Find the right compound
Select your fitting and find the right compound for your intend
AKROMIDĀ®
B3 1 FR black (6580)
PA6 FR(30)
AKROMIDĀ® B3 1 FR black (6580) - PA6, unreinforced, flame retardant, UL-listed, good surface, public transportation, new mobility.
3.600MPa
75MPa
78kJ/mĀ²
AKROMIDĀ® B3 1 FR black (6580) - PA6, unreinforced, flame retardant, UL-listed, good surface, public transportation, new mobility.
AKROLOYĀ®
PA FGF 60 black (6765)
PA66 + PA6I/6T GF 60
AKROLOYĀ® PA FGF 60 black (6765) - semi-aromatic polyamide blend, 60% flat glass fiber reinforced,improved properties 90Ā° to the flow direction
20.000MPa
290MPa
90kJ/mĀ²
AKROLOYĀ® PA FGF 60 black (6765) - semi-aromatic polyamide blend, 60% flat glass fiber reinforced,improved properties 90Ā° to the flow direction
AKROMIDĀ®
B3 GF 50 RM-M black (3146)
PA6 + X GF50
AKROMIDĀ® B3 GF 50 RM-M black (3146) - 50% glass fiber reinforced PA 6 with reduced moisture absorption and very high stiffness and strength
17.000MPa
210MPa
70kJ/mĀ²
AKROMIDĀ® B3 GF 50 RM-M black (3146) - 50% glass fiber reinforced PA 6 with reduced moisture absorption and very high stiffness and strength
AKROMIDĀ®
B3 GF 50 1 grey (5507)
PA6 GF50
AKROMIDĀ® B3 GF 50 1 grey (5507) - 50% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry
16.500MPa
190MPa
70kJ/mĀ²
AKROMIDĀ® B3 GF 50 1 grey (5507) - 50% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry
AKROLOYĀ®
PA GF 30 black (2718)
PA66+PA6I/6T
AKROLOYĀ® PA GF 30 black (2718) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state. The advanced version of this Product is AKROLOYĀ® PA GF 30 black (6415) with a modern stabilization technology, featuring improved weld-line strength and an even wider process window.
10.500MPa
210MPa
80kJ/mĀ²
AKROLOYĀ® PA GF 30 black (2718) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state. The advanced version of this Product is AKROLOYĀ® PA GF 30 black (6415) with a modern stabilization technology, featuring improved weld-line strength and an even wider process window.
AKROMIDĀ®
B3 GF 35 1 black (2486)
PA6 GF35
AKROMIDĀ® B3 GF 35 1 black (2486) is a 35% glass fibre reinforced, heat stabilised Polyamid 6 with high stiffness and strength.
11.500MPa
195MPa
100kJ/mĀ²
AKROMIDĀ® B3 GF 35 1 black (2486) is a 35% glass fibre reinforced, heat stabilised Polyamid 6 with high stiffness and strength.
AKROMIDĀ®
A3 GK 30 LA black (4624)
PA66 GB30
AKROMIDĀ® A3 GK 30 LA black (4624) is a 30% glass bead filled polyamide 6.6 with low warpage, high surface appearance and lasermarkable.
5.000MPa
90MPa
25kJ/mĀ²
AKROMIDĀ® A3 GK 30 LA black (4624) is a 30% glass bead filled polyamide 6.6 with low warpage, high surface appearance and lasermarkable.
AKROTEKĀ®
PK-VM GF 30 LT black (8653)PK GF30
AKROTEKĀ® PK-VM GF 30 LT black (8653) is a 30% glass fibre reinforced, lasertransparent low viscous polyketone with high stiffness and strength. Due to its very good media resistance, the material is suitable for use in applications that carry cooling water. This type was developed as the successor to PK-VM GF 30 LT black (8530) und PK-VM GF 30 LT black (6934) in order to meet the requirements for a larger processing window during processing.
Features
Properties
8.300MPa
130MPa
65kJ/mĀ²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Flexural modulus
ISO 178
Flexural strength
ISO 178
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Melting temperature
ISO 11357-3
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Molding shrinkage
ISO 294-4
Rheological Properties
MVR
ISO 1133
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.