AKROMID®

B3 GF 15 grey (6270)

PA6 GF15

AKROMID® B3 GF 15 grey (6270) is a 15% glass fibre reinforced polyamide 6 with average stiffness and strength.

Modulus

6.000MPa

Strength

110MPa

Impact

50kJ/m²

AKROMID® B3 GF 15 grey (6270) is a 15% glass fibre reinforced polyamide 6 with average stiffness and strength.

AKROMID®

A3 ICF 30 5 black (6495)

PA66 CF30

AKROMID® A3 ICF 30 5 black (6495) is a 30% carbon fibre reinforced, high heat stabilised polyamide 6.6 with high flexural strength and good sliding properties

Modulus

23.000MPa

Strength

235MPa

Impact

50kJ/m²

AKROMID® A3 ICF 30 5 black (6495) is a 30% carbon fibre reinforced, high heat stabilised polyamide 6.6 with high flexural strength and good sliding properties

AKROMID®

B28 GM 5/25 FR black (7492)

PA6 (GF5+GB25) FR(40)

AKROMID® B28 GM 5/25 FR black (7492) is a 5% glass fibre reinforced, 25% glass bead filled, halogen-free flame retardant, easy flowing polyamide 6 with high stiffness and strength

Modulus

5.000MPa

Strength

55MPa

Impact

30kJ/m²

AKROMID® B28 GM 5/25 FR black (7492) is a 5% glass fibre reinforced, 25% glass bead filled, halogen-free flame retardant, easy flowing polyamide 6 with high stiffness and strength

AKROMID®

B28 GF 35 FR EN black (7484)

PA6 GF35 FR(40)

AKROMID® B28 GF 35 FR EN black (7484) - PA6, 35% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL94 V0 from 1,6 mm, e-mobility.

Modulus

12.600MPa

Strength

152MPa

Impact

70kJ/m²

AKROMID® B28 GF 35 FR EN black (7484) - PA6, 35% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL94 V0 from 1,6 mm, e-mobility.

AKROMID®

T5 GF 50 natural (7834)

PPA GF50

AKROMID® T5 GF 50 natural (7834) - 50% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications

Modulus

18.500MPa

Strength

275MPa

Impact

95kJ/m²

AKROMID® T5 GF 50 natural (7834) - 50% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications

AKROMID®

B3 GF 25 1 L black (4637)

PA6+PP GF25

AKROMID® B3 GF 25 1 L black (4637) - PA6/PP-Blend, 25% glass fibre reinforced, lower density, cost reduced, calcium chloride

Modulus

7.500MPa

Strength

135MPa

Impact

68kJ/m²

AKROMID® B3 GF 25 1 L black (4637) - PA6/PP-Blend, 25% glass fibre reinforced, lower density, cost reduced, calcium chloride

AKROMID®

B3 ICF 10 1 black (6194)

PA6 CF10

AKROMID® B3 ICF 10 1 black (6194) is a 10% carbon fibre reinforced, heat stabilised polyamide 6 with good sliding properties

Modulus

8.500MPa

Strength

125MPa

Impact

45kJ/m²

AKROMID® B3 ICF 10 1 black (6194) is a 10% carbon fibre reinforced, heat stabilised polyamide 6 with good sliding properties

146474880

AKROMID®

Internal

A3 CF 30 5 black (8729)PA66 CF30

AKROMID® A3 CF 30 5 black (8729) is a 30% carbon fibre reinforced, high temperature stabilised polyamide 6.6 with elevated mechanical properties and good sliding properties.

Features

heat stabilised 160

Properties

Modulus

26.000MPa

Strength

300MPa

Impact

90kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
26000 MPa
17500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
300 MPa
220 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2 %
3,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
23000 MPa
17000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
400 MPa
300 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
90 kJ/m²
110 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
40°C | d.a.m.
-
10 kJ/m²
13 kJ/m²
8 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
254 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
260 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,26 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,8 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
104 Ω x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
104 Ω

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more