Description

AKROMIDĀ®

T5 GF 30 8 black (6457)

PPA GF30

AKROMIDĀ® T5 GF 30 8 black (6457) - PPA, 30% glass fiber, food contact, kitchen and household appliances, fitting, water meter, ACS, WRAS, NSF 61, EU 10/2011, FDA

Modulus

11.500MPa

Strength

210MPa

Impact

65kJ/mĀ²

AKROMIDĀ® T5 GF 30 8 black (6457) - PPA, 30% glass fiber, food contact, kitchen and household appliances, fitting, water meter, ACS, WRAS, NSF 61, EU 10/2011, FDA

AKROMIDĀ®

A3 ICF 30 5 black (6495)

PA66 CF30

AKROMIDĀ® A3 ICF 30 5 black (6495) is a 30% carbon fibre reinforced, high heat stabilised polyamide 6.6 with high flexural strength and good sliding properties

Modulus

23.000MPa

Strength

235MPa

Impact

50kJ/mĀ²

AKROMIDĀ® A3 ICF 30 5 black (6495) is a 30% carbon fibre reinforced, high heat stabilised polyamide 6.6 with high flexural strength and good sliding properties

AKROMIDĀ®

UL

A3 GF 30 FR EN black (6654)

PA66 GF30 FR(40)

AKROMIDĀ® A3 GF 30 FR EN black (6654) is a PA66 with 30% glass-fibers and flame retardant free of halogens and red phosphorus. The product contains an organic stabilization package and is optimized for use in electronic and electric applications. This formulation has been listed at UL under the name AKROMIDĀ® A3 GF 30 FR black (7751). Please consider AKROMIDĀ® A3 GF 30 FR black (7751), in case EN quality is not explicitly necessary, because EN requires additional effort and testing.

Modulus

10.500MPa

Strength

150MPa

Impact

67kJ/mĀ²

AKROMIDĀ® A3 GF 30 FR EN black (6654) is a PA66 with 30% glass-fibers and flame retardant free of halogens and red phosphorus. The product contains an organic stabilization package and is optimized for use in electronic and electric applications. This formulation has been listed at UL under the name AKROMIDĀ® A3 GF 30 FR black (7751). Please consider AKROMIDĀ® A3 GF 30 FR black (7751), in case EN quality is not explicitly necessary, because EN requires additional effort and testing.

AKROMIDĀ®

B28 GM 5/25 FR black (7492)

PA6 (GF5+GB25) FR(40)

AKROMIDĀ® B28 GM 5/25 FR black (7492) is a 5% glass fibre reinforced, 25% glass bead filled, halogen-free flame retardant, easy flowing polyamide 6 with high stiffness and strength

Modulus

5.000MPa

Strength

55MPa

Impact

30kJ/mĀ²

AKROMIDĀ® B28 GM 5/25 FR black (7492) is a 5% glass fibre reinforced, 25% glass bead filled, halogen-free flame retardant, easy flowing polyamide 6 with high stiffness and strength

AKROMIDĀ®

A3 GF 30 1 L natural (4715)

PA66+PP GF30

AKROMIDĀ® A3 GF 30 1 L natural (4715) - PA6.6/PP-Blend, 30% glass fibre reinforced, lower density, cost reduced, zinc chloride

Modulus

8.600MPa

Strength

155MPa

Impact

77kJ/mĀ²

AKROMIDĀ® A3 GF 30 1 L natural (4715) - PA6.6/PP-Blend, 30% glass fibre reinforced, lower density, cost reduced, zinc chloride

AKROMIDĀ®

A3 GM 25/15 1 black (7003)

PA66 (GF25+GB15)

AKROMIDĀ® A3 GM 25/15 1 black (7003) - 25% glass fibre, 15% glass bead, heat stabilised, polyamide 6.6, good surface, low warpage

Modulus

10.000MPa

Strength

180MPa

Impact

70kJ/mĀ²

AKROMIDĀ® A3 GM 25/15 1 black (7003) - 25% glass fibre, 15% glass bead, heat stabilised, polyamide 6.6, good surface, low warpage

AKROLOYĀ®

UL

PA GF 60 7 natural (2941)

PA66+PA6I/6T GF60

AKROLOYĀ® PA GF 60 7 natural (2941) is a 60% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state. The advanced version of this Product is AKROLOYĀ® PA GF 60 natural (6465) with a modern stabilization technology, featuring improved weld-line strength and an even wider process window. UL listed.

