AKROLOY® PA GF 60 beige(7632) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

Modulus

22.300MPa

Strength

265MPa

Impact

85kJ/m²

AKROLOY® PA GF 60 beige(7632) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

AKROMID^®

A3 GK 30 LA black (4624)

PA66 GB30

AKROMID® A3 GK 30 LA black (4624) is a 30% glass bead filled polyamide 6.6 with low warpage, high surface appearance and lasermarkable.

Modulus

5.000MPa

Strength

90MPa

Impact

25kJ/m²

AKROMID® A3 GK 30 LA black (4624) is a 30% glass bead filled polyamide 6.6 with low warpage, high surface appearance and lasermarkable.

AKROMID^®

A3 GF 30 1 L natural (4715)

PA66+PP GF30

AKROMID® A3 GF 30 1 L natural (4715) - PA6.6/PP-Blend, 30% glass fibre reinforced, lower density, cost reduced, zinc chloride

Modulus

8.600MPa

Strength

155MPa

Impact

77kJ/m²

AKROMID® A3 GF 30 1 L natural (4715) - PA6.6/PP-Blend, 30% glass fibre reinforced, lower density, cost reduced, zinc chloride

AKROMID^®

A3 6 LT black (5651)

PA66

AKROMID® A3 6 LT black (5651) is an unreinforced, inorganic high temperature stabilised and laser-transparent polyamide 6.6

Modulus

3.500MPa

Strength

90MPa

Impact

180kJ/m²

AKROMID® A3 6 LT black (5651) is an unreinforced, inorganic high temperature stabilised and laser-transparent polyamide 6.6

AKROMID^®

B3 ICF 10 1 black (6194)

PA6 CF10

AKROMID® B3 ICF 10 1 black (6194) is a 10% carbon fibre reinforced, heat stabilised polyamide 6 with good sliding properties

Modulus

8.500MPa

Strength

125MPa

Impact

45kJ/m²

AKROMID® B3 ICF 10 1 black (6194) is a 10% carbon fibre reinforced, heat stabilised polyamide 6 with good sliding properties

1 50 51 5280

AKROMID^®

A3 GF 35 2 black (7226)PA66 GF35

AKROMID® A3 GF 35 2 black (7226) is a 35% glass fiber reinforced polyamide 6.6. It is characterised by high stiffness and strength. Furthermore, the material is heat and UV-stabilised and therefore perfectly suitable for technical parts in industrial engineering and in the automotive industry.

Features

UV-stabilised

Properties

Modulus

11.500MPa

Strength

215MPa

Impact

90kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.

1 mm/min | conditioned

11500 MPa

8400 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.

5 mm/min | conditioned

215 MPa

145 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.

5 mm/min | conditioned

3 %

5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.

23°C | conditioned

90 kJ/m²

100 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.

23°C | conditioned

15 kJ/m²

19 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa

255 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa

260 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa

220 °C

Melting temperature

ISO 11357-3

DSC, 10K/min

262 °C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness

HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness

General properties

Density

ISO 1183

23°C

1,4 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.

1,8 - 2,0 %

Water absorption

ISO 62

23°C, saturated

4,7 - 5,3 %

Molding shrinkage

ISO 294-4

flow

transverse

0,1 - 0,3 %

0,6 - 0,8 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.

conditioned

10¹³ Ω x cm

10¹⁰ Ω x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.

conditioned

10¹² Ω

10¹⁰ Ω

Comparative tracking index

IEC 60112

Test liquid A

600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Find the right compound

A3 GF 35 2 black (7226)PA66 GF35

Mechanical Properties

Tensile modulus

Tensile stress at break

Tensile strain at break

Charpy impact strength

Charpy notched impact strength

Thermal Properties

Temperature of deflection under load HDT/A

Temperature of deflection under load HDT/B

Temperature of deflection under load HDT/C

Melting temperature

Flammability

Burning rate

Burning rate (<100 mm/min)

General properties

Density

Humidity absorption

Water absorption

Molding shrinkage

Electrical Properties

Volume resistivity IEC

Surface resistivity

Comparative tracking index

Do you have any questions? We are happy to help.

Find the right compound

A3 GF 35 2 black (7226).css-117ixes{line-height:1.5;display:block;margin-top:var(--chakra-space-2);font-weight:var(--chakra-fontWeights-normal);font-size:var(--chakra-fontSizes-sm);color:var(--chakra-colors-kisPrimaryTextLight-700);}PA66 GF35

Mechanical Properties

Tensile modulus

Tensile stress at break

Tensile strain at break

Charpy impact strength

Charpy notched impact strength

Thermal Properties

Temperature of deflection under load HDT/A

Temperature of deflection under load HDT/B

Temperature of deflection under load HDT/C

Melting temperature

Flammability

Burning rate

Burning rate (<100 mm/min)

General properties

Density

Humidity absorption

Water absorption

Molding shrinkage

Electrical Properties

Volume resistivity IEC

Surface resistivity

Comparative tracking index

Do you have any questions? We are happy to help.

A3 GF 35 2 black (7226)PA66 GF35