AKROLOY®

PARA ICF 40 black (6130)

PARA CF40

AKROLOY® PARA ICF 40 black (6130) is a 40% carbon fibre reinforced Polyarylamide with very high stiffness. The material offers a higher process stability as well as a better weld line performance than its predecessor (6128), while the colour depth is reduced.

Modulus

39.000MPa

Strength

280MPa

Impact

35kJ/m²

AKROLOY® PARA ICF 40 black (6130) is a 40% carbon fibre reinforced Polyarylamide with very high stiffness. The material offers a higher process stability as well as a better weld line performance than its predecessor (6128), while the colour depth is reduced.

AKROMID®

B3 GF 15 black (2490)

PA6 GF15

AKROMID® B3 GF 15 black (2490) is a 15% glass fibre reinforced polyamide 6 with medium stiffness and strength

Modulus

6.100MPa

Strength

120MPa

Impact

52kJ/m²

AKROMID® B3 GF 15 black (2490) is a 15% glass fibre reinforced polyamide 6 with medium stiffness and strength

AKROLOY®

UL

PA GF 60 7 natural (2941)

PA66+PA6I/6T GF60

AKROLOY® PA GF 60 7 natural (2941) is a 60% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state. The advanced version of this Product is AKROLOY® PA GF 60 natural (6465) with a modern stabilization technology, featuring improved weld-line strength and an even wider process window. UL listed.

Modulus

21.000MPa

Strength

275MPa

Impact

100kJ/m²

AKROLOY® PA GF 60 7 natural (2941) is a 60% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state. The advanced version of this Product is AKROLOY® PA GF 60 natural (6465) with a modern stabilization technology, featuring improved weld-line strength and an even wider process window. UL listed.

AKROMID®

B3 GF 35 1 black (2486)

PA6 GF35

AKROMID® B3 GF 35 1 black (2486) is a 35% glass fibre reinforced, heat stabilised Polyamid 6 with high stiffness and strength.

Modulus

11.500MPa

Strength

195MPa

Impact

100kJ/m²

AKROMID® B3 GF 35 1 black (2486) is a 35% glass fibre reinforced, heat stabilised Polyamid 6 with high stiffness and strength.

AKROMID®

A3 ICF 30 black (5021)

PA66 CF30

AKROMID® A3 ICF 30 black (5021) is a 30% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties

Modulus

24.000MPa

Strength

240MPa

Impact

55kJ/m²

AKROMID® A3 ICF 30 black (5021) is a 30% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties

AKROMID®

Preliminary

B3 GF 50 ECO black (7926)

PA6 GF50

AKROMID® B3 GF 50 ECO black (7926) - PA 6, GF 50, high strength, high stiffness, heat stabilised, recycled, Co2 reduction, sustainable.

Modulus

16.000MPa

Strength

200MPa

Impact

95kJ/m²

AKROMID® B3 GF 50 ECO black (7926) - PA 6, GF 50, high strength, high stiffness, heat stabilised, recycled, Co2 reduction, sustainable.

AKROMID®

T5 GF 50 natural (7834)

PPA GF50

AKROMID® T5 GF 50 natural (7834) - 50% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications

Modulus

18.500MPa

Strength

275MPa

Impact

95kJ/m²

AKROMID® T5 GF 50 natural (7834) - 50% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications

145464780

AKROMID®

B3 ICF 20 1 L black (5296)PA6 + PP CF20

AKROMID® B3 ICF 20 1 L black (5296) is a 20% carbon fibre reinforced, heat stabilised polyamide-blend with high flexural strength, good sliding properties and a reduced density compared to standard PA6 ICF 20

Features

heat stabilised 130
reduced density

Properties

Modulus

14.200MPa

Strength

140MPa

Impact

50kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
14200 MPa
9700 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
140 MPa
120 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,5 %
4,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
13000 MPa
9700 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
230 MPa
170 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
3 %
5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
50 kJ/m²
60 kJ/m²
45 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
9 kJ/m²
11 kJ/m²
6 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
200 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
222 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

GWIT

IEC 60695-2-13

1,6 mm Wall thickness
675 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,15 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,6 - 1,8 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,4 - 0,6 %

Electrical Properties

Surface resistivity

DIN EN 62631-3-2

d.a.m.
106 Ω

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more