AKROMID®

Preliminary

B3 GF 40 5 black (8725)

PA6 GF40

AKROMID® B3 GF 40 5 black (8725) - PA6, 40% GF, high heat stabilised, UV stabilised, technical parts in industrial engineering, automotive industry, agriculture.

Modulus

12.500MPa

Strength

200MPa

Impact

95kJ/m²

AKROMID® B3 GF 40 5 black (8725) - PA6, 40% GF, high heat stabilised, UV stabilised, technical parts in industrial engineering, automotive industry, agriculture.

AKROMID®

B3 1 S3 black (7956)

PA6-I

AKROMID® B3 1 S3 black (7956) - PA 6 unreinforced, impact modified whilst maintaining good flowability, for connecting and fixing systems

Modulus

2.200MPa

Strength

55MPa

Impact

180kJ/m²

AKROMID® B3 1 S3 black (7956) - PA 6 unreinforced, impact modified whilst maintaining good flowability, for connecting and fixing systems

AKROMID®

Preliminary

B3 S1 natural (7748)

PA6-I

AKROMID® B3 S1 natural (7748) is an unreinforced, cold impact strength polyamide 6

Modulus

1.350MPa

Strength

35MPa

Impact

180kJ/m²

AKROMID® B3 S1 natural (7748) is an unreinforced, cold impact strength polyamide 6

AKROTEK®

UL

PK-VM GF 30 7 HU black (8695)

PK GF30

AKROTEK® PK-VM GF 30 7 HU black (8695) - Polyketon, 30% glass fibre reinforced, chemical and hydrolysis resistance

Modulus

8.000MPa

Strength

130MPa

Impact

65kJ/m²

AKROTEK® PK-VM GF 30 7 HU black (8695) - Polyketon, 30% glass fibre reinforced, chemical and hydrolysis resistance

PRECITE®

Preliminary

K GF 10 ECO black (8696)

PBT-PET- GF 10

PRECITE® K GF 10 ECO black (8696) - PBT/PET blend, recycled PET content, 10% glass fiber, high strength, good surface, good dimensional stability, automotive, industrial, household, E&E, sports & leisure.

Modulus

4.800MPa

Strength

100MPa

Impact

25kJ/m²

PRECITE® K GF 10 ECO black (8696) - PBT/PET blend, recycled PET content, 10% glass fiber, high strength, good surface, good dimensional stability, automotive, industrial, household, E&E, sports & leisure.

PRECITE®

Preliminary

K GF 20 ECO black (8697)

PBT-PET - GF 20

PRECITE® K GF 20 ECO black (8697) - PBT/PET blend, recycled PET content, 20% glass fiber, high strength, good surface, good dimensional stability, automotive, industrial, household, E&E, sports & leisure.

Modulus

7.200MPa

Strength

125MPa

Impact

50kJ/m²

PRECITE® K GF 20 ECO black (8697) - PBT/PET blend, recycled PET content, 20% glass fiber, high strength, good surface, good dimensional stability, automotive, industrial, household, E&E, sports & leisure.

AKROMID®

B3 GF 30 5 black (7285)

PA6 GF30

AKROMID® B3 GF 30 5 black (7285) - PA6, 30% GF, high heat stabilised, technical parts in industrial engineering and automotive industry.

Modulus

9.500MPa

Strength

170MPa

Impact

85kJ/m²

AKROMID® B3 GF 30 5 black (7285) - PA6, 30% GF, high heat stabilised, technical parts in industrial engineering and automotive industry.

153545580

AKROMID®

A3 GK 30 6 natural (6774)PA66 GB30

AKROMID® A3 GK 30 6 natural (6774) is a 30% glass beads filled and inorganic high temperature stabilised PA6.6. It is characterized by a high surface quality and low tendency to warp, which makes it suitable for use in technically demanding components in mechanical engineering and in the automotive industry.

Features

heat stabilised 160
recycled content
low warpage

Properties

Modulus

4.600MPa

Strength

90MPa

Impact

25kJ/m²

Sustainability

Recycled content

30 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
4600 MPa
2000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
90 MPa
52 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
≥ 4 %
25 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
4400 MPa
2000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
135 MPa
70 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
8 %
14 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
25 kJ/m²
170 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
4,5 kJ/m²
5 kJ/m²

Thermal Properties

Melting temperature

ISO 11357-3

DSC, 10K/min
262 °C

General properties

Density

ISO 1183

23°C
1,36 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,9 - 2,1 %

Molding shrinkage

ISO 294-4

flow
transverse
1,1 %
1,3 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more