T5 GF 50 natural (7834)
PPA GF50
AKROMID® T5 GF 50 natural (7834) - 50% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications
18.500MPa
275MPa
95kJ/m²
AKROMID® T5 GF 50 natural (7834) - 50% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications
AKROMID®
B3 1 S3 black (7956)
PA6-I
AKROMID® B3 1 S3 black (7956) - PA 6 unreinforced, impact modified whilst maintaining good flowability, for connecting and fixing systems
2.200MPa
55MPa
180kJ/m²
AKROMID® B3 1 S3 black (7956) - PA 6 unreinforced, impact modified whilst maintaining good flowability, for connecting and fixing systems
AKROMID®
C3 GF 25 1 FR grey (8803)
PA66+PA6 GF25 FR(40)
AKROMID® C3 GF 25 1 FR grey (8803) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, RAL 7035, lasermarkable, high strength, UL-listed, automotive, E&E.
9.100MPa
120MPa
46kJ/m²
AKROMID® C3 GF 25 1 FR grey (8803) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, RAL 7035, lasermarkable, high strength, UL-listed, automotive, E&E.
AKROMID®
T91 GF 30 FR natural (8667)
PPA GF30 FR(40)
AKROMID® T91 GF 30 FR natural (8667) - PA9T, flame retardant, 30% glass fiber, high stiffness, high strength, free of halogenes, good flowability, low water uptake, reflow soldering, SMT devices, E&E, automotive.
10.500MPa
150MPa
55kJ/m²
AKROMID® T91 GF 30 FR natural (8667) - PA9T, flame retardant, 30% glass fiber, high stiffness, high strength, free of halogenes, good flowability, low water uptake, reflow soldering, SMT devices, E&E, automotive.
AKROMID®
T9 GF 30 S1 black (7873)
PPA-I GF30
AKROMID® T9 GF 30 S1 black (7873) is a 30% glass fibre reinforced, cold impact strength polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
8.700MPa
165MPa
95kJ/m²
AKROMID® T9 GF 30 S1 black (7873) is a 30% glass fibre reinforced, cold impact strength polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
AKROLOY®
PARA ICF 40 black (6130)
PARA CF40
AKROLOY® PARA ICF 40 black (6130) is a 40% carbon fibre reinforced Polyarylamide with very high stiffness. The material offers a higher process stability as well as a better weld line performance than its predecessor (6128), while the colour depth is reduced.
39.000MPa
280MPa
35kJ/m²
AKROLOY® PARA ICF 40 black (6130) is a 40% carbon fibre reinforced Polyarylamide with very high stiffness. The material offers a higher process stability as well as a better weld line performance than its predecessor (6128), while the colour depth is reduced.
AKROMID®
B3 GF 30 5 black (7285)
PA6 GF30
AKROMID® B3 GF 30 5 black (7285) - PA6, 30% GF, high heat stabilised, technical parts in industrial engineering and automotive industry.
9.500MPa
170MPa
85kJ/m²
AKROMID® B3 GF 30 5 black (7285) - PA6, 30% GF, high heat stabilised, technical parts in industrial engineering and automotive industry.
AKROLOY®
AKROLOY® PARA GF 35 FR orange (8039) is a flame retardant, 35% glass-fiber reinforced Polyarylamide with highest modulus and strength. The material is based on a flame retardant system that is free of red phosphorus and halogens and is colored in orange similar to RAL 2003. Due to its very good flowability, an improved surface quality is achieved. This grade is also suitable for applications in electrical industries, which need low creep even in conditioned state.
Features
Properties
14.500MPa
190MPa
50kJ/m²
ISO 527-2
ISO 527-2
ISO 527-2
ISO 179-1/1eU
ISO 179-1/1eA
ISO 75
ISO 11357-3
UL 94
IEC 60695-2-12
IEC 60695-2-13
ISO 1183
ISO 294-4
DIN EN IEC 62631-3-2
IEC 60112
IEC 60243
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.