Select your fitting and find the right compound for your intend
AKROLOY®
PARA ICF 40 black (6130)
PARA CF40
AKROLOY® PARA ICF 40 black (6130) is a 40% carbon fibre reinforced Polyarylamide with very high stiffness. The material offers a higher process stability as well as a better weld line performance than its predecessor (6128), while the colour depth is reduced.
39.000MPa
280MPa
35kJ/m²
AKROLOY® PARA ICF 40 black (6130) is a 40% carbon fibre reinforced Polyarylamide with very high stiffness. The material offers a higher process stability as well as a better weld line performance than its predecessor (6128), while the colour depth is reduced.
AKROMID®
B3 GF 50 ECO black (7926)
PA6 GF50
AKROMID® B3 GF 50 ECO black (7926) - PA 6, GF 50, high strength, high stiffness, heat stabilised, recycled, Co2 reduction, sustainable.
16.000MPa
200MPa
95kJ/m²
AKROMID® B3 GF 50 ECO black (7926) - PA 6, GF 50, high strength, high stiffness, heat stabilised, recycled, Co2 reduction, sustainable.
AKROMID®
B3 GF 15 black (2490)
PA6 GF15
AKROMID® B3 GF 15 black (2490) is a 15% glass fibre reinforced polyamide 6 with medium stiffness and strength
6.100MPa
120MPa
52kJ/m²
AKROMID® B3 GF 15 black (2490) is a 15% glass fibre reinforced polyamide 6 with medium stiffness and strength
AKROMID®
B3 GM 10/20 1 black (8748)
PA6 (GF10+GB20)
AKROMID® B3 GM 10/20 1 black (8748) - PA6, 10% glass fibre, 20% glass bead, heat stabilised, easy flowing, good surface, reduced warpage.
5.700MPa
110MPa
30kJ/m²
AKROMID® B3 GM 10/20 1 black (8748) - PA6, 10% glass fibre, 20% glass bead, heat stabilised, easy flowing, good surface, reduced warpage.
AKROMID®
C3 GF 35 1 natural (4748)
PA66+PA6 GF35
AKROMID® C3 GF 35 1 natural (4748) - 35% glass fiber reinforced PA 6.6/6 blend, heat stabilised, technical parts in industrial engineering and automotive industry
11.000MPa
200MPa
100kJ/m²
AKROMID® C3 GF 35 1 natural (4748) - 35% glass fiber reinforced PA 6.6/6 blend, heat stabilised, technical parts in industrial engineering and automotive industry
AKROMID®
A3 2 S1 grey (5972)
PA66-I
AKROMID® A3 2 S1 grey (5972) - PA 6.6, unreinforced, impact modified, UV-stabilised, for connecting and fixing systems, automotive, electro, furniture
1.800MPa
45MPa
NA
AKROMID® A3 2 S1 grey (5972) - PA 6.6, unreinforced, impact modified, UV-stabilised, for connecting and fixing systems, automotive, electro, furniture
AKROTEK®
PK-VM CF 10 TM black (6135)
PK CF10
AKROTEK® PK-VM CF 10 TM black (6135) - Polyketon, 10% carbon fiber reinforced, chemical, tribological modification, high elongation at break
3.500MPa
59MPa
100kJ/m²
AKROTEK® PK-VM CF 10 TM black (6135) - Polyketon, 10% carbon fiber reinforced, chemical, tribological modification, high elongation at break
AKROMID®
AKROMID® B3 ICF 10 black (5118) is a 10% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties
Properties
8.000MPa
120MPa
50kJ/m²
ISO 527-2
ISO 527-2
ISO 527-2
ISO 178
ISO 178
ISO 178
ISO 179-1/1eU
ISO 179-1/1eA
ISO 75
ISO 11357-3
UL 94
ISO 1183
ISO 1110
ISO 294-4
DIN EN 62631-3-2
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.