AKROTEK®

Preliminary

PK-VM M 7 natural (8858)

PK M7

AKROTEK® PK-VM M 7 natural (8858) - 7 % mineral reinforced Polyketon, high flowability and good weldline perfomance.

Modulus

2.700MPa

Strength

65MPa

Impact

120kJ/m²

AKROTEK® PK-VM M 7 natural (8858) - 7 % mineral reinforced Polyketon, high flowability and good weldline perfomance.

AKROMID®

A3 GF 50 ECO black (8571)

PA66 GF50

AKROMID® A3 GF 50 ECO black (8571) - PA 6.6, 50% glass fiber, recycling, high stiffness and strength, heat-stabilised, laser markable, automotive, mechanical engineering.

Modulus

16.000MPa

Strength

190MPa

Impact

80kJ/m²

AKROMID® A3 GF 50 ECO black (8571) - PA 6.6, 50% glass fiber, recycling, high stiffness and strength, heat-stabilised, laser markable, automotive, mechanical engineering.

AKROTEK®

Preliminary

PK-VM GF 60 black (8689)

PK GF60

AKROTEK® PK-VM GF 60 black (8689)- Polyketon, 60% glass fibre reinforced, chemical and hydrolysis resistance

Modulus

16.700MPa

Strength

170MPa

Impact

60kJ/m²

AKROTEK® PK-VM GF 60 black (8689)- Polyketon, 60% glass fibre reinforced, chemical and hydrolysis resistance

AKROMID®

UL
Preliminary

C3 GF 25 1 FR grey (8803)

PA66+PA6 GF25 FR(40)

AKROMID® C3 GF 25 1 FR grey (8803) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, RAL 7035, lasermarkable, high strength, UL-listed, automotive, E&E.

Modulus

9.100MPa

Strength

120MPa

Impact

46kJ/m²

AKROMID® C3 GF 25 1 FR grey (8803) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, RAL 7035, lasermarkable, high strength, UL-listed, automotive, E&E.

AKROMID®

Preliminary

T91 GF 30 FR natural (8667)

PPA GF30 FR(40)

AKROMID® T91 GF 30 FR natural (8667) - PA9T, flame retardant, 30% glass fiber, high stiffness, high strength, free of halogenes, good flowability, low water uptake, reflow soldering, SMT devices, E&E, automotive.

Modulus

10.500MPa

Strength

150MPa

Impact

55kJ/m²

AKROMID® T91 GF 30 FR natural (8667) - PA9T, flame retardant, 30% glass fiber, high stiffness, high strength, free of halogenes, good flowability, low water uptake, reflow soldering, SMT devices, E&E, automotive.

AKROMID®

Preliminary

C3 GF 30 1 natural (8574)

PA66 + PA6 GF30

AKROMID® C3 GF 30 1 natural (8574) - PA6.6/6 blend, 30% glass fiber reinforced, heat stabilised, industrial engineering, automotive industry

Modulus

9.300MPa

Strength

185MPa

Impact

75kJ/m²

AKROMID® C3 GF 30 1 natural (8574) - PA6.6/6 blend, 30% glass fiber reinforced, heat stabilised, industrial engineering, automotive industry

AKROTEK®

PK-VM GF 30 natural (8661)

PK GF30

AKROTEK® PK-VM GF 30 natural (8661) - Polyketon, 30% glass fiber reinforced, chemical and hydrolysis resistance

Modulus

8.300MPa

Strength

144MPa

Impact

76kJ/m²

AKROTEK® PK-VM GF 30 natural (8661) - Polyketon, 30% glass fiber reinforced, chemical and hydrolysis resistance

153545580

AKROMID®

Preliminary

NEXT U28 ICF 30 1 black (8233)PA11 CF30

AKROMID® NEXT U28 ICF 30 1 black (8233) is a Polyamide 11 reinforced with 30% recycled carbon fibre. The PA 11 is made from castor seed oil (bio-based content > 92%). The compound's low density as well as excellent ductility even at lower temperatures combined with high stiffness and strength enable the use for demanding applications, e.g., for lightweight construction or sports & leisure.

Features

heat stabilised 130
recycled content
reduced density
reduced moisture
3D printing / additive manufacturing
Sports & leisure
lightweight construction

Properties

Modulus

15.300MPa

Strength

165MPa

Impact

75kJ/m²

Sustainability

Biobased carbon content

52 %

Recycled content

30 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
15300 MPa
10900 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
165 MPa
140 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
4,8 %
4,8 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
15000 MPa
12000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
260 MPa
220 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
3,7 %
4,2 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
75 kJ/m²
70 kJ/m²
70 kJ/m²
65 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
13 kJ/m²
12 kJ/m²
9 kJ/m²
8 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
180 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
189 °C

General properties

Density

ISO 1183

23°C
1,22 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,7 - 0,9 %

Water absorption

ISO 62

23°C, saturated
1,3 - 1,7 %

Molding shrinkage

ISO 294-4

flow
transverse
0,3 - 0,5 %
0,7 - 0,9 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.