AKROMID®

B3 GF 30 S1 black (1281)

PA6-I GF30

AKROMID® B3 GF 30 S1 black (1281) - PA 6, 30% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive

Modulus

8.800MPa

Strength

150MPa

Impact

85kJ/m²

AKROMID® B3 GF 30 S1 black (1281) - PA 6, 30% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive

AKROMID®

A3 GF 30 S1 black (1365)

PA66-I GF30

AKROMID® A3 GF 30 S1 black (1365) - PA 6.6, 30% glass fiber reinforced, impact modified, for connecting and fixing systems, automotive, E&E

Modulus

9.600MPa

Strength

180MPa

Impact

105kJ/m²

AKROMID® A3 GF 30 S1 black (1365) - PA 6.6, 30% glass fiber reinforced, impact modified, for connecting and fixing systems, automotive, E&E

AKROMID®

A3 GK 40 1 black (1804)

PA66 GB40

AKROMID® A3 GK 40 1 black (1804) - PA 6.6, 40% glass beads reinforced, good surface, low warpage, heat stabilised

Modulus

5.500MPa

Strength

95MPa

Impact

25kJ/m²

AKROMID® A3 GK 40 1 black (1804) - PA 6.6, 40% glass beads reinforced, good surface, low warpage, heat stabilised

AKROLEN®

PP GFM 25/15 natural (2118)

PP (GF25+MD15)

AKROLEN® PP GFM 25/15 natural (2118) is a 25% glass fibre reinforced, 15% mineral filled polypropylene with good surface, dimensional stability and light inherent color

Modulus

6.500MPa

Strength

NA

Impact

45kJ/m²

AKROLEN® PP GFM 25/15 natural (2118) is a 25% glass fibre reinforced, 15% mineral filled polypropylene with good surface, dimensional stability and light inherent color

AKROMID®

A3 5 S3 15 black (1434)

PA66-I

AKROMID® A3 5 S3 15 black 950058 (1434) - unreinforced PA 6.6, impact modified, for connecting and fixing systems used at elevated temperatures

Modulus

2.500MPa

Strength

65MPa

Impact

180kJ/m²

AKROMID® A3 5 S3 15 black 950058 (1434) - unreinforced PA 6.6, impact modified, for connecting and fixing systems used at elevated temperatures

AKROMID®

B3 GF 50 S1 black (2000)

PA6-I GF50

AKROMID® B3 GF 50 S1 black 950089 (2000) - PA 6, 50% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive

Modulus

15.000MPa

Strength

190MPa

Impact

100kJ/m²

AKROMID® B3 GF 50 S1 black 950089 (2000) - PA 6, 50% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive

AKROMID®

B3 GM 15/15 black (1830)

PA6 (GF15+GB15)

AKROMID® B3 GM 15/15 black (1830) is a 15% glass fibre and 15% glass bead reinforced polyamide 6 with good surface and low warpage

Modulus

7.200MPa

Strength

130MPa

Impact

64kJ/m²

AKROMID® B3 GM 15/15 black (1830) is a 15% glass fibre and 15% glass bead reinforced polyamide 6 with good surface and low warpage

155565780

AKROTEK®

PK-VM GF 50 8 black (6936)PK GF50

AKROTEK® PK-VM GF 50 8 black (6936) is a 50% glass fibre reinforced polyketone with very high stiffness and strength. PK is characterized by its outstanding media resistance, which qualifies it to be used for components that are in contact with chemicals. The material corresponds to the European food guideline EU 10/2011 and to the American FDA 21 CFR. This grade is suitable for parts of kitchen and household appliances. Please note that the material is NOT suitable anymore for drinking water contact and does NOT meet the requirements according to KTW, DVGW W270, ACS, WRAS as well as NSF61.

Features

hydrolysis / chemically stabilised

Regulatory

eu102011fda

Properties

Modulus

14.000MPa

Strength

170MPa

Impact

50kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
14000 MPa
14000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
170 MPa
150 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,4 %
2,4 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
50 kJ/m²
45 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
16 kJ/m²
16 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
220 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,65 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,4 - 0,5 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,4 - 0,6 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more