AKROMID®

A3 6 LT black (5651)

PA66

AKROMID® A3 6 LT black (5651) is an unreinforced, inorganic high temperature stabilised and laser-transparent polyamide 6.6

Modulus

3.500MPa

Strength

90MPa

Impact

180kJ/m²

AKROMID® A3 6 LT black (5651) is an unreinforced, inorganic high temperature stabilised and laser-transparent polyamide 6.6

AKROMID®

A3 2 S1 grey (5972)

PA66-I

AKROMID® A3 2 S1 grey (5972) - PA 6.6, unreinforced, impact modified, UV-stabilised, for connecting and fixing systems, automotive, electro, furniture

Modulus

1.800MPa

Strength

45MPa

Impact

NA

AKROMID® A3 2 S1 grey (5972) - PA 6.6, unreinforced, impact modified, UV-stabilised, for connecting and fixing systems, automotive, electro, furniture

AKROMID®

B3 9 natural (6409)

PA6

AKROMID® B3 9 natural (6409) - PA6, unreinforced, process optimized, furniture industry, automotive, cable gland

Modulus

3.300MPa

Strength

85MPa

Impact

NA

AKROMID® B3 9 natural (6409) - PA6, unreinforced, process optimized, furniture industry, automotive, cable gland

AKROMID®

A3 GF 30 6 natural (6398)

PA66 GF30

AKROMID® A3 GF 30 6 natural (6398) is a 30% glass fibre reinforced, inorganic high heat stabilised polyamide 6.6 with high stiffness and strength

Modulus

10.000MPa

Strength

200MPa

Impact

85kJ/m²

AKROMID® A3 GF 30 6 natural (6398) is a 30% glass fibre reinforced, inorganic high heat stabilised polyamide 6.6 with high stiffness and strength

AKROMID®

UL

B3 1 FR natural (6437)

PA6 FR(30)

AKROMID® B3 1 FR natural (6437) - PA6, unreinforced, flame retardant, UL-listed, good surface, public transportation, new mobility.

Modulus

3.500MPa

Strength

75MPa

Impact

85kJ/m²

AKROMID® B3 1 FR natural (6437) - PA6, unreinforced, flame retardant, UL-listed, good surface, public transportation, new mobility.

AKROMID®

A3 GF 35 2 black (7226)

PA66 GF35

AKROMID® A3 GF 35 2 black (7226) - 35% glass fiber reinforced PA 6.6, UV-stabilised, technical parts in industrial engineering and automotive industry

Modulus

11.500MPa

Strength

215MPa

Impact

90kJ/m²

AKROMID® A3 GF 35 2 black (7226) - 35% glass fiber reinforced PA 6.6, UV-stabilised, technical parts in industrial engineering and automotive industry

AKROMID®

B3 S1 black (7629)

PA6-I

AKROMID® B3 S1 black (7629) - PA 6 unreinforced and cold impact modified, for furniture and cunstruction industry, sports and leisure

Modulus

1.700MPa

Strength

45MPa

Impact

180kJ/m²

AKROMID® B3 S1 black (7629) - PA 6 unreinforced and cold impact modified, for furniture and cunstruction industry, sports and leisure

147484980

AKROMID®

Preliminary

NEXT U28 ICF 30 1 black (8233)PA11 CF30

AKROMID® NEXT U28 ICF 30 1 black (8233) is a Polyamide 11 reinforced with 30% recycled carbon fibre. The PA 11 is made from castor seed oil (bio-based content > 92%). The compound's low density as well as excellent ductility even at lower temperatures combined with high stiffness and strength enable the use for demanding applications, e.g., for lightweight construction or sports & leisure.

Features

heat stabilised 130
recycled content
reduced density
reduced moisture
3D printing / additive manufacturing
Sports & leisure
lightweight construction

Properties

Modulus

15.300MPa

Strength

165MPa

Impact

75kJ/m²

Sustainability

Biobased carbon content

52 %

Recycled content

30 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
15300 MPa
10900 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
165 MPa
140 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
4,8 %
4,8 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
15000 MPa
12000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
260 MPa
220 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
3,7 %
4,2 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
75 kJ/m²
70 kJ/m²
70 kJ/m²
65 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
13 kJ/m²
12 kJ/m²
9 kJ/m²
8 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
180 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
189 °C

General properties

Density

ISO 1183

23°C
1,22 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,7 - 0,9 %

Water absorption

ISO 62

23°C, saturated
1,3 - 1,7 %

Molding shrinkage

ISO 294-4

flow
transverse
0,3 - 0,5 %
0,7 - 0,9 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.