Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/m²
558 Compounds found
Recommended  
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

AKROMID®

UL
Preliminary

C3 GF 25 1 FR grey (8803)

PA66+PA6 GF25 FR(40)

AKROMID® C3 GF 25 1 FR grey (8803) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, RAL 7035, lasermarkable, high strength, UL-listed, automotive, E&E.

Modulus

9.100MPa

Strength

120MPa

Impact

46kJ/m²

AKROMID® C3 GF 25 1 FR grey (8803) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, RAL 7035, lasermarkable, high strength, UL-listed, automotive, E&E.

AKROTEK®

UL

PK-VM GF 30 7 HU black (8695)

PK GF30

AKROTEK® PK-VM GF 30 7 HU black (8695) - Polyketon, 30% glass fibre reinforced, chemical and hydrolysis resistance

Modulus

8.000MPa

Strength

130MPa

Impact

65kJ/m²

AKROTEK® PK-VM GF 30 7 HU black (8695) - Polyketon, 30% glass fibre reinforced, chemical and hydrolysis resistance

AKROMID®

UL

B28 GM 15/15 1 FR black (8750)

PA6 (GF15+GB15) FR(40)

AKROMID® B28 GM 15/15 1 FR black (8750) - PA6, 15% glass fibre, 15% glass beads, flame retardant, free of halogene, high stiffness and strength, very good flowability, laser markable, E&E.

Modulus

8.400MPa

Strength

105MPa

Impact

45kJ/m²

AKROMID® B28 GM 15/15 1 FR black (8750) - PA6, 15% glass fibre, 15% glass beads, flame retardant, free of halogene, high stiffness and strength, very good flowability, laser markable, E&E.

AKROMID®

Preliminary

B3 GF 40 5 black (8725)

PA6 GF40

AKROMID® B3 GF 40 5 black (8725) - PA6, 40% GF, high heat stabilised, UV stabilised, technical parts in industrial engineering, automotive industry, agriculture.

Modulus

12.500MPa

Strength

200MPa

Impact

95kJ/m²

AKROMID® B3 GF 40 5 black (8725) - PA6, 40% GF, high heat stabilised, UV stabilised, technical parts in industrial engineering, automotive industry, agriculture.

AKROTEK®

Preliminary

PK-VM M 7 natural (8858)

PK M7

AKROTEK® PK-VM M 7 natural (8858) - 7 % mineral reinforced Polyketon, high flowability and good weldline perfomance.

Modulus

2.700MPa

Strength

65MPa

Impact

120kJ/m²

AKROTEK® PK-VM M 7 natural (8858) - 7 % mineral reinforced Polyketon, high flowability and good weldline perfomance.

PRECITE®

Preliminary

K GF 10 ECO black (8696)

PBT-PET- GF 10

PRECITE® K GF 10 ECO black (8696) - PBT/PET blend, recycled PET content, 10% glass fiber, high strength, good surface, good dimensional stability, automotive, industrial, household, E&E, sports & leisure.

Modulus

4.800MPa

Strength

100MPa

Impact

25kJ/m²

PRECITE® K GF 10 ECO black (8696) - PBT/PET blend, recycled PET content, 10% glass fiber, high strength, good surface, good dimensional stability, automotive, industrial, household, E&E, sports & leisure.

PRECITE®

Preliminary

K GF 20 ECO black (8697)

PBT-PET - GF 20

PRECITE® K GF 20 ECO black (8697) - PBT/PET blend, recycled PET content, 20% glass fiber, high strength, good surface, good dimensional stability, automotive, industrial, household, E&E, sports & leisure.

Modulus

7.200MPa

Strength

125MPa

Impact

50kJ/m²

PRECITE® K GF 20 ECO black (8697) - PBT/PET blend, recycled PET content, 20% glass fiber, high strength, good surface, good dimensional stability, automotive, industrial, household, E&E, sports & leisure.

154555680

AKROLOY®

PA GF 60 black (6418)PA66+PA6I/6T GF60

AKROLOY® PA GF 60 black (6418) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

Properties

Modulus

21.000MPa

Strength

275MPa

Impact

100kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
21000 MPa
20000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
275 MPa
225 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,4 %
2,4 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
21000 MPa
21000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
410 MPa
360 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
2,5 %
2,6 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
100 kJ/m²
100 kJ/m²
95 kJ/m²
95 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
19 kJ/m²
19 kJ/m²
18 kJ/m²
18 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
245 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
193 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
255 °C

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
20.000 h
150 °C
115 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,69 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,1 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,2 - 0,4 %

Rheological Properties

Flowability

AKRO

1 mm Thickness
2 mm Thickness
60 mm
200 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.