Select your fitting and find the right compound for your intend
AKROMIDĀ®
T5 GF 50 natural (7834)
PPA GF50
AKROMIDĀ® T5 GF 50 natural (7834) - 50% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications
18.500MPa
275MPa
95kJ/mĀ²
AKROMIDĀ® T5 GF 50 natural (7834) - 50% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications
AKROMIDĀ®
B3 1 S3 black (7956)
PA6-I
AKROMIDĀ® B3 1 S3 black (7956) - PA 6 unreinforced, impact modified whilst maintaining good flowability, for connecting and fixing systems
2.200MPa
55MPa
180kJ/mĀ²
AKROMIDĀ® B3 1 S3 black (7956) - PA 6 unreinforced, impact modified whilst maintaining good flowability, for connecting and fixing systems
AKROMIDĀ®
C3 GF 25 1 FR grey (8803)
PA66+PA6 GF25 FR(40)
AKROMIDĀ® C3 GF 25 1 FR grey (8803) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, RAL 7035, lasermarkable, high strength, UL-listed, automotive, E&E.
9.100MPa
120MPa
46kJ/mĀ²
AKROMIDĀ® C3 GF 25 1 FR grey (8803) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, RAL 7035, lasermarkable, high strength, UL-listed, automotive, E&E.
AKROMIDĀ®
T91 GF 30 FR natural (8667)
PPA GF30 FR(40)
AKROMIDĀ® T91 GF 30 FR natural (8667) - PA9T, flame retardant, 30% glass fiber, high stiffness, high strength, free of halogenes, good flowability, low water uptake, reflow soldering, SMT devices, E&E, automotive.
10.500MPa
150MPa
55kJ/mĀ²
AKROMIDĀ® T91 GF 30 FR natural (8667) - PA9T, flame retardant, 30% glass fiber, high stiffness, high strength, free of halogenes, good flowability, low water uptake, reflow soldering, SMT devices, E&E, automotive.
AKROMIDĀ®
T9 GF 30 S1 black (7873)
PPA-I GF30
AKROMIDĀ® T9 GF 30 S1 black (7873) is a 30% glass fibre reinforced, cold impact strength polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
8.700MPa
165MPa
95kJ/mĀ²
AKROMIDĀ® T9 GF 30 S1 black (7873) is a 30% glass fibre reinforced, cold impact strength polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
AKROLOYĀ®
PARA ICF 40 black (6130)
PARA CF40
AKROLOYĀ® PARA ICF 40 black (6130) is a 40% carbon fibre reinforced Polyarylamide with very high stiffness. The material offers a higher process stability as well as a better weld line performance than its predecessor (6128), while the colour depth is reduced.
39.000MPa
280MPa
35kJ/mĀ²
AKROLOYĀ® PARA ICF 40 black (6130) is a 40% carbon fibre reinforced Polyarylamide with very high stiffness. The material offers a higher process stability as well as a better weld line performance than its predecessor (6128), while the colour depth is reduced.
AKROMIDĀ®
B3 GF 30 5 black (7285)
PA6 GF30
AKROMIDĀ® B3 GF 30 5 black (7285) - PA6, 30% GF, high heat stabilised, technical parts in industrial engineering and automotive industry.
9.500MPa
170MPa
85kJ/mĀ²
AKROMIDĀ® B3 GF 30 5 black (7285) - PA6, 30% GF, high heat stabilised, technical parts in industrial engineering and automotive industry.
PRECITEĀ®
PRECITEĀ® P3 GF 30 natural (6850) is a 30% glass fibre reinforced, medium viscous polybutylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.
Properties
10.000MPa
145MPa
65kJ/mĀ²
ISO 527-2
ISO 527-2
ISO 527-2
ISO 178
ISO 178
ISO 179-1/1eU
ISO 179-1/1eA
ISO 75
ISO 11357-3
ISO 1183
ISO 1110
ISO 62
ISO 294-4
DIN EN IEC 62631-3-2
DIN EN 62631-3-2
IEC 60112
ISO 1133
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.