AKROMIDĀ®
B3 GM 10/20 1 black (8748)
PA6 (GF10+GB20)
AKROMIDĀ® B3 GM 10/20 1 black (8748) - PA6, 10% glass fibre, 20% glass bead, heat stabilised, easy flowing, good surface, reduced warpage.
5.700MPa
110MPa
30kJ/mĀ²
AKROMIDĀ® B3 GM 10/20 1 black (8748) - PA6, 10% glass fibre, 20% glass bead, heat stabilised, easy flowing, good surface, reduced warpage.
AKROTEKĀ®
PK-HM natural (7536)
PK
AKROTEKĀ® PK-HM natural (7536) - Polyketon, Tribology, friction and wear, chemical resistance, extrusion
1.400MPa
60MPa
180kJ/mĀ²
AKROTEKĀ® PK-HM natural (7536) - Polyketon, Tribology, friction and wear, chemical resistance, extrusion
AKROMIDĀ®
T9 ICF 20 6 black (7907)
PPA CF 20
AKROMIDĀ® T9 ICF 20 6 black (7907) is a with 20% recycled carbon fibre reinforced polyphthalamide with high stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
14.000MPa
190MPa
35kJ/mĀ²
AKROMIDĀ® T9 ICF 20 6 black (7907) is a with 20% recycled carbon fibre reinforced polyphthalamide with high stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
AKROMIDĀ®
B28 GM 15/15 1 FR black (8750)
PA6 (GF15+GB15) FR(40)
AKROMIDĀ® B28 GM 15/15 1 FR black (8750) - PA6, 15% glass fibre, 15% glass beads, flame retardant, free of halogene, high stiffness and strength, very good flowability, laser markable, E&E.
8.400MPa
105MPa
45kJ/mĀ²
AKROMIDĀ® B28 GM 15/15 1 FR black (8750) - PA6, 15% glass fibre, 15% glass beads, flame retardant, free of halogene, high stiffness and strength, very good flowability, laser markable, E&E.
AKROTEKĀ®
PK-VM M 7 natural (8858)
PK M7
AKROTEKĀ® PK-VM M 7 natural (8858) - 7 % mineral reinforced Polyketon, high flowability and good weldline perfomance.
2.700MPa
65MPa
120kJ/mĀ²
AKROTEKĀ® PK-VM M 7 natural (8858) - 7 % mineral reinforced Polyketon, high flowability and good weldline perfomance.
AKROMIDĀ®
B3 GF 40 5 black (8636)
PA6 GF40
AKROMIDĀ® B3 GF 40 5 black (8636) - PA6, 40% GF, high heat stabilised, UV stabilised, technical parts in industrial engineering, automotive industry, agriculture.
12.500MPa
200MPa
95kJ/mĀ²
AKROMIDĀ® B3 GF 40 5 black (8636) - PA6, 40% GF, high heat stabilised, UV stabilised, technical parts in industrial engineering, automotive industry, agriculture.
PRECITEĀ®
K GF 10 ECO black (8696)
PBT-PET- GF 10
PRECITEĀ® K GF 10 ECO black (8696) - PBT/PET blend, recycled PET content, 10% glass fiber, high strength, good surface, good dimensional stability, automotive, industrial, household, E&E, sports & leisure.
4.800MPa
100MPa
25kJ/mĀ²
PRECITEĀ® K GF 10 ECO black (8696) - PBT/PET blend, recycled PET content, 10% glass fiber, high strength, good surface, good dimensional stability, automotive, industrial, household, E&E, sports & leisure.
AKROMIDĀ®
B28 GF 35 FR EN black (7484)PA6 GF35 FR(40)
AKROMIDĀ® B28 GF 35 FR EN black (7484) is a flame retardant PA6 with 35% glass fibres. The flame retardant system is free of red phosphorus and halogens, leading to optimised electrical properties for e-mobility applications. Due to formulation and production measures, electrical neutrality with regard to halogen compounds < 10 ppm for bromine + iodine can be guaranteed. Due to its very good flowability, it is characterised by easy processability as well as good surface properties. The material has excellent long-term heat stability and outstanding mechanical properties. This product is subject to an increased testing effort.
Features
Properties
12.600MPa
152MPa
70kJ/mĀ²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Flexural modulus
ISO 178
Flexural strength
ISO 178
Flexural strain at break
ISO 178
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Melting temperature
ISO 11357-3
Temperature index for 50% loss of tensile strength
IEC 60216
Flammability
Burning rate
UL 94
GWFI
IEC 60695-2-12
HWI
UL 746A
HAI
UL 746A
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Molding shrinkage
ISO 294-4
Electrical Properties
Volume resistivity IEC
DIN EN IEC 62631-3-2
Surface resistivity
DIN EN 62631-3-2
Comparative tracking index
IEC 60112
Dielectric strength
IEC 60243
Inclined-Plane Tracking, IPT
ASTM D2303-13
High voltage arc tracking rate (HVTR)
UL 746A
High Volt, Low Current Arc Resistance
ASTM D495
Rheological Properties
Flowability
AKRO
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.