AKROMID®

B3 GF 30 S1 black (1281)

PA6-I GF30

AKROMID® B3 GF 30 S1 black (1281) - PA 6, 30% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive

Modulus

8.800MPa

Strength

150MPa

Impact

85kJ/m²

AKROMID® B3 GF 30 S1 black (1281) - PA 6, 30% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive

AKROMID®

A3 GK 40 1 black (1804)

PA66 GB40

AKROMID® A3 GK 40 1 black (1804) - PA 6.6, 40% glass beads reinforced, good surface, low warpage, heat stabilised

Modulus

5.500MPa

Strength

95MPa

Impact

25kJ/m²

AKROMID® A3 GK 40 1 black (1804) - PA 6.6, 40% glass beads reinforced, good surface, low warpage, heat stabilised

AKROMID®

A3 GF 30 S1 black (1365)

PA66-I GF30

AKROMID® A3 GF 30 S1 black (1365) - PA 6.6, 30% glass fiber reinforced, impact modified, for connecting and fixing systems, automotive, E&E

Modulus

9.600MPa

Strength

180MPa

Impact

105kJ/m²

AKROMID® A3 GF 30 S1 black (1365) - PA 6.6, 30% glass fiber reinforced, impact modified, for connecting and fixing systems, automotive, E&E

AKROLEN®

PP GFM 25/15 natural (2118)

PP (GF25+MD15)

AKROLEN® PP GFM 25/15 natural (2118) is a 25% glass fibre reinforced, 15% mineral filled polypropylene with good surface, dimensional stability and light inherent color

Modulus

6.500MPa

Strength

NA

Impact

45kJ/m²

AKROLEN® PP GFM 25/15 natural (2118) is a 25% glass fibre reinforced, 15% mineral filled polypropylene with good surface, dimensional stability and light inherent color

AKROMID®

A3 GF 25 1 black (2384)

PA66 GF25

AKROMID® A3 GF 25 1 black (2384) is a 25% glass fibre reinforced, heat stabilised polyamide 6.6 with high stiffness and strength.

Modulus

8.500MPa

Strength

175MPa

Impact

70kJ/m²

AKROMID® A3 GF 25 1 black (2384) is a 25% glass fibre reinforced, heat stabilised polyamide 6.6 with high stiffness and strength.

AKROMID®

A3 5 S3 15 black (1434)

PA66-I

AKROMID® A3 5 S3 15 black 950058 (1434) - unreinforced PA 6.6, impact modified, for connecting and fixing systems used at elevated temperatures

Modulus

2.500MPa

Strength

65MPa

Impact

180kJ/m²

AKROMID® A3 5 S3 15 black 950058 (1434) - unreinforced PA 6.6, impact modified, for connecting and fixing systems used at elevated temperatures

AKROMID®

B3 GF 50 S1 black (2000)

PA6-I GF50

AKROMID® B3 GF 50 S1 black 950089 (2000) - PA 6, 50% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive

Modulus

15.000MPa

Strength

190MPa

Impact

100kJ/m²

AKROMID® B3 GF 50 S1 black 950089 (2000) - PA 6, 50% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive

155565780

AKROMID®

C3 GF 30 5 XTC natural (4499)PA66 + PA6 GF 30

AKROMID® C3 GF 30 5 XTC natural (4499) is a 30% glass fibre reinforced, high temperature stabilised polaymide 6.6/6 - Blend with high stiffness and strength and extra high temperature tolerance.

Features

heat stabilised 230

Properties

Modulus

9.500MPa

Strength

185MPa

Impact

95kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
9500 MPa
6000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
185 MPa
115 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,5 %
6,5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
95 kJ/m²
90 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
13 kJ/m²
13 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
230 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
250 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
245 °C

Coefficient of linear thermal expansion

ISO 11359-1/2

23°C to 80°C | parallel
23°C to 80°C | transverse
0,15 10⁻⁴/K
1,12 10⁻⁴/K

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,36 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,0 - 2,2 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,6 - 0,8 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
conditioned
1013 Ω x cm
1010 Ω x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
conditioned
1012 Ω
1010 Ω

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.