AKROMID®

B3 GF 15 black (2490)

PA6 GF15

AKROMID® B3 GF 15 black (2490) is a 15% glass fibre reinforced polyamide 6 with medium stiffness and strength

Modulus

6.100MPa

Strength

120MPa

Impact

52kJ/m²

AKROMID® B3 GF 15 black (2490) is a 15% glass fibre reinforced polyamide 6 with medium stiffness and strength

AKROLOY®

UL

PA GF 60 7 natural (2941)

PA66+PA6I/6T GF60

AKROLOY® PA GF 60 7 natural (2941) is a 60% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state. The advanced version of this Product is AKROLOY® PA GF 60 natural (6465) with a modern stabilization technology, featuring improved weld-line strength and an even wider process window. UL listed.

Modulus

21.000MPa

Strength

275MPa

Impact

100kJ/m²

AKROLOY® PA GF 60 7 natural (2941) is a 60% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state. The advanced version of this Product is AKROLOY® PA GF 60 natural (6465) with a modern stabilization technology, featuring improved weld-line strength and an even wider process window. UL listed.

AKROMID®

A3 GK 30 LA black (4624)

PA66 GB30

AKROMID® A3 GK 30 LA black (4624) is a 30% glass bead filled polyamide 6.6 with low warpage, high surface appearance and lasermarkable.

Modulus

5.000MPa

Strength

90MPa

Impact

25kJ/m²

AKROMID® A3 GK 30 LA black (4624) is a 30% glass bead filled polyamide 6.6 with low warpage, high surface appearance and lasermarkable.

AKROMID®

A3 GF 30 1 L natural (4715)

PA66+PP GF30

AKROMID® A3 GF 30 1 L natural (4715) - PA6.6/PP-Blend, 30% glass fibre reinforced, lower density, cost reduced, zinc chloride

Modulus

8.600MPa

Strength

155MPa

Impact

77kJ/m²

AKROMID® A3 GF 30 1 L natural (4715) - PA6.6/PP-Blend, 30% glass fibre reinforced, lower density, cost reduced, zinc chloride

AKROMID®

B3 GF 15 grey (6270)

PA6 GF15

AKROMID® B3 GF 15 grey (6270) is a 15% glass fibre reinforced polyamide 6 with average stiffness and strength.

Modulus

6.000MPa

Strength

110MPa

Impact

50kJ/m²

AKROMID® B3 GF 15 grey (6270) is a 15% glass fibre reinforced polyamide 6 with average stiffness and strength.

AKROMID®

UL

B3 1 FR natural (6437)

PA6 FR(30)

AKROMID® B3 1 FR natural (6437) - PA6, unreinforced, flame retardant, UL-listed, good surface, public transportation, new mobility.

Modulus

3.500MPa

Strength

75MPa

Impact

85kJ/m²

AKROMID® B3 1 FR natural (6437) - PA6, unreinforced, flame retardant, UL-listed, good surface, public transportation, new mobility.

AKROMID®

A3 ICF 30 5 black (6495)

PA66 CF30

AKROMID® A3 ICF 30 5 black (6495) is a 30% carbon fibre reinforced, high heat stabilised polyamide 6.6 with high flexural strength and good sliding properties

Modulus

23.000MPa

Strength

235MPa

Impact

50kJ/m²

AKROMID® A3 ICF 30 5 black (6495) is a 30% carbon fibre reinforced, high heat stabilised polyamide 6.6 with high flexural strength and good sliding properties

147484980

AKROLOY®

UL

PARA GF 60 HU natural (8516)PARA GF60

AKROLOY® PARA GF 60 HU natural (8516) is a 60% glass fibre reinforced polyarylamid with very high stiffness and strength, even in conditioned state owing to its lower moisture uptake. Furthermore, the material shows very good flowability and surface properties. It is perfectly suitable for parts where dimensional stabilitiy is required. Besides, it can be used as an alternative for aluminium and zinc diecast alloys. The material is listed at UL in all colors.

Features

reduced moisture
easy flow
metal substitution

Regulatory

ul

Properties

Modulus

24.000MPa

Strength

300MPa

Impact

80kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
24000 MPa
24000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
300 MPa
270 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,0 %
2,0 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
23500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
400 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
80 kJ/m²
85 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/C

ISO 75

8 MPa
205 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
238 °C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
HB Class
HB Class
HB Class

HWI

UL 746A

0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
4 PLC
2 PLC
2 PLC

HAI

UL 746A

0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
0 PLC
0 PLC
0 PLC

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,76 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,7 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,2 %
0,2 - 0,4 %

Electrical Properties

Comparative tracking index

IEC 60112

Test liquid A
> 600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more