Modulus

21.000MPa

Strength

275MPa

Impact

100kJ/mĀ²

AKROLOYĀ® PA GF 60 7 natural (2941) is a 60% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state. The advanced version of this Product is AKROLOYĀ® PA GF 60 natural (6465) with a modern stabilization technology, featuring improved weld-line strength and an even wider process window. UL listed.

147484980

AKROMIDĀ®

UL

C3 GF 25 1 FR natural (7208)PA66+PA6 GF25 FR(40)

AKROMIDĀ® C3 GF 25 1 FR natural (7208) is a 25 % glass fiber reinforced, flame retardant and heat stabilised PA6/6.6 blend. Listed to UL 94 in all-colours, the material is based on a flame retardant system that is free of red phosphorus and halogens. Due to its good flowability, an improved surface quality is achieved. This grade is also suitable for applications with high strength requirements in the automotive and E&E markets.

Features

heat stabilised 130
flame retardant
easy flow
E&E

Regulatory

ul

Properties

Modulus

9.200MPa

Strength

140MPa

Impact

73kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
9200 MPa
6300 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
140 MPa
95 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,3 %
5,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
8600 MPa
5900 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
225 MPa
160 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
3,5 %
5 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
73 kJ/mĀ²
75 kJ/mĀ²
74 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
11 kJ/mĀ²
15 kJ/mĀ²

Thermal Properties

RTI electrical

UL 746B

UL
0,8mm Wall thickness
UL
1,6mm Wall thickness
UL
3,2mm Wall thickness
150 Ā°C
150 Ā°C
150 Ā°C

RTI impact

UL 746B

UL
0,8mm Wall thickness
UL
1,6mm Wall thickness
UL
3,2mm Wall thickness
125 Ā°C
125 Ā°C
125 Ā°C

RTI strength

UL 746B

UL
0,8mm Wall thickness
UL
1,6mm Wall thickness
UL
3,2mm Wall thickness
140 Ā°C
140 Ā°C
140 Ā°C

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
225 Ā°C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
251 Ā°C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
168 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 Ā°C

Coefficient of linear thermal expansion

ISO 11359-1/2

23Ā°C to 80Ā°C | parallel
23Ā°C to 80Ā°C | transverse
0,19 10ā»ā“/K
1,02 10ā»ā“/K

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
20.000 h
155 Ā°C
130 Ā°C

Flammability

Burning rate

UL 94

UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
V-0 Class
V-0 Class
V-0 Class

Burning rate 5V

UL 94

1,6 mm Wall thickness
3,2 mm Wall thickness
5VA Class
5VA Class

GWFI

IEC 60695-2-12

UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
960 Ā°C
960 Ā°C
960 Ā°C

GWIT

IEC 60695-2-13

UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
750 Ā°C
750 Ā°C
750 Ā°C

HWI

UL 746A

UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
0 PLC
0 PLC
0 PLC

HAI

UL 746A

UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
0 PLC
0 PLC
0 PLC

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,37 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,8 - 2,0 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

UL
d.a.m.
1012 ā„¦ x cm

Comparative tracking index

IEC 60112

Test liquid A
> 600 V

Comparative tracking index

ASTM D3638

UL
0 PLC

Dielectric strength

IEC 60243

UL
3 mm
12 kV/mm

Inclined-Plane Tracking, IPT

ASTM D2303-13

1 kV

High voltage arc tracking rate (HVTR)

UL 746A

UL
1 PLC

High Volt, Low Current Arc Resistance

ASTM D495

UL
6 PLC

Rheological Properties

Flowability

AKRO

1 mm Thickness
2 mm Thickness
220 mm
480 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more