AKROMID^®

B3 GF 30 5 black (7285)

PA6 GF30

AKROMID® B3 GF 30 5 black (7285) - PA6, 30% GF, high heat stabilised, technical parts in industrial engineering and automotive industry.

Modulus

9.500MPa

Strength

170MPa

Impact

85kJ/m²

AKROMID® B3 GF 30 5 black (7285) - PA6, 30% GF, high heat stabilised, technical parts in industrial engineering and automotive industry.

AKROMID^®

B28 GM 15/15 1 FR black (8750)

PA6 (GF15+GB15) FR(40)

AKROMID® B28 GM 15/15 1 FR black (8750) - PA6, 15% glass fibre, 15% glass beads, flame retardant, free of halogene, high stiffness and strength, very good flowability, laser markable, E&E.

Modulus

8.400MPa

Strength

105MPa

Impact

45kJ/m²

AKROMID® B28 GM 15/15 1 FR black (8750) - PA6, 15% glass fibre, 15% glass beads, flame retardant, free of halogene, high stiffness and strength, very good flowability, laser markable, E&E.

AKROMID^®

Preliminary

C3 GF 30 1 natural (8574)

PA66 + PA6 GF30

AKROMID® C3 GF 30 1 natural (8574) - PA6.6/6 blend, 30% glass fiber reinforced, heat stabilised, industrial engineering, automotive industry

Modulus

9.300MPa

Strength

185MPa

Impact

75kJ/m²

AKROMID® C3 GF 30 1 natural (8574) - PA6.6/6 blend, 30% glass fiber reinforced, heat stabilised, industrial engineering, automotive industry

AKROMID^®

Preliminary

T91 GF 30 FR natural (8667)

PPA GF30 FR(40)

AKROMID® T91 GF 30 FR natural (8667) - PA9T, flame retardant, 30% glass fiber, high stiffness, high strength, free of halogenes, good flowability, low water uptake, reflow soldering, SMT devices, E&E, automotive.

Modulus

10.500MPa

Strength

150MPa

Impact

55kJ/m²

AKROMID^®

Preliminary

B3 GF 40 5 black (8725)

PA6 GF40

AKROMID® B3 GF 40 5 black (8725) - PA6, 40% GF, high heat stabilised, UV stabilised, technical parts in industrial engineering, automotive industry, agriculture.

Modulus

12.500MPa

Strength

200MPa

Impact

95kJ/m²

AKROMID® B3 GF 40 5 black (8725) - PA6, 40% GF, high heat stabilised, UV stabilised, technical parts in industrial engineering, automotive industry, agriculture.

AKROTEK^®

Preliminary

PK-VM M 7 natural (8858)

PK M7

AKROTEK® PK-VM M 7 natural (8858) - 7 % mineral reinforced Polyketon, high flowability and good weldline perfomance.

Modulus

2.700MPa

Strength

65MPa

Impact

120kJ/m²

AKROTEK® PK-VM M 7 natural (8858) - 7 % mineral reinforced Polyketon, high flowability and good weldline perfomance.

AKROMID^®

Preliminary

B3 GF 40 5 black (8636)

PA6 GF40

AKROMID® B3 GF 40 5 black (8636) - PA6, 40% GF, high heat stabilised, UV stabilised, technical parts in industrial engineering, automotive industry, agriculture.

Modulus

12.500MPa

Strength

200MPa

Impact

95kJ/m²

AKROMID® B3 GF 40 5 black (8636) - PA6, 40% GF, high heat stabilised, UV stabilised, technical parts in industrial engineering, automotive industry, agriculture.

1 54 55 5680

AKROMID^®

A3 GF 50 1 black (2387)PA66 GF50

AKROMID® A3 GF 50 1 black (2387) is a 50% glass fiber reinforced polyamide 6.6. It is characterised by a very high stiffness and strength. Furthermore, the material is heat stabilised and therefore perfectly suitable for technical parts in industrial engineering and in the automotive industry, e.g. gearbox components.

Features

heat stabilised 130

Properties

Modulus

16.700MPa

Strength

250MPa

Impact

105kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.

