AKROMID®

B3 ICF 10 1 black (6194)

PA6 CF10

AKROMID® B3 ICF 10 1 black (6194) is a 10% carbon fibre reinforced, heat stabilised polyamide 6 with good sliding properties

Modulus

8.500MPa

Strength

125MPa

Impact

45kJ/m²

AKROMID® B3 ICF 10 1 black (6194) is a 10% carbon fibre reinforced, heat stabilised polyamide 6 with good sliding properties

AKROMID®

A3 ICF 30 5 black (6495)

PA66 CF30

AKROMID® A3 ICF 30 5 black (6495) is a 30% carbon fibre reinforced, high heat stabilised polyamide 6.6 with high flexural strength and good sliding properties

Modulus

23.000MPa

Strength

235MPa

Impact

50kJ/m²

AKROMID® A3 ICF 30 5 black (6495) is a 30% carbon fibre reinforced, high heat stabilised polyamide 6.6 with high flexural strength and good sliding properties

AKROMID®

Preliminary

B28 GF 30 natural (6941)

PA 6 GF 30

AKROMID B28 GF 30 natural (6941) - PA 6, glass fiber reinforced, easy flow, good surface, bus fire standard ECE R 118.03, high stiffness and strength.

Modulus

10.200MPa

Strength

180MPa

Impact

80kJ/m²

AKROMID B28 GF 30 natural (6941) - PA 6, glass fiber reinforced, easy flow, good surface, bus fire standard ECE R 118.03, high stiffness and strength.

AKROMID®

B3 GF 40 5 black (7286)

PA6 GF40

AKROMID® B3 GF 40 5 black (7286) - 40% glass fiber reinforced PA 6, high heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

12.500MPa

Strength

200MPa

Impact

95kJ/m²

AKROMID® B3 GF 40 5 black (7286) - 40% glass fiber reinforced PA 6, high heat stabilised, technical parts in industrial engineering and automotive industry

AKROMID®

UL

B3 1 FR orange (7698)

PA6 FR(30)

AKROMID® B3 1 FR orange (7698) - PA6, unreinforced, flame retardant, UL-listed, good surface, public transportation, new mobility.

Modulus

3.600MPa

Strength

75MPa

Impact

NA

AKROMID® B3 1 FR orange (7698) - PA6, unreinforced, flame retardant, UL-listed, good surface, public transportation, new mobility.

AKROTEK®

PK-HM natural (7536)

PK

AKROTEK® PK-HM natural (7536) - Polyketon, Tribology, friction and wear, chemical resistance, extrusion

Modulus

1.400MPa

Strength

60MPa

Impact

180kJ/m²

AKROTEK® PK-HM natural (7536) - Polyketon, Tribology, friction and wear, chemical resistance, extrusion

AKROMID®

B3 GF 30 5 black (7285)

PA6 GF30

AKROMID® B3 GF 30 5 black (7285) - PA6, 30% GF, high heat stabilised, technical parts in industrial engineering and automotive industry.

Modulus

9.500MPa

Strength

170MPa

Impact

85kJ/m²

AKROMID® B3 GF 30 5 black (7285) - PA6, 30% GF, high heat stabilised, technical parts in industrial engineering and automotive industry.

148495080

AKROMID®

A3 GF 30 4 black (3571)PA66 GF30

AKROMID® A3 GF 30 4 black (3571) is a 30% glass fiber reinforced polyamide 6.6. It is characterised by high stiffness and strength. Furthermore, the material is hydrolysis and chemically stabilised and therefore perfectly suitable for e.g. cooling systems in the automotive industry.

Features

hydrolysis / chemically stabilised

Properties

Modulus

11.500MPa

Strength

210MPa

Impact

80kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
11500 MPa
6800 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
210 MPa
140 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,5 %
7 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
10000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
310 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
4,5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
80 kJ/m²
100 kJ/m²
65 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
12 kJ/m²
20 kJ/m²
9 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
250 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
260 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
205 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,37 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,7 - 0,9 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
conditioned
1013 Ω x cm
1010 Ω x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
conditioned
1012 Ω
1010 Ω

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more