AKROMIDĀ®

B3 GF 30 S1 black (1281)

PA6-I GF30

AKROMIDĀ® B3 GF 30 S1 black (1281) - PA 6, 30% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive

Modulus

8.800MPa

Strength

150MPa

Impact

85kJ/mĀ²

AKROMIDĀ® B3 GF 30 S1 black (1281) - PA 6, 30% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive

AKROMIDĀ®

A3 GK 40 1 black (1804)

PA66 GB40

AKROMIDĀ® A3 GK 40 1 black (1804) - PA 6.6, 40% glass beads reinforced, good surface, low warpage, heat stabilised

Modulus

5.500MPa

Strength

95MPa

Impact

25kJ/mĀ²

AKROMIDĀ® A3 GK 40 1 black (1804) - PA 6.6, 40% glass beads reinforced, good surface, low warpage, heat stabilised

AKROMIDĀ®

A3 GF 30 S1 black (1365)

PA66-I GF30

AKROMIDĀ® A3 GF 30 S1 black (1365) - PA 6.6, 30% glass fiber reinforced, impact modified, for connecting and fixing systems, automotive, E&E

Modulus

9.600MPa

Strength

180MPa

Impact

105kJ/mĀ²

AKROMIDĀ® A3 GF 30 S1 black (1365) - PA 6.6, 30% glass fiber reinforced, impact modified, for connecting and fixing systems, automotive, E&E

AKROLENĀ®

PP GFM 25/15 natural (2118)

PP (GF25+MD15)

AKROLENĀ® PP GFM 25/15 natural (2118) is a 25% glass fibre reinforced, 15% mineral filled polypropylene with good surface, dimensional stability and light inherent color

Modulus

6.500MPa

Strength

NA

Impact

45kJ/mĀ²

AKROLENĀ® PP GFM 25/15 natural (2118) is a 25% glass fibre reinforced, 15% mineral filled polypropylene with good surface, dimensional stability and light inherent color

AKROMIDĀ®

A3 GF 25 1 black (2384)

PA66 GF25

AKROMIDĀ® A3 GF 25 1 black (2384) is a 25% glass fibre reinforced, heat stabilised polyamide 6.6 with high stiffness and strength.

Modulus

8.500MPa

Strength

175MPa

Impact

70kJ/mĀ²

AKROMIDĀ® A3 GF 25 1 black (2384) is a 25% glass fibre reinforced, heat stabilised polyamide 6.6 with high stiffness and strength.

AKROMIDĀ®

A3 5 S3 15 black (1434)

PA66-I

AKROMIDĀ® A3 5 S3 15 black 950058 (1434) - unreinforced PA 6.6, impact modified, for connecting and fixing systems used at elevated temperatures

Modulus

2.500MPa

Strength

65MPa

Impact

180kJ/mĀ²

AKROMIDĀ® A3 5 S3 15 black 950058 (1434) - unreinforced PA 6.6, impact modified, for connecting and fixing systems used at elevated temperatures

AKROMIDĀ®

B3 GF 50 S1 black (2000)

PA6-I GF50

AKROMIDĀ® B3 GF 50 S1 black 950089 (2000) - PA 6, 50% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive

Modulus

15.000MPa

Strength

190MPa

Impact

100kJ/mĀ²

AKROMIDĀ® B3 GF 50 S1 black 950089 (2000) - PA 6, 50% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive

155565780

AKROMIDĀ®

Preliminary

NEXT 5.6 3 GF 30 FR black (8465)PA56 GF30 FR(40)

AKROMIDĀ® NEXT 5.6 3 GF 30 FR black (8465) is a partially bio-based and flame retardant PA 5.6 and meets the requirement according to UL94 V0 @ 0,8 mm. The flame-retardant system is free of red phosphorus and halogens. PA 5.6 is a HMD-free (hexamethylenediamine) alternative to PA 6.6. With 30% glass fibre reinforcement, the material is suitable for components with high strength requirements for E&E and E-Mobility, such as busbar supports, switches, terminal strips and connector housings. This grade is laser markable.

Features

Bio-based
heat stabilised 130
flame retardant
E&E

Properties

Modulus

11.000MPa

Strength

137MPa

Impact

64kJ/mĀ²

Sustainability

Biobased carbon content

32 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
11000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
137 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
2,6 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
64 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
10 kJ/mĀ²

Thermal Properties

Melting temperature

ISO 11357-3

DSC, 10K/min
254 Ā°C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
V-0 Class
V-0 Class
V-0 Class

GWFI

IEC 60695-2-12

0,8 mm Wall thickness
1,6 mm Wall thickness
960 Ā°C
960 Ā°C

GWIT

IEC 60695-2-13

0,8 mm Wall thickness
1,6 mm Wall thickness
725 Ā°C
700 Ā°C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,40 g/cmĀ³

Electrical Properties

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more