AKROMIDĀ®

A3 GK 30 LA black (4624)

PA66 GB30

AKROMIDĀ® A3 GK 30 LA black (4624) is a 30% glass bead filled polyamide 6.6 with low warpage, high surface appearance and lasermarkable.

Modulus

5.000MPa

Strength

90MPa

Impact

25kJ/mĀ²

AKROMIDĀ® A3 GK 30 LA black (4624) is a 30% glass bead filled polyamide 6.6 with low warpage, high surface appearance and lasermarkable.

AKROMIDĀ®

B3 GF 25 1 L black (4637)

PA6+PP GF25

AKROMIDĀ® B3 GF 25 1 L black (4637) - PA6/PP-Blend, 25% glass fibre reinforced, lower density, cost reduced, calcium chloride

Modulus

7.500MPa

Strength

135MPa

Impact

68kJ/mĀ²

AKROMIDĀ® B3 GF 25 1 L black (4637) - PA6/PP-Blend, 25% glass fibre reinforced, lower density, cost reduced, calcium chloride

AKROMIDĀ®

T5 GF 50 8 black (6205)

PPA GF50

AKROMIDĀ® T5 GF 50 8 black (6205) - PPA, 50% glass fiber, food contact, kitchen and household appliances, fitting, water meter, ACS, WRAS, NSF 61, EU 10/2011, FDA

Modulus

19.000MPa

Strength

270MPa

Impact

85kJ/mĀ²

AKROMIDĀ® T5 GF 50 8 black (6205) - PPA, 50% glass fiber, food contact, kitchen and household appliances, fitting, water meter, ACS, WRAS, NSF 61, EU 10/2011, FDA

AKROMIDĀ®

B28 GM 5/25 FR black (7492)

PA6 (GF5+GB25) FR(40)

AKROMIDĀ® B28 GM 5/25 FR black (7492) is a 5% glass fibre reinforced, 25% glass bead filled, halogen-free flame retardant, easy flowing polyamide 6 with high stiffness and strength

Modulus

5.000MPa

Strength

55MPa

Impact

30kJ/mĀ²

AKROMIDĀ® B28 GM 5/25 FR black (7492) is a 5% glass fibre reinforced, 25% glass bead filled, halogen-free flame retardant, easy flowing polyamide 6 with high stiffness and strength

AKROMIDĀ®

T5 GF 40 8 black (7963)

PPA GF40

AKROMIDĀ® T5 GF 40 8 black (7963) - PPA, 40% glass fiber, food contact, kitchen and household appliances

Modulus

15.000MPa

Strength

235MPa

Impact

80kJ/mĀ²

AKROMIDĀ® T5 GF 40 8 black (7963) - PPA, 40% glass fiber, food contact, kitchen and household appliances

AKROMIDĀ®

A3 ICF 30 black (5021)

PA66 CF30

AKROMIDĀ® A3 ICF 30 black (5021) is a 30% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties

Modulus

24.000MPa

Strength

240MPa

Impact

55kJ/mĀ²

AKROMIDĀ® A3 ICF 30 black (5021) is a 30% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties

AKROMIDĀ®

A3 GM 25/15 1 black (7003)

PA66 (GF25+GB15)

AKROMIDĀ® A3 GM 25/15 1 black (7003) - 25% glass fibre, 15% glass bead, heat stabilised, polyamide 6.6, good surface, low warpage

Modulus

10.000MPa

Strength

180MPa

Impact

70kJ/mĀ²

AKROMIDĀ® A3 GM 25/15 1 black (7003) - 25% glass fibre, 15% glass bead, heat stabilised, polyamide 6.6, good surface, low warpage

147484980

AKROMIDĀ®

A3 GF 35 3 black (1802)PA66 GF35

AKROMIDĀ® A3 GF 35 3 black (1802) is a 35% glass fiber reinforced polyamide 6.6. It is characterised by a high stiffness and strength. Furthermore, the material is nucleated. It is perfectly suitable for technical parts in industrial engineering and in the automotive industry.

Features

nucleated

Properties

Modulus

11.500MPa

Strength

180MPa

Impact

50kJ/mĀ²

Sustainability

Recycled content

30 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
11500 MPa
8400 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
180 MPa
120 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,3 %
4,2 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
8000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
250 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
3,7 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
50 kJ/mĀ²
> 55 kJ/mĀ²
53 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
9 kJ/mĀ²
13 kJ/mĀ²
6 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
250 Ā°C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
265 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 Ā°C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,41 g/cmĀ³

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,65 - 0,85 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.