AKROMIDĀ®

B3 GF 30 5 black (7285)

PA6 GF30

AKROMIDĀ® B3 GF 30 5 black (7285) - PA6, 30% GF, high heat stabilised, technical parts in industrial engineering and automotive industry.

Modulus

9.500MPa

Strength

170MPa

Impact

85kJ/mĀ²

AKROMIDĀ® B3 GF 30 5 black (7285) - PA6, 30% GF, high heat stabilised, technical parts in industrial engineering and automotive industry.

AKROMIDĀ®

Preliminary

C3 GF 30 1 natural (8574)

PA66 + PA6 GF30

AKROMIDĀ® C3 GF 30 1 natural (8574) - PA6.6/6 blend, 30% glass fiber reinforced, heat stabilised, industrial engineering, automotive industry

Modulus

9.300MPa

Strength

185MPa

Impact

75kJ/mĀ²

AKROMIDĀ® C3 GF 30 1 natural (8574) - PA6.6/6 blend, 30% glass fiber reinforced, heat stabilised, industrial engineering, automotive industry

AKROTEKĀ®

UL

PK-VM GF 30 7 HU black (8695)

PK GF30

AKROTEKĀ® PK-VM GF 30 7 HU black (8695) - Polyketon, 30% glass fibre reinforced, chemical and hydrolysis resistance

Modulus

8.000MPa

Strength

130MPa

Impact

65kJ/mĀ²

AKROTEKĀ® PK-VM GF 30 7 HU black (8695) - Polyketon, 30% glass fibre reinforced, chemical and hydrolysis resistance

AKROMIDĀ®

Preliminary

B3 GF 40 5 black (8726)

PA6 GF40

AKROMIDĀ® B3 GF 40 5 black (8726) - PA6, 40% GF, high heat stabilised, UV stabilised, technical parts in industrial engineering, automotive industry, agriculture.

Modulus

12.500MPa

Strength

200MPa

Impact

95kJ/mĀ²

AKROMIDĀ® B3 GF 40 5 black (8726) - PA6, 40% GF, high heat stabilised, UV stabilised, technical parts in industrial engineering, automotive industry, agriculture.

AKROMIDĀ®

A3 GF 50 ECO black (8571)

PA66 GF50

AKROMIDĀ® A3 GF 50 ECO black (8571) - PA 6.6, 50% glass fiber, recycling, high stiffness and strength, heat-stabilised, laser markable, automotive, mechanical engineering.

Modulus

16.000MPa

Strength

190MPa

Impact

80kJ/mĀ²

AKROMIDĀ® A3 GF 50 ECO black (8571) - PA 6.6, 50% glass fiber, recycling, high stiffness and strength, heat-stabilised, laser markable, automotive, mechanical engineering.

PRECITEĀ®

Preliminary

K GF 20 ECO black (8697)

PBT-PET - GF 20

PRECITEĀ® K GF 20 ECO black (8697) - PBT/PET blend, recycled PET content, 20% glass fiber, high strength, good surface, good dimensional stability, automotive, industrial, household, E&E, sports & leisure.

Modulus

7.200MPa

Strength

125MPa

Impact

50kJ/mĀ²

PRECITEĀ® K GF 20 ECO black (8697) - PBT/PET blend, recycled PET content, 20% glass fiber, high strength, good surface, good dimensional stability, automotive, industrial, household, E&E, sports & leisure.

AKROTEKĀ®

Preliminary

PK-VM GF 60 black (8689)

PK GF60

AKROTEKĀ® PK-VM GF 60 black (8689)- Polyketon, 60% glass fibre reinforced, chemical and hydrolysis resistance

Modulus

16.700MPa

Strength

170MPa

Impact

60kJ/mĀ²

AKROTEKĀ® PK-VM GF 60 black (8689)- Polyketon, 60% glass fibre reinforced, chemical and hydrolysis resistance

154555680

AKROMIDĀ®

A3 GF 35 3 black (1802)PA66 GF35

AKROMIDĀ® A3 GF 35 3 black (1802) is a 35% glass fiber reinforced polyamide 6.6. It is characterised by a high stiffness and strength. Furthermore, the material is nucleated. It is perfectly suitable for technical parts in industrial engineering and in the automotive industry.

Features

nucleated

Properties

Modulus

11.500MPa

Strength

180MPa

Impact

50kJ/mĀ²

Sustainability

Recycled content

30 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
11500 MPa
8400 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
180 MPa
120 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,3 %
4,2 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
8000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
250 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
3,7 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
50 kJ/mĀ²
> 55 kJ/mĀ²
53 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
9 kJ/mĀ²
13 kJ/mĀ²
6 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
250 Ā°C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
265 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 Ā°C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,41 g/cmĀ³

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,65 - 0,85 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.