1 mm/min | conditioned

16700 MPa

12600 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.

5 mm/min | conditioned

250 MPa

180 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.

5 mm/min | conditioned

2,5 %

3,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.

2 mm/min | conditioned

15200 MPa

13600 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.

2 mm/min | conditioned

380 MPa

310 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.

23°C | conditioned

30°C | d.a.m.

45°C | d.a.m.

45°C | conditioned

105 kJ/m²

110 kJ/m²

105 kJ/m²

90 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.

23°C | conditioned

30°C | d.a.m.

45°C | d.a.m.

45°C | conditioned

19 kJ/m²

23 kJ/m²

16 kJ/m²

15 kJ/m²

Ball indentation hardness

ISO 2039-1

961N/30s | d.a.m.

290 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa

260 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa

260 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa

235 °C

Melting temperature

ISO 11357-3

DSC, 10K/min

262 °C

Coefficient of linear thermal expansion

ISO 11359-1/2

23°C to 80°C | parallel

23°C to 80°C | transverse

0,17 10⁻⁴/K

0,88 10⁻⁴/K

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h

20.000 h

160 - 175 °C

130 - 150 °C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness

HB Class

GWFI

IEC 60695-2-12

1,6 mm Wall thickness

650 °C

GWIT

IEC 60695-2-13

1,6 mm Wall thickness

675 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness

General properties

Density

ISO 1183

23°C

1,57 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.

1,3 - 1,5 %

Water absorption

ISO 62

23°C, saturated

3,7 - 4,3 %

Molding shrinkage

ISO 294-4

flow

transverse

0,1 - 0,3 %

0,5 - 0,7 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.

conditioned

10¹³ Ω x cm

10¹⁰ Ω x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.

conditioned

10¹² Ω

10¹⁰ Ω

Comparative tracking index

IEC 60112

Test liquid A

600 V

Rheological Properties

Flowability

AKRO

1 mm Thickness

2 mm Thickness

200 mm

350 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Find the right compound

A3 GF 50 1 black (2387)PA66 GF50

Mechanical Properties

Tensile modulus

Tensile stress at break

Tensile strain at break

Flexural modulus

Flexural strength

Charpy impact strength

Charpy notched impact strength

Ball indentation hardness

Thermal Properties

Temperature of deflection under load HDT/A

Temperature of deflection under load HDT/B

Temperature of deflection under load HDT/C

Melting temperature

Coefficient of linear thermal expansion

Temperature index for 50% loss of tensile strength

Flammability

Burning rate

GWFI

GWIT

Burning rate (<100 mm/min)

General properties

Density

Humidity absorption

Water absorption

Molding shrinkage

Electrical Properties

Volume resistivity IEC

Surface resistivity

Comparative tracking index

Rheological Properties

Flowability

Do you have any questions? We are happy to help.

Find the right compound

A3 GF 50 1 black (2387).css-117ixes{line-height:1.5;display:block;margin-top:var(--chakra-space-2);font-weight:var(--chakra-fontWeights-normal);font-size:var(--chakra-fontSizes-sm);color:var(--chakra-colors-kisPrimaryTextLight-700);}PA66 GF50

Mechanical Properties

Tensile modulus

Tensile stress at break

Tensile strain at break

Flexural modulus

Flexural strength

Charpy impact strength

Charpy notched impact strength

Ball indentation hardness

Thermal Properties

Temperature of deflection under load HDT/A

Temperature of deflection under load HDT/B

Temperature of deflection under load HDT/C

Melting temperature

Coefficient of linear thermal expansion

Temperature index for 50% loss of tensile strength

Flammability

Burning rate

GWFI

GWIT

Burning rate (<100 mm/min)

General properties

Density

Humidity absorption

Water absorption

Molding shrinkage

Electrical Properties

Volume resistivity IEC

Surface resistivity

Comparative tracking index

Rheological Properties

Flowability

Do you have any questions? We are happy to help.

A3 GF 50 1 black (2387)PA66 GF50