Select your fitting and find the right compound for your intend
AKROLOYĀ®
PARA ICF 40 black (6130)
PARA CF40
AKROLOYĀ® PARA ICF 40 black (6130) is a 40% carbon fibre reinforced Polyarylamide with very high stiffness. The material offers a higher process stability as well as a better weld line performance than its predecessor (6128), while the colour depth is reduced.
39.000MPa
280MPa
35kJ/mĀ²
AKROLOYĀ® PARA ICF 40 black (6130) is a 40% carbon fibre reinforced Polyarylamide with very high stiffness. The material offers a higher process stability as well as a better weld line performance than its predecessor (6128), while the colour depth is reduced.
AKROMIDĀ®
A3 GF 50 8 HU black (8116)
PA66 GF50
AKROMIDĀ® A3 GF 50 8 HU black (8116) - PA 6.6, 50% glass fibre, heat ageing resistant, high rigidity and strength, UL HB all colors listed, NSF 61, WRAS, EU10/2011
17.400MPa
265MPa
115kJ/mĀ²
AKROMIDĀ® A3 GF 50 8 HU black (8116) - PA 6.6, 50% glass fibre, heat ageing resistant, high rigidity and strength, UL HB all colors listed, NSF 61, WRAS, EU10/2011
AKROMIDĀ®
B3 GF 50 RM-M black (3146)
PA6 + X GF50
AKROMIDĀ® B3 GF 50 RM-M black (3146) - 50% glass fiber reinforced PA 6 with reduced moisture absorption and very high stiffness and strength
17.000MPa
210MPa
70kJ/mĀ²
AKROMIDĀ® B3 GF 50 RM-M black (3146) - 50% glass fiber reinforced PA 6 with reduced moisture absorption and very high stiffness and strength
AKROMIDĀ®
A3 GK 30 LA black (4624)
PA66 GB30
AKROMIDĀ® A3 GK 30 LA black (4624) is a 30% glass bead filled polyamide 6.6 with low warpage, high surface appearance and lasermarkable.
5.000MPa
90MPa
25kJ/mĀ²
AKROMIDĀ® A3 GK 30 LA black (4624) is a 30% glass bead filled polyamide 6.6 with low warpage, high surface appearance and lasermarkable.
AKROMIDĀ®
B3 GF 50 1 grey (5507)
PA6 GF50
AKROMIDĀ® B3 GF 50 1 grey (5507) - 50% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry
16.500MPa
190MPa
70kJ/mĀ²
AKROMIDĀ® B3 GF 50 1 grey (5507) - 50% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry
AKROMIDĀ®
T9 ICF 20 6 black (7907)
PPA CF 20
AKROMIDĀ® T9 ICF 20 6 black (7907) is a with 20% recycled carbon fibre reinforced polyphthalamide with high stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
14.000MPa
190MPa
35kJ/mĀ²
AKROMIDĀ® T9 ICF 20 6 black (7907) is a with 20% recycled carbon fibre reinforced polyphthalamide with high stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
AKROMIDĀ®
A3 GF 30 1 L natural (4715)
PA66+PP GF30
AKROMIDĀ® A3 GF 30 1 L natural (4715) - PA6.6/PP-Blend, 30% glass fibre reinforced, lower density, cost reduced, zinc chloride
8.600MPa
155MPa
77kJ/mĀ²
AKROMIDĀ® A3 GF 30 1 L natural (4715) - PA6.6/PP-Blend, 30% glass fibre reinforced, lower density, cost reduced, zinc chloride
AKROMIDĀ®
AKROMIDĀ® A3 GF 35 2 black (7226) is a 35% glass fiber reinforced polyamide 6.6. It is characterised by high stiffness and strength. Furthermore, the material is heat and UV-stabilised and therefore perfectly suitable for technical parts in industrial engineering and in the automotive industry.
Features
Properties
11.500MPa
215MPa
90kJ/mĀ²
ISO 527-2
ISO 527-2
ISO 527-2
ISO 179-1/1eU
ISO 179-1/1eA
ISO 75
ISO 75
ISO 75
ISO 11357-3
UL 94
FMVSS 302
ISO 1183
ISO 1110
ISO 62
ISO 294-4
DIN EN IEC 62631-3-2
DIN EN 62631-3-2
IEC 60112
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.