A3 GF 30 S1 black (1365)

PA66-I GF30

AKROMIDĀ® A3 GF 30 S1 black (1365) - PA 6.6, 30% glass fiber reinforced, impact modified, for connecting and fixing systems, automotive, E&E

Modulus

9.600MPa

Strength

180MPa

Impact

105kJ/mĀ²

AKROMIDĀ® A3 GF 30 S1 black (1365) - PA 6.6, 30% glass fiber reinforced, impact modified, for connecting and fixing systems, automotive, E&E

AKROMIDĀ®

A3 GK 40 1 black (1804)

PA66 GB40

AKROMIDĀ® A3 GK 40 1 black (1804) - PA 6.6, 40% glass beads reinforced, good surface, low warpage, heat stabilised

Modulus

5.500MPa

Strength

95MPa

Impact

25kJ/mĀ²

AKROMIDĀ® A3 GK 40 1 black (1804) - PA 6.6, 40% glass beads reinforced, good surface, low warpage, heat stabilised

AKROMIDĀ®

B3 GF 30 S1 black (1281)

PA6-I GF30

AKROMIDĀ® B3 GF 30 S1 black (1281) - PA 6, 30% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive

Modulus

8.800MPa

Strength

150MPa

Impact

85kJ/mĀ²

AKROMIDĀ® B3 GF 30 S1 black (1281) - PA 6, 30% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive

AKROLENĀ®

PP GFM 25/15 natural (2118)

PP (GF25+MD15)

AKROLENĀ® PP GFM 25/15 natural (2118) is a 25% glass fibre reinforced, 15% mineral filled polypropylene with good surface, dimensional stability and light inherent color

Modulus

6.500MPa

Strength

NA

Impact

45kJ/mĀ²

AKROLENĀ® PP GFM 25/15 natural (2118) is a 25% glass fibre reinforced, 15% mineral filled polypropylene with good surface, dimensional stability and light inherent color

AKROMIDĀ®

B3 GM 15/15 black (1830)

PA6 (GF15+GB15)

AKROMIDĀ® B3 GM 15/15 black (1830) is a 15% glass fibre and 15% glass bead reinforced polyamide 6 with good surface and low warpage

Modulus

7.200MPa

Strength

130MPa

Impact

64kJ/mĀ²

AKROMIDĀ® B3 GM 15/15 black (1830) is a 15% glass fibre and 15% glass bead reinforced polyamide 6 with good surface and low warpage

AKROMIDĀ®

A3 5 S3 15 black (1434)

PA66-I

AKROMIDĀ® A3 5 S3 15 black 950058 (1434) - unreinforced PA 6.6, impact modified, for connecting and fixing systems used at elevated temperatures

Modulus

2.500MPa

Strength

65MPa

Impact

180kJ/mĀ²

AKROMIDĀ® A3 5 S3 15 black 950058 (1434) - unreinforced PA 6.6, impact modified, for connecting and fixing systems used at elevated temperatures

AKROMIDĀ®

B3 GF 50 S1 black (2000)

PA6-I GF50

AKROMIDĀ® B3 GF 50 S1 black 950089 (2000) - PA 6, 50% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive

Modulus

15.000MPa

Strength

190MPa

Impact

100kJ/mĀ²

AKROMIDĀ® B3 GF 50 S1 black 950089 (2000) - PA 6, 50% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive

155565780

AKROMIDĀ®

A3 GF 30 S1 black (1365)PA66-I GF30

AKROMIDĀ® A3 GF 30 S1 black (1365) is a 30% glass fiber reinforced, impact modified Polyamide 6.6. It is characterised by high stiffness and strength as well as a higher impact strength compared to a standard PA 6.6 GF 30. The material is perfectly suitable for connecting and fixing systems as well as for precision parts in the automotive industry.

Features

impact modified

Properties

Modulus

9.600MPa

Strength

180MPa

Impact

105kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
9600 MPa
8000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
180 MPa
120 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
5 %
6 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
30Ā°C | conditioned
-
105 kJ/mĀ²
110 kJ/mĀ²
85 kJ/mĀ²
100 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
30Ā°C | conditioned
-
17 kJ/mĀ²
20 kJ/mĀ²
12 kJ/mĀ²
12 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
255 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 Ā°C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,34 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,7 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,7 - 0,9 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.