AKROMID®

Preliminary

T5 GF 40 6 natural (8003)

PPA GF40

AKROMID® T5 GF 40 6 natural (8003) - 40% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications

Modulus

16.000MPa

Strength

245MPa

Impact

80kJ/m²

AKROMID® T5 GF 40 6 natural (8003) - 40% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications

AKROMID®

C3 GF 35 1 natural (4748)

PA66+PA6 GF35

AKROMID® C3 GF 35 1 natural (4748) - 35% glass fiber reinforced PA 6.6/6 blend, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

11.000MPa

Strength

200MPa

Impact

100kJ/m²

AKROMID® C3 GF 35 1 natural (4748) - 35% glass fiber reinforced PA 6.6/6 blend, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMID®

UL

B3 1 FR black (6580)

PA6 FR(30)

AKROMID® B3 1 FR black (6580) - PA6, unreinforced, flame retardant, UL-listed, good surface, public transportation, new mobility.

Modulus

3.600MPa

Strength

75MPa

Impact

78kJ/m²

AKROMID® B3 1 FR black (6580) - PA6, unreinforced, flame retardant, UL-listed, good surface, public transportation, new mobility.

AKROMID®

B28 GF 35 FR EN black (7484)

PA6 GF35 FR(40)

AKROMID® B28 GF 35 FR EN black (7484) - PA6, 35% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL94 V0 from 1,6 mm, e-mobility.

Modulus

12.600MPa

Strength

152MPa

Impact

70kJ/m²

AKROMID® B28 GF 35 FR EN black (7484) - PA6, 35% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL94 V0 from 1,6 mm, e-mobility.

AKROLOY®

PA GF 60 beige (7632)

PA66+PA6I/6T GF60

AKROLOY® PA GF 60 beige(7632) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

Modulus

22.300MPa

Strength

265MPa

Impact

85kJ/m²

AKROLOY® PA GF 60 beige(7632) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

AKROMID®

Preliminary

NEXT U28 ICF 30 1 black (8233)

PA11 CF30

AKROMID® NEXT U28 ICF 30 1 black (8233) - PA11 made of renewable raw materials, recycled carbon fibre, low density, high ductility

Modulus

15.300MPa

Strength

165MPa

Impact

75kJ/m²

AKROMID® NEXT U28 ICF 30 1 black (8233) - PA11 made of renewable raw materials, recycled carbon fibre, low density, high ductility

AKROMID®

UL

A3 GF 35 1 HU black (8417)

PA66 GF35

AKROMID® A3 GF 35 1 HU black (8417) - PA 6.6, 35% glass fibre, heat ageing resistant, high rigidity and strength, very good flowability, UL listed HB.

Modulus

12.000MPa

Strength

215MPa

Impact

75kJ/m²

AKROMID® A3 GF 35 1 HU black (8417) - PA 6.6, 35% glass fibre, heat ageing resistant, high rigidity and strength, very good flowability, UL listed HB.

150515280

AKROMID®

Preliminary

B28 GF 15 natural (6940)PA6 GF 15

AKROMID B28 GF 15 natural (6940) is a 15% glass fibre reinforced, easy flowing PA6. Due to its very good flowability, this grade has a good surface. It complies with the bus fire standard ECE R 118.03 annex 6, 7, 8 and is suitable for panels and components in luggage racks where medium stiffness and strength is required. The material is easy to colour.

Features

easy flow
public transportation

Regulatory

ece11803

Properties

Modulus

5.300MPa

Strength

120MPa

Impact

39kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
5300 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
120 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
3 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
4500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
210 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
39 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
205 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
220 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Burning rate

UL 94

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
HB Class
HB Class
HB Class
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

Protection Bus

ECE 118

Appendix 6, 7, 8

General properties

Density

ISO 1183

23°C
1,23 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,2 - 0,4 %
0,6 - 0,8 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.