

2.000MPa

Strength

50MPa

Impact

180kJ/m²

AKROMID® A3 S1 natural (2310) - PA 6.6, unreinforced, cold impact modified, for connecting and fixing systems, automotive, E&E

AKROMID®

B3 GF 15 S3 black (2345)

PA6-I GF15

AKROMID® B3 GF 15 S3 black (2345) - PA 6 with 15% glass fiber reinforcement and impact modified, good surface appearance

Modulus

5.500MPa

Strength

110MPa

Impact

75kJ/m²

AKROMID® B3 GF 15 S3 black (2345) - PA 6 with 15% glass fiber reinforcement and impact modified, good surface appearance

AKROMID®

A3 GF 15 1 natural (2308)

PA66 GF15

AKROMID® A3 GF 15 1 natural (2308) - 15% glass fibre, heat stabilised, polyamide 6.6, medium stiffness and strength

Modulus

6.400MPa

Strength

140MPa

Impact

45kJ/m²

AKROMID® A3 GF 15 1 natural (2308) - 15% glass fibre, heat stabilised, polyamide 6.6, medium stiffness and strength

156575880

AKROMID®

A3 S3 natural (1176)PA66-I

AKROMID® A3 S3 natural (1176) is an unreinforced, dry impact modified Polyamide 6.6. The material is characterised by a very high impact strength and therefore perfectly suitable for connecting and fixing systems which are used in the automotive and electro industry and that are exposed to high loading speeds. The material has a light inherent color.

Features

impact modified

Properties

Modulus

2.800MPa

Strength

67MPa

Impact

180kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
2800 MPa
1700 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
67 MPa
45 MPa

Tensile strain at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
6 %
26 %

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
> 30 %
> 50 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
2850 MPa
1600 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
no break
no break
no break
no break

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
17 kJ/m²
95 kJ/m²
8 kJ/m²

Ball indentation hardness

ISO 2039-1

358N/30s | d.a.m.
93 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
67 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
213 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
263 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,1 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,1 %

Molding shrinkage

ISO 294-4

flow
transverse
1,8 %
2,1 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
1015 Ω x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
1014 Ω

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more