AKROTEKĀ®

Preliminary

PK-VM GF 10 black (8685)

PK GF10

AKROTEKĀ® PK-VM GF 10 black (8685) - Polyketon, 10% glass fibre reinforced, chemical and hydrolysis resistance

Modulus

3.500MPa

Strength

70MPa

Impact

55kJ/mĀ²

AKROTEKĀ® PK-VM GF 10 black (8685) - Polyketon, 10% glass fibre reinforced, chemical and hydrolysis resistance

AKROMIDĀ®

Preliminary

B3 GF 40 5 black (8725)

PA6 GF40

AKROMIDĀ® B3 GF 40 5 black (8725) - PA6, 40% GF, high heat stabilised, UV stabilised, technical parts in industrial engineering, automotive industry, agriculture.

Modulus

12.500MPa

Strength

200MPa

Impact

95kJ/mĀ²

AKROMIDĀ® B3 GF 40 5 black (8725) - PA6, 40% GF, high heat stabilised, UV stabilised, technical parts in industrial engineering, automotive industry, agriculture.

AKROTEKĀ®

PK-VM GF 30 natural (8661)

PK GF30

AKROTEKĀ® PK-VM GF 30 natural (8661) - Polyketon, 30% glass fiber reinforced, chemical and hydrolysis resistance

Modulus

8.300MPa

Strength

144MPa

Impact

76kJ/mĀ²

AKROTEKĀ® PK-VM GF 30 natural (8661) - Polyketon, 30% glass fiber reinforced, chemical and hydrolysis resistance

AKROMIDĀ®

UL

B28 GM 15/15 1 FR black (8750)

PA6 (GF15+GB15) FR(40)

AKROMIDĀ® B28 GM 15/15 1 FR black (8750) - PA6, 15% glass fibre, 15% glass beads, flame retardant, free of halogene, high stiffness and strength, very good flowability, laser markable, E&E.

Modulus

8.400MPa

Strength

105MPa

Impact

45kJ/mĀ²

AKROMIDĀ® B28 GM 15/15 1 FR black (8750) - PA6, 15% glass fibre, 15% glass beads, flame retardant, free of halogene, high stiffness and strength, very good flowability, laser markable, E&E.

AKROMIDĀ®

A3 GK 40 1 black (1804)

PA66 GB40

AKROMIDĀ® A3 GK 40 1 black (1804) - PA 6.6, 40% glass beads reinforced, good surface, low warpage, heat stabilised

Modulus

5.500MPa

Strength

95MPa

Impact

25kJ/mĀ²

AKROMIDĀ® A3 GK 40 1 black (1804) - PA 6.6, 40% glass beads reinforced, good surface, low warpage, heat stabilised

AKROMIDĀ®

B3 GF 30 S1 black (1281)

PA6-I GF30

AKROMIDĀ® B3 GF 30 S1 black (1281) - PA 6, 30% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive

Modulus

8.800MPa

Strength

150MPa

Impact

85kJ/mĀ²

AKROMIDĀ® B3 GF 30 S1 black (1281) - PA 6, 30% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive

AKROMIDĀ®

A3 GF 30 S1 black (1365)

PA66-I GF30

AKROMIDĀ® A3 GF 30 S1 black (1365) - PA 6.6, 30% glass fiber reinforced, impact modified, for connecting and fixing systems, automotive, E&E

Modulus

9.600MPa

Strength

180MPa

Impact

105kJ/mĀ²

AKROMIDĀ® A3 GF 30 S1 black (1365) - PA 6.6, 30% glass fiber reinforced, impact modified, for connecting and fixing systems, automotive, E&E

154555680

AKROMIDĀ®

B3 GF 40 1 L black (4581)PA6 + PP GF40

AKROMIDĀ® B3 GF 40 1 L black (4581) is a PA6/PP-blend with reduced density compared to standard PA6 with 40% glass fibre reinforcement, the material is suitable for components with high strength and stiffness where cost and weight reduction are required at the same time. The chemical resistance of AKROMIDĀ® B3 GF 40 1 L black (4581) is particularly superior to calcium chloride (CaClā‚‚).

Features

heat stabilised 130
reduced density

Properties

Modulus

11.000MPa

Strength

150MPa

Impact

70kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
11000 MPa
8400 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
150 MPa
115 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,1 %
4,2 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
30Ā°C | conditioned
-
70 kJ/mĀ²
66 kJ/mĀ²
55 kJ/mĀ²
55 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
30Ā°C | conditioned
-
16 kJ/mĀ²
18 kJ/mĀ²
15 kJ/mĀ²
15 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
201 Ā°C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
217 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 Ā°C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,36 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,2 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,4 - 0,6 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more