Find the right compound
Select your fitting and find the right compound for your intend
AKROMIDĀ®
NEXT U28 GF 35 1 natural (8642)
PA11 GF35
AKROMIDĀ® NEXT U28 GF 35 1 natural (8642) - PA11 made of renewable raw materials, low density, high ductility
8.200MPa
130MPa
100kJ/mĀ²
AKROMIDĀ® NEXT U28 GF 35 1 natural (8642) - PA11 made of renewable raw materials, low density, high ductility
AKROMIDĀ®
B3 GF 40 5 black (8726)
PA6 GF40
AKROMIDĀ® B3 GF 40 5 black (8726) - PA6, 40% GF, high heat stabilised, UV stabilised, technical parts in industrial engineering, automotive industry, agriculture.
12.500MPa
200MPa
95kJ/mĀ²
AKROMIDĀ® B3 GF 40 5 black (8726) - PA6, 40% GF, high heat stabilised, UV stabilised, technical parts in industrial engineering, automotive industry, agriculture.
AKROMIDĀ®
B3 1 FR grey (8051)
PA6 FR(30)
AKROMIDĀ® B3 1 FR grey (8051) - PA6, unreinforced, flame retardant, UL-listed, good surface, public transportation, new mobility.
3.600MPa
75MPa
NA
AKROMIDĀ® B3 1 FR grey (8051) - PA6, unreinforced, flame retardant, UL-listed, good surface, public transportation, new mobility.
AKROMIDĀ®
NEXT U28 ICF 30 1 black (8233)
PA11 CF30
AKROMIDĀ® NEXT U28 ICF 30 1 black (8233) - PA11 made of renewable raw materials, recycled carbon fibre, low density, high ductility
15.300MPa
165MPa
75kJ/mĀ²
AKROMIDĀ® NEXT U28 ICF 30 1 black (8233) - PA11 made of renewable raw materials, recycled carbon fibre, low density, high ductility
PRECITEĀ®
P3 GF 10 black (7813)
PBT GF 10
PRECITEĀ® P3 GF 10 black (7813) is a 10% glass fibre reinforced, medium viscous poly(butylene terephthalate) with medium stiffness and toughness as well as high dimensional and chemical resistance.
4.600MPa
90MPa
25kJ/mĀ²
PRECITEĀ® P3 GF 10 black (7813) is a 10% glass fibre reinforced, medium viscous poly(butylene terephthalate) with medium stiffness and toughness as well as high dimensional and chemical resistance.
AKROMIDĀ®
A3 GF 35 1 HU black (8417)
PA66 GF35
AKROMIDĀ® A3 GF 35 1 HU black (8417) - PA 6.6, 35% glass fibre, heat ageing resistant, high rigidity and strength, very good flowability, UL listed HB.
12.000MPa
215MPa
75kJ/mĀ²
AKROMIDĀ® A3 GF 35 1 HU black (8417) - PA 6.6, 35% glass fibre, heat ageing resistant, high rigidity and strength, very good flowability, UL listed HB.
AKROMIDĀ®
T5 GF 40 6 black (8002)
PPA GF40
AKROMIDĀ® T5 GF 40 6 black (8002) - 40% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications
16.000MPa
245MPa
80kJ/mĀ²
AKROMIDĀ® T5 GF 40 6 black (8002) - 40% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications
AKROMIDĀ®
B3 GF 30 1 L natural (4684)PA6+PP GF30
AKROMIDĀ® B3 GF 30 1 L natural (4684) is a PA6/PP-blend with reduced density compared to standard PA6 with 30% glass fibre reinforcement. The material is suitable for components with high strength and stiffness where cost and weight reduction are required at the same time. The chemical resistance of AKROMIDĀ® B3 GF 30 1 L natural (4684) is particularly superior to calcium chloride (CaClā).
Features
Properties
8.500MPa
150MPa
70kJ/mĀ²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Flexural modulus
ISO 178
Flexural strength
ISO 178
Flexural strain at break
ISO 178
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Melting temperature
ISO 11357-3
Flammability
Burning rate
UL 94
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Molding shrinkage
ISO 294-4
Rheological Properties
MVR
ISO 1133
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.