PK-VM GF 30 7 HU black (8695)

PK GF30

AKROTEKĀ® PK-VM GF 30 7 HU black (8695) - Polyketon, 30% glass fibre reinforced, chemical and hydrolysis resistance

Modulus

8.000MPa

Strength

130MPa

Impact

65kJ/mĀ²

AKROTEKĀ® PK-VM GF 30 7 HU black (8695) - Polyketon, 30% glass fibre reinforced, chemical and hydrolysis resistance

PRECITEĀ®

Preliminary

K GF 10 ECO black (8696)

PBT-PET- GF 10

PRECITEĀ® K GF 10 ECO black (8696) - PBT/PET blend, recycled PET content, 10% glass fiber, high strength, good surface, good dimensional stability, automotive, industrial, household, E&E, sports & leisure.

Modulus

4.800MPa

Strength

100MPa

Impact

25kJ/mĀ²

PRECITEĀ® K GF 10 ECO black (8696) - PBT/PET blend, recycled PET content, 10% glass fiber, high strength, good surface, good dimensional stability, automotive, industrial, household, E&E, sports & leisure.

AKROTEKĀ®

PK-VM GF 30 natural (8661)

PK GF30

AKROTEKĀ® PK-VM GF 30 natural (8661) - Polyketon, 30% glass fiber reinforced, chemical and hydrolysis resistance

Modulus

8.300MPa

Strength

144MPa

Impact

76kJ/mĀ²

AKROTEKĀ® PK-VM GF 30 natural (8661) - Polyketon, 30% glass fiber reinforced, chemical and hydrolysis resistance

AKROMIDĀ®

Preliminary

B3 GF 40 5 black (8726)

PA6 GF40

AKROMIDĀ® B3 GF 40 5 black (8726) - PA6, 40% GF, high heat stabilised, UV stabilised, technical parts in industrial engineering, automotive industry, agriculture.

Modulus

12.500MPa

Strength

200MPa

Impact

95kJ/mĀ²

AKROMIDĀ® B3 GF 40 5 black (8726) - PA6, 40% GF, high heat stabilised, UV stabilised, technical parts in industrial engineering, automotive industry, agriculture.

AKROMIDĀ®

Preliminary

NEXT U28 GF 35 1 natural (8642)

PA11 GF35

AKROMIDĀ® NEXT U28 GF 35 1 natural (8642) - PA11 made of renewable raw materials, low density, high ductility

Modulus

8.200MPa

Strength

130MPa

Impact

100kJ/mĀ²

AKROMIDĀ® NEXT U28 GF 35 1 natural (8642) - PA11 made of renewable raw materials, low density, high ductility

AKROMIDĀ®

UL
Preliminary

C3 GF 25 1 FR grey (8803)

PA66+PA6 GF25 FR(40)

AKROMIDĀ® C3 GF 25 1 FR grey (8803) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, RAL 7035, lasermarkable, high strength, UL-listed, automotive, E&E.

Modulus

9.100MPa

Strength

120MPa

Impact

46kJ/mĀ²

AKROMIDĀ® C3 GF 25 1 FR grey (8803) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, RAL 7035, lasermarkable, high strength, UL-listed, automotive, E&E.

PRECITEĀ®

Preliminary

K GF 20 ECO black (8697)

PBT-PET - GF 20

PRECITEĀ® K GF 20 ECO black (8697) - PBT/PET blend, recycled PET content, 20% glass fiber, high strength, good surface, good dimensional stability, automotive, industrial, household, E&E, sports & leisure.

Modulus

7.200MPa

Strength

125MPa

Impact

50kJ/mĀ²

PRECITEĀ® K GF 20 ECO black (8697) - PBT/PET blend, recycled PET content, 20% glass fiber, high strength, good surface, good dimensional stability, automotive, industrial, household, E&E, sports & leisure.

153545580

PRECITEĀ®

Preliminary

P3 GF 50 black (6925)PBT GF 50

PRECITEĀ® P3 GF 50 black (6925) is a 50% glass fibre reinforced, medium viscous poly(butylene terephthalate) (PBT) with very high stiffness and toughness as well as high dimensional and chemical resistance.

Properties

Modulus

17.000MPa

Strength

175MPa

Impact

60kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
17000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
175 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
1,9 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
16500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
285 MPa

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
60 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
12 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
215 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
225 Ā°C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

GWFI

IEC 60695-2-12

1,6 mm Wall thickness
725 Ā°C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,71 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
0,2 %

Water absorption

ISO 62

23Ā°C, saturated
0,4 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Electrical Properties

Dielectric strength

IEC 60243

3 mm
425 kV/mm

Rheological Properties

MVR

ISO 1133

250Ā°C/2,16kg
2 cmĀ³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.