AKROTEKĀ®

PK-VM GF 30 natural (8661)

PK GF30

AKROTEKĀ® PK-VM GF 30 natural (8661) - Polyketon, 30% glass fiber reinforced, chemical and hydrolysis resistance

Modulus

8.300MPa

Strength

144MPa

Impact

76kJ/mĀ²

AKROTEKĀ® PK-VM GF 30 natural (8661) - Polyketon, 30% glass fiber reinforced, chemical and hydrolysis resistance

AKROTEKĀ®

Preliminary

PK-VM GF 10 black (8685)

PK GF10

AKROTEKĀ® PK-VM GF 10 black (8685) - Polyketon, 10% glass fibre reinforced, chemical and hydrolysis resistance

Modulus

3.500MPa

Strength

70MPa

Impact

55kJ/mĀ²

AKROTEKĀ® PK-VM GF 10 black (8685) - Polyketon, 10% glass fibre reinforced, chemical and hydrolysis resistance

AKROMIDĀ®

Preliminary

NEXT U28 GF 35 1 natural (8642)

PA11 GF35

AKROMIDĀ® NEXT U28 GF 35 1 natural (8642) - PA11 made of renewable raw materials, low density, high ductility

Modulus

8.200MPa

Strength

130MPa

Impact

100kJ/mĀ²

AKROMIDĀ® NEXT U28 GF 35 1 natural (8642) - PA11 made of renewable raw materials, low density, high ductility

PRECITEĀ®

Preliminary

K GF 10 ECO black (8696)

PBT-PET- GF 10

PRECITEĀ® K GF 10 ECO black (8696) - PBT/PET blend, recycled PET content, 10% glass fiber, high strength, good surface, good dimensional stability, automotive, industrial, household, E&E, sports & leisure.

Modulus

4.800MPa

Strength

100MPa

Impact

25kJ/mĀ²

PRECITEĀ® K GF 10 ECO black (8696) - PBT/PET blend, recycled PET content, 10% glass fiber, high strength, good surface, good dimensional stability, automotive, industrial, household, E&E, sports & leisure.

AKROMIDĀ®

Preliminary

C3 GF 30 1 natural (8574)

PA66 + PA6 GF30

AKROMIDĀ® C3 GF 30 1 natural (8574) - PA6.6/6 blend, 30% glass fiber reinforced, heat stabilised, industrial engineering, automotive industry

Modulus

9.300MPa

Strength

185MPa

Impact

75kJ/mĀ²

AKROMIDĀ® C3 GF 30 1 natural (8574) - PA6.6/6 blend, 30% glass fiber reinforced, heat stabilised, industrial engineering, automotive industry

AKROTEKĀ®

Preliminary

PK-VM GF 60 black (8689)

PK GF60

AKROTEKĀ® PK-VM GF 60 black (8689)- Polyketon, 60% glass fibre reinforced, chemical and hydrolysis resistance

Modulus

16.700MPa

Strength

170MPa

Impact

60kJ/mĀ²

AKROTEKĀ® PK-VM GF 60 black (8689)- Polyketon, 60% glass fibre reinforced, chemical and hydrolysis resistance

AKROTEKĀ®

UL

PK-VM GF 30 7 HU black (8695)

PK GF30

AKROTEKĀ® PK-VM GF 30 7 HU black (8695) - Polyketon, 30% glass fibre reinforced, chemical and hydrolysis resistance

Modulus

8.000MPa

Strength

130MPa

Impact

65kJ/mĀ²

AKROTEKĀ® PK-VM GF 30 7 HU black (8695) - Polyketon, 30% glass fibre reinforced, chemical and hydrolysis resistance

153545580

AKROMIDĀ®

B28 GF 50 9 natural (6570)PA6 GF50

AKROMIDĀ® B28 GF 50 9 natural (6570) is a 50% glass fiber reinforced polyamide 6. It is characterised by an improved flowability and mold release compared to a standard PA 6 GF 50. Furthermore, the material impresses with its high stiffness and strength. It is therefore perfectly suitable for technical applications in industrial engineering, furniture industry and in the automotive industry.

Features

easy flow

Properties

Modulus

17.000MPa

Strength

250MPa

Impact

115kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
17000 MPa
10500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
250 MPa
150 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,8 %
4,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
15000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
350 MPa

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
115 kJ/mĀ²
120 kJ/mĀ²
100 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
22 kJ/mĀ²
26 kJ/mĀ²
16 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
220 Ā°C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
220 Ā°C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
185 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 Ā°C

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
20.000 h
160 Ā°C
130 Ā°C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,56 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,3 - 1,6 %

Water absorption

ISO 62

23Ā°C, saturated
4,5 - 5,1 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,4 - 0,6 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
conditioned
1013 ā„¦ x cm
1010 ā„¦ x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
conditioned
1012 ā„¦
1010 ā„¦

Comparative tracking index

IEC 60112

Test liquid A
600 V

Rheological Properties

Flowability

AKRO

2 mm Thickness
540 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more