Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/m²
558 Compounds found
Recommended  
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

AKROMID®

UL

B3 1 FR natural (6437)

PA6 FR(30)

AKROMID® B3 1 FR natural (6437) - PA6, unreinforced, flame retardant, UL-listed, good surface, public transportation, new mobility.

Modulus

3.500MPa

Strength

75MPa

Impact

85kJ/m²

AKROMID® B3 1 FR natural (6437) - PA6, unreinforced, flame retardant, UL-listed, good surface, public transportation, new mobility.

AKROMID®

A3 GF 30 1 L natural (4715)

PA66+PP GF30

AKROMID® A3 GF 30 1 L natural (4715) - PA6.6/PP-Blend, 30% glass fibre reinforced, lower density, cost reduced, zinc chloride

Modulus

8.600MPa

Strength

155MPa

Impact

77kJ/m²

AKROMID® A3 GF 30 1 L natural (4715) - PA6.6/PP-Blend, 30% glass fibre reinforced, lower density, cost reduced, zinc chloride

AKROMID®

A3 ICF 30 black (5021)

PA66 CF30

AKROMID® A3 ICF 30 black (5021) is a 30% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties

Modulus

24.000MPa

Strength

240MPa

Impact

55kJ/m²

AKROMID® A3 ICF 30 black (5021) is a 30% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties

AKROMID®

A3 GM 25/15 1 black (7003)

PA66 (GF25+GB15)

AKROMID® A3 GM 25/15 1 black (7003) - 25% glass fibre, 15% glass bead, heat stabilised, polyamide 6.6, good surface, low warpage

Modulus

10.000MPa

Strength

180MPa

Impact

70kJ/m²

AKROMID® A3 GM 25/15 1 black (7003) - 25% glass fibre, 15% glass bead, heat stabilised, polyamide 6.6, good surface, low warpage

AKROMID®

T5 GF 50 natural (7834)

PPA GF50

AKROMID® T5 GF 50 natural (7834) - 50% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications

Modulus

18.500MPa

Strength

275MPa

Impact

95kJ/m²

AKROMID® T5 GF 50 natural (7834) - 50% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications

AKROMID®

Preliminary

B3 GF 50 4 RM-M 2 black (8234)

PA6+X GF50

AKROMID® B3 GF 50 4 RM-M 2 black (8234) - 50% glass fiber reinforced PA 6 with good surface properties, UV stabilised, chemically stabilised, reduced moisture absorption

Modulus

16.800MPa

Strength

210MPa

Impact

50kJ/m²

AKROMID® B3 GF 50 4 RM-M 2 black (8234) - 50% glass fiber reinforced PA 6 with good surface properties, UV stabilised, chemically stabilised, reduced moisture absorption

AKROMID®

A3 2 S1 grey (5972)

PA66-I

AKROMID® A3 2 S1 grey (5972) - PA 6.6, unreinforced, impact modified, UV-stabilised, for connecting and fixing systems, automotive, electro, furniture

Modulus

1.800MPa

Strength

45MPa

Impact

NA

AKROMID® A3 2 S1 grey (5972) - PA 6.6, unreinforced, impact modified, UV-stabilised, for connecting and fixing systems, automotive, electro, furniture

147484980

AKROLOY®

PA GF 50 8 black (6732)PA66+PA6I/6T GF50

AKROLOY® PA GF 50 8 black (6732) is a 50% glass fiber reinforced, semi-aromatic polyamide blend. It is characterised by lower moisture absorption compared to standard PA 6.6 compounds, thus convincing through very high stiffness and strength even in the conditioned state. The material is therefore perfectly suitable for technical applications with high demands for dimensional stability. Furthermore, it can be used as an alternative for aluminium and zinc diecast alloys. The compound fulfill FDA, EU10/2011 and ACS.

Features

reduced moisture

Regulatory

acseu102011fda

Properties

Modulus

17.500MPa

Strength

260MPa

Impact

105kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
17500 MPa
16000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
260 MPa
185 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,4 %
2,4 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
16500 MPa
15000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
385 MPa
285 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
2,8 %
2,9 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
105 kJ/m²
105 kJ/m²
95 kJ/m²
95 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
17 kJ/m²
17 kJ/m²
17 kJ/m²
17 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
245 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
185 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
255 °C

General properties

Density

ISO 1183

23°C
1,56 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,3 - 1,5 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,3 - 0,5 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more